- Beitrag zu einem Tagungsband (160)
- Zeitschriftenartikel (108)
- Vortrag (64)
- Beitrag zu einem Sammelband (24)
- Forschungsbericht (13)
- Buchkapitel (3)
- Tagungsband (Herausgeberschaft für den kompletten Band) (1)
- Posterpräsentation (1)
- Forschungsdatensatz (1)
Sprache
- Englisch (218)
- Deutsch (142)
- Russisch (10)
- Mehrsprachig (2)
- Italienisch (1)
- Serbisch (1)
- Chinesisch (1)
Referierte Publikation
- nein (375) (entfernen)
Schlagworte
- Laser beam welding (57)
- Laserstrahlschweißen (16)
- Solidification cracking (13)
- Welding simulation (13)
- Additive Manufacturing (12)
- Additive manufacturing (11)
- Laser welding (11)
- Numerical simulation (10)
- Laser metal deposition (9)
- Additive Fertigung (8)
Organisationseinheit der BAM
- 9 Komponentensicherheit (166)
- 9.3 Schweißtechnische Fertigungsverfahren (161)
- 7 Bauwerkssicherheit (5)
- 7.2 Ingenieurbau (4)
- 9.6 Additive Fertigung metallischer Komponenten (3)
- 9.0 Abteilungsleitung und andere (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.9 Chemische und optische Sensorik (1)
- 7.7 Modellierung und Simulation (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (1)
- 8.3 Thermografische Verfahren (1)
Eingeladener Vortrag
- nein (64)
Laser metal deposition is described with its applications for additive manufacturing. The necessary process chain is discussed, with regard to weld bead dimensions and 3D build-up strategy. Metallurgical cross sections, x-ray and tensile tests are conducted. As demonstrative components, a gas turbine burner and a turbine blade are shown.
This work aims to find the thermal cycles during and after fusion welding through simulation by first calculating the resulting local temperature field in the quasi-stationary part of the process. Here complete-penetration keyhole laser beam welding with a laser power of 18 kW on a 15 mm thick slab of a low-alloyed steel at a welding speed of 2 m/min is considered. In order to physically depict the laser material interaction a multi-physics numerical model including the effects of phase transformation, thermo-capillary convection, natural convection and temperature-dependent material properties up to evaporation temperature is developed. It uses a fixed keyhole geometry with a right truncated circular cone shape to introduce the laser beam energy to the workpiece. In a subsequent study, the resulting local temperature field is then used as an equivalent heat source in order to predict the unsteady thermal cycle during and after fusion welding. The translational movement of the laser beam through the workpiece is represented by a moving mesh approach. For the simulation, stationary heat transfer and fluid dynamics are described by a system of strongly coupled partial differential equations. These are solved with the commercial finite element software COMSOL Multiphysics 5.0. The results of the numerical simulation are validated by experiments, where the weld bead shapes and the thermal cycles show good correlation.
The weld quality and the possible defect formation are directly determined by the weld pool shape and the thermo-fluid dynamics therein. In this paper, an untypical weld pool profile, i.e., elongated at its top and bottom but narrowed at the middle, is found experimentally and numerically in the wire feed laser beam welding. The detrimental influence of the weld pool narrowing on the element transport is analyzed and discussed. A magnetohydrodynamic technique is utilized to suppress the narrowing, aiming at a more homogenous element distribution. It is found that a low-temperature region is formed in the middle of the weld pool due to the interaction of the two dominant circulations from the top and bottom regions. The weld pool is significantly narrowed due to the untypical growth of the mushy zone in the low-temperature region, which results in a direct blocking effect on the downward flow and the premature solidification in the middle region. The Lorentz force produced by a transverse oscillating magnetic field shows the potential to change the flow pattern into a single-circulation type and the low-temperature-gradient region is mitigated.
Therefore, the downward transfer channel is widened, and its premature solidification is prevented. The numerical results are well validated by experimental measurements of metal/glass observation and X-ray fluorescence element mapping.
The present research work aims at clarification of the effect of the welding electrode type on the mechanical properties of SMA welded joints of 9%Ni steel plates. Properties of produced SMA welded joints were evaluated using different non-destructive and destructive investigation methods. In comparison with the conventionally used Ni-based welding electrode ENiCrMo-3 (AWS A5.11), an experimentally produced non-conventional ferritic welding electrode with 11%Ni (ENi11-Company specification) has resulted in a better combination of the mechanical properties of SMA welded joints of this steel type for critical cryogenic applications. Besides, a positive economic impact for the experimentally produced non-conventional ferritic welding electrode, due to its lower cost, could be another attractive aspect.
The additional element from the filler wire in the laser beam welding is usually distributed inhomogeneously in the final weld due to the high solidification rate of weld pool. It has been found that the electromagnetic stirring produced by an external oscillating magnetic field can enhance the material mixing in the weld pool to achieve a more uniform element distribution. However, the magnetic field has a highly non-linear and multi-coupled interaction with the weld pool behavior, which makes the quantitative explanation of the physical mechanism difficult. In this study, the effect of electromagnetic stirring on the transport phenomena in the wire feed laser beam welding is investigated by a numerical modelling. A 3D transient multi-physical model considering the magnetohydrodynamics, heat transfer, fluid flow, keyhole dynamics and element transport is developed. The multiple reflections and the Fresnel absorption of the laser on the keyhole wall are calculated using the ray tracing method. The numerical results show that a Lorentz force produced by the oscillating magnetic field and its induced eddy current gives significant influence on the transport phenomena in the molten pool. The forward and downward flow is enhanced by the electromagnetic stirring, which homogenizes the distribution of the additional elements from a nickel-based filler wire in a steel weld pool. The numerical results show a good agreement with the high-speed images of the molten pool, the fusion line from the optical micrograph and the element distribution from the energy dispersive X-ray spectroscopy. This work provides a physical base for the electromagnetic-controlled laser beam welding and some guidance for the selection of electromagnetic parameters.
The additional element from the filler wire in the laser beam welding is usually distributed inhomogeneously in the final weld due to the high solidification rate of weld pool. It has been found that the electromagnetic stirring produced by an external oscillating magnetic field can enhance the material mixing in the weld pool to achieve a more uniform element distribution. However, the magnetic field has a highly non-linear and multi-coupled interaction with the weld pool behavior, which makes the quantitative explanation of the physical mechanism difficult. In this study, the effect of electromagnetic stirring on the transport phenomena in the wire feed laser beam welding is investigated by a numerical modelling. A 3D transient multi-physical model considering the magnetohydrodynamics, heat transfer, fluid flow, keyhole dynamics and element transport is developed. The multiple reflections and the Fresnel absorption of the laser on the keyhole wall are calculated using the ray tracing method. The numerical results show that a Lorentz force produced by the oscillating magnetic field and its induced eddy current gives significant influence on the transport phenomena in the molten pool. The forward and downward flow is enhanced by the electromagnetic stirring, which homogenizes the distribution of the additional elements from a nickel-based filler wire in a steel weld pool. The numerical results show a good agreement with the high-speed images of the molten pool, the fusion line from the optical micrograph and the element distribution from the energy dispersive X-ray spectroscopy. This work provides a physical base for the electromagnetic-controlled laser beam welding and some guidance for the selection of electromagnetic parameters.
In this study, a three-dimensional CFD-simulation model was developed to simulate the fluid flow in the weld pool. The CFD-model showed a bulging region in the middle of the depth, which is separated from the top surface and bottom surface by two narrowing regions. It can be concluded that the interaction of the movement of the laser source with the Marangoni vortex leads to a teardrop shape at the upper and bottom surface of the workpiece. Additionally, it shows that the bulging in the weld is a result of the backflows on the upper and lower sides due to the thermo-capillary-driven flows. The weld pool shape was used as a heat source in a two-dimensional thermomechanical model, which allows a highly accurate transformation of the weld pool dimensions obtained from the CFD model. This developed technique allows the consideration of physical aspects, which cannot be considered when using traditional heat sources. The mechanical model has shown that the chronological order of the solidification of the weld has a significant influence on the nature and distribution of the stresses in the weld. High tensile stress has been observed in the bulging region, i.e. in the susceptible region for solidification cracking, when compared to the other narrowing regions, which show compressive stress.
Die Präsentation gibt einen Überblick bezüglich der von der BAM im Rahmen des SimCoLas Verbundprojekts durchgeführten Arbeiten zum Thema "Photonische Prozessketten". Die numerisch abgebildete Prozesskette Tiefziehen/Laserstrahlschweißen wird darsgestellt und diskutiert. Fokus der Diskussion ist die entwickelte Methodik zur konsistenten Abbildung numerischer Prozessketten mit der Applikation Heissrisskritikalität beim Laserstrahlschweißen.
Additive Fertigungsverfahren gewinnen aufgrund der schnellen, flexiblen und kosten-günstigen Fertigung von Bauteilen zunehmend an Bedeutung. Das Laserpulverauf-tragschweißen (LPA) wurde anfangs hauptsächlich als Beschichtungsverfahren ein-gesetzt. Diese Technologie bewerkstelligt aber auch das Reparieren von verschlisse-nen Bauteilen, sodass diese zeitsparend und ressourcenschonend erneuert werden können. Die hohe Aufbaurate, die flexible Pulverzusammensetzung sowie die hohe Endkonturnähe ermöglichen heutzutage die Entwicklung und additive Fertigung von neuen Materialien, wie zum Beispiel Nickel-Titan-Formgedächtnislegierungen.
Komplexe Bauteile ohne Fügestellen sind die Spezialität additiver Verfahren. Immer deutlicher wird der Wert dieser Technologie für den Turbomaschinenbau, etwa bei der Fertigung von Turbinenschaufeln mit inneren Kühlstrukturen. Wichtig für vorbildgetreue Turbinenkomponenten: Die Technologie ermöglicht die Fertigung von Freiformen und Hinterschnitten, von außen- und innenliegenden filigranen, komplexen Strukturen als Einzelteil - und das in einem einzigen Arbeitsschritt. Des Weiteren benötigen additive Verfahren keine formgebenden Werkzeuge und weisen demnach kürzere Prozessketten im Vergleich zu konventionellen Herstellungsverfahren auf. Wirtschaftliche Vorteile kommen vor allem bei kleinen Losgrößen und Bauteilabmessungen zur Geltung.
In diesem Artikel werden am Beispiel einer Turbinenschaufel Schlüsseltechnologien einer additiven Prozesskette gezeigt. Zunächst erfolgt die additive Fertigung einer Turbinenschaufel mittels Selective Laser Melting (SLM). Das Verfahren ermöglicht die Integration innenliegender Kühlkanäle. An dieser Schaufel wird anschließend mittels Laser-PulverAuftragschweißen (LPA) die Reparatur unterschiedlicher Beschädigungen demonstriert. Im nächsten Schritt der Prozesskette bietet ein optischer 3D-Scan der Schaufel die Möglichkeit zur Qualitätskontrolle und zum Vergleich der Bauteilabmessungen mit der Sollgeometrie.
Additive manufacturing promises a high potential for the maritime sector. Directed Energy Deposition (DED) in particular offers the opportunity to produce large-volume maritime components like propeller hubs or blades without the need of a costly casting process. The post processing of such components usually generates a large amount of aluminum bronze grinding waste. The aim of the presented project is to develop a sustainable circular AM process chain for maritime components by recycling aluminum bronze grinding waste to be used as raw material to manufacture ship Propellers with a laser-powder DED process. In the present paper, grinding waste is investigated using a dynamic image Analysis system and compared to commercial DED powder. To be able to compare the material quality and to verify DED process parameters, semi-academic sample geometries are manufactured.
In dieser Studie wurde die Heißrissanfälligkeit beim Laserstrahlschweißen für die Werkstoffe 1.4376, 1.4301 und 1.4828 mit Hilfe des CTW Test quantifiziert. Bei den Versuchen konnten Erstarrungsrisse in den Proben generiert werden. Zusätzlich können mit der Bildkorrelations-Technik die lokalen Dehnungen und Dehnungsraten während des Heißrisstests gemessen wer den. In Verbindung mit einem externen Diodenlaser zum Beleuchten der zu messende Oberfläche und lnterferenzfiltern an den Kameras konnten die DIC Messungen ohne optische Störungen durchgeführt werden.
Die Ergebnisse zeigen, dass die Heißrissbildung bei einer externen Belastung von 3 % für die Stahlsorte 1.4376 zu erwarten ist. Für die Stahls orte 1.4301 beträgt dieser Grenzwert 2 % und 1,5 % für die Stahlgüte 1.4828. Außerdem ist zu beobachten, dass die Gesamtrisslänge mit zu nehmender äußerer Zugbeanspruchung steigt
In einer Vielzahl technischer Anwendungen spielt die Aufrechterhaltung eines definierten Reibungs- und Verschleißverhaltens zwischen bewegten Oberflächen für die Sicherheit und Funktionalität eine ent-scheidende Rolle. Die Oberflächentechnik versucht durch geeignete Verfahren die Randschichten zu ertüchtigen, um Reibung und Verschleiß zu kontrollieren. Eine Verbesserung der Materialeigenschaften kann durch flächige Beschichtungen erreicht werden. Zusätzlich ermöglichen Oberflächenstrukturierun-gen breite Möglichkeiten zur Beeinflussung des Schmierungszustandes bzw. der Kontaktbedingungen. Neben Negativstrukturen bieten ebenfalls erhabene Mikrostrukturen großes Potenzial zur Beeinflussung des tribologischen Verhaltens. Ihr Einsatz ist aber aufgrund der besonderen Verschleißproblematik er-habener Strukturen momentan limitiert, so dass in der Regel zusätzliche verschleißreduzierende Be-schichtungen notwendig werden.
In diesem Beitrag wurde das Verfahren der Laserimplantation angewandt, mit dem erhabene und sepa-rierte Oberflächenstrukturen hoher Verschleißfestigkeit in einem Fertigungsschritt erzeugbar sind. Das Verfahren basiert auf einem lokalisierten Dispergieren von Hartstoffpartikeln. Hierfür wurde erstmalig ein gepulster Faserlaser mit hoher Strahlqualität zur Erzeugung punkt- und linienförmiger Mikrostrukturen angewandt. Versuche wurden auf dem Kaltarbeitsstahl X153CrMoV12 unter Anwendung von Titandibo-rid als Hartstoff durchgeführt. Anhand von Härtemessungen konnte gezeigt werden, dass sowohl punkt- als auch linienförmige Strukturen mit Härten über 1000 HV1 und einer feinkörnigen Mikrostruktur mit feinverteilten Hartstoffpartikeln herstellbar sind. Des Weiteren war es möglich, die Implantgeometrien, welche an Querschliffen und durch Weißlichtinterferometeraufnahmen erfasst wurden, durch die Puls-leistung und Pulsdauer zu steuern.
In einer Vielzahl technischer Anwendungen spielt die Aufrechterhaltung eines definierten Reibungs- und Verschleißverhaltens zwischen bewegten Oberflächen für die Sicherheit und Funktionalität eine entscheidende Rolle. Die Oberflächentechnik versucht durch geeignete Verfahren die Randschichten zu ertüchtigen, um Reibung und Verschleiß zu kontrollieren. Eine Verbesserung der Materialeigenschaften kann durch flächige Beschichtungen erreicht werden. Zusätzlich ermöglichen Oberflächenstrukturierungen breite Möglichkeiten zur Beeinflussung des Schmierungszustandes bzw. der Kontaktbedingungen. Neben Negativstrukturen bieten ebenfalls erhabene Mikrostrukturen großes Potenzial zur Beeinflussung des tribologischen Verhaltens. Ihr Einsatz ist aber aufgrund der besonderen Verschleißproblematik erhabener Strukturen momentan limitiert, so dass in der Regel zusätzliche verschleißreduzierende Beschichtungen notwendig werden.
In diesem Beitrag wurde das Verfahren der Laserimplantation angewandt, mit dem erhabene und separierte Oberflächenstrukturen hoher Verschleißfestigkeit in einem Fertigungsschritt erzeugbar sind. Das Verfahren basiert auf einem lokalisierten Dispergieren von Hartstoffpartikeln. Hierfür wurde erstmalig ein gepulster Faserlaser mit hoher Strahlqualität zur Erzeugung punkt- und linienförmiger Mikrostrukturen angewandt. Versuche wurden auf dem Kaltarbeitsstahl X153CrMoV12 unter Anwendung von Titandiborid als Hartstoff durchgeführt. Anhand von Härtemessungen konnte gezeigt werden, dass sowohl punkt- als auch linienförmige Strukturen mit Härten über 1000 HV1 und einer feinkörnigen Mikrostruktur mit feinverteilten Hartstoffpartikeln herstellbar sind. Des Weiteren war es möglich, die Implantgeometrien, welche an Querschliffen und durch Weißlichtinterferometeraufnahmen erfasst wurden, durch die Pulsleistung und Pulsdauer zu steuern.
Im Rahmen eines AiF-Forschungsvorhabens wurde die Beeinflussung des Schweißprozesses mittels generierter Wechselstrom-Magnetfelder (ACMagnetfelder) beim Laserstrahlschweißen von Aluminiumlegierungen untersucht. Das vorrangige Augenmerk galt hierbei der Entfernung von Poren sowie der Stabilisierung der Schweißnahtoberfläche zur Vermeidung von rauen Schweißnähten. Das Schweißen mit Einsatz des AC-Magneten erzeugte im Vergleich zu den Referenznähten deutlich flachere Schweißnähte mit reduzierter Porenanzahl, die typische Schuppenstruktur wurde unterdrückt. Das Magnetfeld bewirkte bei entsprechenden Parametern der magnetischen Flussdichte und der Frequenz eine Halbierung der Rauigkeit der Schweißnahtoberfläche. Neben der Oberflächenberuhigung wurde auch die Verteilung von Poren in der Schmelze beeinflusst. Es konnte nachgewiesen werden, dass bei einer geeigneten Auswahl der Parameter von AC-Magnetfeldern die Porositätsanteile in der Schweißnaht auf ein Zehntel gegenüber den Referenzschweißnähten reduziert werden können.-----------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
Within the framework of an AiF research project, investigations were conducted into the influences exerted on the welding process using generated alternating current (AC) magnetic fields during the laser beam welding of aluminium alloys. In this respect, attention was principally paid to removing pores and to stabilising the weld surface in order to avoid rough welds. In comparison with the reference welds, welding utilising the AC magnet produced considerably flatter welds with a reduced number of pores and the typical ripple structure was suppressed. With corresponding parameters for the magnetic flux density and the frequency, the roughness of the weld surface was halved using the magnetic field. In addition to the surface stabilisation, influences were also exerted on the distribution of pores in the molten metal. It was possible to prove that, by selecting suitable parameters for AC magnetic fields, the porosity proportions in the weld can be reduced to one tenth of those in the reference welds.
The process of laser metal deposition can be applied in many ways. Mostly, it is relevant to coating, for repair welding and for additive manufacturing. To increase the effectiveness and the productiveness, a good process understanding is necessary. Statistical test planning is effectual and often used for this purpose. For financial and temporal reasons, a restriction of the test space is reasonable. In this case, it is recommended to use a D-optimal experimental design which is practically applied to extend existing test plans or if process Limits are known. This paper investigates the applicability of a D-optimum experimental design for the laser metal deposition. The results are compared to the current results of a full factorial test plan.
Known restrictions are used for the limitation of the test space. Ti6Al4 is utilized as Substrate material and powder. Comparable results of the D-optimal experimental design and of the full factorial test plan can be demonstrated. However, 80 % of time can be saved by the experimental procedure. For this reason, the application of D-optimal experimental design for laser metal deposition is recommend.
Hybrid laser-arc welding (HLAW) was applied for butt welding of 14.5 mm thick plates of ferritic cryogenic steel X8Ni9 containing 9% Ni, which is used for manufacturing storage and transport facilities of liquefied natural gas (LNG). The weld seam formation and the achievable metallurgical and mechanical properties of the hybrid welds were investigated experimentally for two types of filler wire, an austenitic wire dissimilar to the base metal (BM) and an experimentally produced matching ferritic wire. Safe penetration and uniform distribution of the austenitic filler metal in the narrow hybrid weld could only be achieved in the upper, arcdominated part of the weld. The pronounced heterogeneous distribution of the austenitic filler metal in the middle part and in the root area of the weld could not ensure sufficient notched impact toughness of the weld metal (WM). As a result, a decrease in the impact energy down to 17±3 J was observed, which is below the acceptance level of ≥34 J for cryogenic applications. In contrast, the use of a matching ferritic filler wire resulted in satisfactory impact energy of the hybrid welds of up to 134±52 J at the concerned cryogenic temperature of -196 °C. The obtained results contribute to an important and remarkable conversion in automated manufacturing of LNG facilities. In other words, the results will help to develop a new laser-based welding technology, where both quality and productivity are considered.The efficiency of the developed welding process has been demonstrated by manufacturing a prototype where a segment of the inner wall of large size LNG storage tank was constructed. In this concern, hybrid laser arc welding was conducted in both horizontal (2G) and vertical (3G) positions as a simulation to the actual onsite manufacturing. The prototype was fabricated twice where its quality was confirmed based on non-destructive and destructive examinations.
Due to rapid, localized heating and cooling, distortions accumulate in additive manufactured laser metal deposition (LMD) components, leading to a loss of dimensional accuracy or even cracking. Numerical welding simulations allow the prediction of these deviations and their optimization before conducting experiments. To assess the viability of the simulation tool for the use in a predictive manner, comprehensive systems as well as to choose the optimal product matches, product analysis methods are needed. Indeed, most of the known methods aim to analyze a product or one product family on the physical level. Different product families, however, may differ largely in terms of the number and nature of components. This fact impedes an efficient comparison and choice of appropriate product family combinations for the production system. A new methodology is proposed to analyze existing products in view of their functional and physical architecture. The aim is to Cluster these products in new assembly oriented product families for the optimization.
Offshore wind energy plays an important role for the desired transition towards a carbon dioxide free industry within the next decades. However, the grounding of the offshore wind plants governs the overall installation process besides bureaucratic bottlenecks.
The application of lightweight principles in steel construction, e.g. the usage dissolved load-bearing structures, so called Jackets foundations, offer great potential in reducing the resource consumption, especially with respect to the needed amount of steel.
In this context this paper focuses on a fully digitalization of the welding manufacturing and as well as testing chain to enable a fully automated manufacturing as well as quality assessment of tubular nodes as key element of Jackets foundation structures. Furthermore, the relationship between the seam shape geometry and resulting fatigue strength is evaluated by numerical methods incorporating bionic principles. It is shown that tubular nodes can be welded fully automatically taking geometry tolerances into account. Moreover, the seam shape could be manufactured as requested by the numerical models which offers great potential for an extended lifetime. Subsequently, the improvements in resource efficiency and reduction of carbon dioxide emissions are evaluated by a life-cycle-assessment.
In additive manufacturing (AM) Laser Metal Deposition (LMD), parts are built by welding layers of powder feedstock onto a substrate. Applications for steel powders include forging tools and structural components for various industries. For large parts, the choice of tool-paths influences the build-rate, the part performance and the distortions in a highly geometry-dependent manner. With weld-path lengths in the range of hundreds of meters, a reliable, automated tool path generation is essential for the usability of LMD processes.
In this contribution, automated tool-path generation approaches are shown and their results are discussed for arbitrary geometries. The investigated path strategies are the classical approaches: “Zig-zag-” and “contour-parallel-strategies”. After generation, the tool-paths are automatically formatted into g-code for experimental build-up and ASCII for a numerical simulation model. Finally, the tool paths are discussed in regards to volume-fill, microstructure and porosity for the experimental samples.
This work presents a part of the IGF project 18737N “Welding distortion simulation” (FOSTA P1140)
To increase the competitiveness of jacket substructures compared to monopiles a changeover from an individual towards a serial jacket production based on automated manufactured tubular joints combined with standardized pipes has to be achieved. Therefore, this paper addresses fatigue tests of automatically welded tubular X-joints focusing on the location of the technical fatigue crack. The detected location of the technical crack is compared to numerical investigations predicting the most fatigue prone notch considering the structural stress approach as well as the notch stress approach. Besides, the welding process of the automated manufactured tubular X-joints is presented.
To increase the competitiveness of jacket substructures compared to monopiles a changeover from an individual towards a serial jacket production based on automated manufactured tubular joints combined with standardized pipes has to be achieved. Therefore, this paper ad-dresses the welding process of automated manufactured tubular X-joints. Additionally, fatigue tests of the automatically welded tubular joints are presented focusing on the location of the technical fatigue crack. The detected location of the technical crack is compared to numerical investigations predicting the most fatigue prone notch con-sidering the structural stress approach as well as the notch stress ap-proach.
To increase the competitiveness of jacket substructures compared to monopiles a changeover from an individual towards a serial jacket production based on automated manufactured tubular joints combined with standardized pipes has to be achieved. Therefore, this paper addresses fatigue tests of automatically welded tubular X-joints focusing on the location of the technical fatigue crack. The detected location of the technical crack is compared to numerical investigations predicting the most fatigue prone notch considering the structural stress approach as well as the notch stress approach. Besides, the welding process of the automated manufactured tubular X-joints is presented.
Zur Effizienzsteigerung beim Einsatz von Lichtbogenverfahren für Fügeaufgaben im Dickblechbereich werden häufig angepasste Verfahren mit möglichst geringer Nahtquerschnittsfläche angewendet, beispielsweise das MSG-Engspaltschweißen für I-Nähte. Die Herausforderung für die Automatisierung des Verfahrens besteht neben der komplexen Prozessführung auch in der oftmals schlechten Zugänglichkeit der Prozesszone für optische Sensorik, weswegen verstärkt auf prozessorientierte Sensorik zurückgegriffen wird. Zur Steigerung des Prozessverständnisses und Entwicklung neuer Regelungskonzepte wurde ein Versuchsaufbau umgesetzt, der sowohl optische Messsysteme als auch prozessorientierte Sensorik in einer gemeinsamen Steuerungsumgebung vereint. Die umfassende prozessbegleitende Sensorik ermöglicht die sukzessive Erweiterung des Prozesswissens, welches direkt zur Umsetzung neuer Steuer- und Regelalgorithmen basierend auf Regressionsmodellen genutzt werden kann. Der gemeinsame Einsatz optischer und prozessorientierter Sensorik wurde zur Auslegung eines Lichtbogensensors zur Höhenführung genutzt. Die Versuchsdurchführung mit dem Ziel der Ableitung nichtlinearer Regressionsmodelle erfolgt automatisiert mit Hilfe eines optischen Sensors. Der Vorteil dieses Verfahrens liegt dabei neben der schnellen Umsetzbarkeit in der direkten Korrelation der Messwerte zu realen physikalischen Systemgrößen und der schnellen Adaption auf unterschiedliche Schweißparameter und -prozesse.
Automatisierungs- und Regelkonzepte für das MSG-Engspaltschweißen - Pendel- und Füllgradregelung
(2018)
Das MSG-Engspaltschweißen eignet sich auf Grund der I-Nahtvorbereitung besonders für das wirtschaftliche Fügen bei hohen Blechdicken über 100 mm und bietet darüber hinaus zusätzliche technologische Vorteile. Für die automatisierte Anwendung des Verfahrens unter Produktionsbedingungen muss dabei die Prozesssicherheit auch für mitunter große Variationen der Spaltbreite entlang der Schweißnaht gesichert bleiben. In erster Linie betrifft dies bei mechanischer Auslenkung der Drahtelektrode die Adaption der Pendelbewegung auf die jeweilige Spaltbreite um eine ausreichende Flankenanbindung zu garantieren. Für die Online-Regelung der Pendelbewegung mittels Lichtbogensensorik wurde eine Methode implementiert die die notwendigen Pendelwinkel an jeder Nahtflanke unabhängig ermittelt und darüber hinaus Fehlstellungen des Brenners sowie Veränderungen des Kontaktrohrabstandes und der Prozessparameter eigenständig kompensiert. Eine Füllgradregelung auf Grundlage optischer Erfassung und Auswertung der Schweißnahtgeometrie wurde zusätzlich eingesetzt um bei veränderlichen Nahtquerschnittsflächen einen vorgegebenen, gleichbleibenden Lagenaufbau zu erzielen.
The present work deals with the development of a strategy for the prevention of end crater defects in high-power laser welding of thick-walled circumferential welds. A series of experiments were performed to understand the influence of the welding parameters on the formation of end crater defects such as pores, cracks, excessive root-side drop-through and shrinkage cavities in the overlap area. An abrupt switch-off of the laser power while closing the circumferential weld leads to a formation of a hole which passes through the whole welded material thickness. A laser power ramp causes solidification cracks which are initiated on the transition from full-penetration mode to partial penetration. Strategies with a reduction of the welding speed shows a creation of inadmissible root sagging. Defocusing the laser beam led to promising results in terms of avoiding end crater defects. Cracks and pores in the overlap area could be effectively avoided by using defocusing techniques. A strategy for avoiding of end crater imperfections was tested on flat specimens of steel grade S355J2 with a wall thickness of 10 mm and then transferred on the 9.5 mm thick pipe sections made of high-strength steel X100Q.
Die Weiterentwicklung des Laser-Pulver-Auftragschweißens im Bereich der additiven Fertigung stellt dieses Verfahren vor neue Herausforderungen.
Bauteile können schnell und endformnah hergestellt werden, was diese Technik für den Prototypenbau sowie Kleinserienfertigung interessant macht.
Die Vielzahl an Varianten, um ein Volumen aus einzelnen Schichten aufzubauen, erhöhen die Möglichkeiten die Eigenschaften des entstehenden Bauteils zu beeinflussen. Hierfür müssen Strategien entwickelt werden, welche einen gleiclunäßigen Materialauftrag bei gleichzeitig optimalen Materialeigenschaften gewährleisten.
Die durchgeführten Untersuchungen behandeln den Einfluss von Pendelstrategien sowie Spiralstrategien auf die Temperaturentwicklung und stellen diese vergleichend gegenüber. Um den unterschiedlichen Bedingungen bei der Bauteilfertigung Rechnung zu tragen, wurden Versuche in Randbereichen sowie im zentralen Bereich des Testobjekts untersucht. Die Ergebnisse verdeutlichen die Notwendigkeit angepasste Baustrategien zu entwickeln, um durch einen stabilen Fertigungsprozess Qualität und Eigenschaften eines Bauteils gewährleisten zu können.
Die stetig zunehmenden Anforderungen an Kraftstoffverbrauch, Schadstoffemission, sowie passive Sicherheit haben die Automobilindustrie vor Herausforderungen gestellt, die nur durch einen konsequenten Einsatz moderner hochfester Stahlwerkstoffe zu bewältigen sind. Obgleich eine generelle Eignung dieser Stähle für das Widerstandspunktschweißen (WPS) gegeben ist, kann es durch verschiedene externe Einflüsse im betrieblichen Umfeld zur Rissbildung in der Schweißverbindung kommen. Der Einfluss dieser Risse auf die mechanischen Eigenschaften ist derzeit nicht hinreichend genau erfasst, so dass häufig die Vorgabe einer rissfreien Schweißverbindung besteht. Die Kenntnis der Rissanfälligkeit der verarbeiteten Materialkombinationen sowie von ungünstigen Schweißparametern ist daher für viele Unternehmen von erheblicher wirtschaftlicher Bedeutung. Im Rahmen des FOSTA Projekts P921 „Entwicklung eines Verfahrens zur Bestimmung der Rissanfälligkeit von hochfesten Stählen beim Widerstandspunktschweißen“ wurde ein Ansatz zur Bestimmung der Rissanfälligkeit von WPS-Verbindungen hochfester Stähle entwickelt. Mittels einer hydraulischen Vorrichtung unter Zugbelastung wurden geschweißte, rissbehaftete Proben optisch ausgewertet. Das Verfahren ist geeignet, um ein Werkstoffranking bezüglich der Rissanfälligkeit beim Widerstandspunktschweißen für Werkstoffe aufzustellen.
Die lokalen Festigkeiten im Bereich einer Schweißverbindung sind maßgebend für deren Widerstandsfähigkeit gegenüber mechanischen Beanspruchungen. Im Gegensatz zu anderen präparationsaufwendigen Methoden, z. B. die Untersuchung von Mikro-Zugproben, liefert die instrumentierte Eindringprüfung mit deutlich geringerem Aufwand Verläufe von Festigkeiten mit sehr guter Ortsauflösung. Es werden wahre Spannungs-Dehnungs-Kurven aus zyklischen Eindringversuchen mittels Auswertungen auf der Basis repräsentativer Spannungen und Dehnungen und auf der Basis neuronaler Netze an Punktschweißverbindungen zweier hochfester Stähle, eines TRIP-Stahls und eines martensitischen Stahls, sowie eines weichen niedrig legierten Stahls bestimmt, jeweils im Bereich des Grundwerkstoffs und der Schweißlinse.
Laser metal deposition (LMD) has been applied as coating technology for many years. Today, the technologies capacity to produce 3D depositions leads to a new field of application as additive manufacturing method. In this paper, 3D laser metal deposition of titanium alloy Ti-6Al-4V is studied with special regard to the demands of additive manufacturing. Therefore, only the powder nozzle is used to create the shielding gas atmosphere, which ensures high geometric flexibility. Furthermore, specimen with high aspect ratio and hundreds of layers are manufactured, which represent typical features in additive manufacturing.
Build-up strategies for generating components of cylindrical shape with laser metal deposition
(2015)
Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process.
Laser Metal Deposition (LMD) as a technology for additive manufacturing allows the production of large components outside of closed working chambers. Industrial applications require a stable process as well as a constant deposition of the filler material in order to ensure uniform volume growth and reproducible mechanical properties. This paper deals with the influence of travel path strategies on temperature profile and material deposition. Meandering and spiral hatching strategies are used in the center as well as in the edge of a specimen. The temperature is measured with thermocouples attatched to the backside of the specimen. The tests are carried out on the materials S235JR and 316L. The results show a strong dependence of the maximum temperatures on the travel path strategy and the welding position on the component.
The amount of absorbed energy in the keyhole as well as its spatial and temporal distribution is essential to model the laser beam welding process. The recoil pressure, which develops because of the evaporation process induced by the absorbed laser energy at the keyhole wall, is a key determining factor for the macroscopic flow of the molten metal in the weld pool during high-power laser beam welding. Consequently, a realistic implementation of the effect of the laser radiation on the weld metal is crucial to obtain reliable and accurate simulation results.
In this paper, we discuss manyfold different improvements on the laser-material interaction, namely the ray-tracing method, in the numerical simulation of the laser beam welding process. The first improvement relates to locating the exact reflection points in the ray tracing method using a so-called cosine condition in the determination algorithm for the intersection of the reflected rays and the keyhole surface. A second correction refers to the numerical treatment of the Gaussian distribution of the laser beam, whose beam width is defined by a decay of the laser intensity by a factor of 1/e2 thus ignoring around 14 % of the total laser beam energy. In a third step, the changes in the laser radiation distribution in the vertical direction were adapted by using different approximations for the converging and the diverging regions of the laser beam thus mimicking the beam caustic. Finally, a virtual mesh refinement was adopted in the ray tracing routine. The obtained numerical results were validated with experimental measurements.
Die Reduktion des Fahrzeuggewichts ist ein wesentlicher Ansatz zur Ver-ringerung des Energie- und Ressourcenverbrauchs und damit zur Senkung der CO2-Emissionen im Automobilbau. In der Karosserieentwicklung kann der vermehrte Einsatz von Aluminiumwerkstoffen einen bedeutenden Beitrag dazu leisten. Im preissensitiven Umfeld des Karosseriebaus etabliert sich das bei Stahlanwendungen genutzte Widerstandspunktschweißen zunehmend auch für Aluminiumverbindungen. Verfahrensbedingte Herausforderungen, wie verkürzte Elektrodenstandzeiten und mangelnde Kenntnis über den Einfluss von Imperfektionen auf die Festigkeit, begrenzen dennoch die Weiterverbreitung des Verfahrens und stellen die Prozessrobustheit insgesamt in Frage. Im Rahmen des hier vorgestellten Forschungsvorhabens wurden das Auftreten verschiedener Brucharten experimentell untersucht und Prognosefunktionen zur Abschätzung der Tragfähigkeit von Widerstandspunktschweißverbindungen unter verschiedenen Belastungsfällen erstellt. Anschließend wurde der Einfluss von Oberflächenrissen und Rissen in der Schweißlinse auf die Scherzugfestigkeit sowohl experimentell als auch simulativ analysiert.
Laser beam processes are increasingly used in the field of additive manufacturing.
Prominent methods are either powderbed-based like Laser Metal Fusion (LMF), or utilizing a powder nozzle like Laser Metal Deposition (LMD). While LMF allows the manufacturing of complex structures, build rate, part volumes and material flexibility are limited. In contrast, LMD is able to operate with high deposition rates on existing parts, and materials can be changed easily during the process. However LMD shape complexity is limited. Utilizing their respective strengths, a combination of these two additive technologies has the potential to produce complex parts with high deposition rates and increased material flexibility. In this paper, combined manufacturing with additive technologies LMF and LMD is described. Its benefit for industry with emphasis on turbomachinery is shown. As reality test for the innovation, an industrial turbine blade is manufactured.
Metal additive manufacturing is often based on laser beam processes like Laser Metal Fusion (LMF) or Laser Metal Deposition (LMD). The LMF process is in particular suitable for very complex geometries. However build rate, part volume and material flexibility are limited in LMF. In contrast, LMD achieves higher deposition rates, less restricted part sizes and the possibility to change the material composition during the build-up process. On the other hand, due to the lower spatial precision of the material deposition process, the complexity of geometries is limited. Therefore, combined manufacturing with both LMF and LMD has the potential to utilize the respective advantages of both technologies.
In this paper, combined additive manufacturing with LMF and LMD is described for Ti-6Al-4V and Inconel 718. First, lattice structures with different wall thickness and void sizes are built with LMF. The influence of LMD material deposition on these LMF-structures is examined regarding metallurgical impact and distortion. Cross-sections, x-ray computer tomography and 3D-scanning results are shown.
For the titanium alloy specimen, oxygen and Nitrogen content in the deposited material are analysed to evaluate the LMD shielding gas atmosphere. The results are used to develop guidelines for a LMD build-up strategy on LMF substrates. With these findings, a gas turbine burner is manufactured as reality test for the combined approach.
Over the past decade, laser beam welding has significantly evolved and established itself as an efficient tool in the industry. Solidification cracking and the weldability of materials have been highly contentious issues for many years. Today, there are many self and externally loaded tests to investigate the hot cracking resistance of steels. The purpose of this paper is to compare the susceptibility of three stainless steel grades to hot cracking by using an externally loaded hot cracking test (CTW) and a self-restraint test in accordance with SEP-220-3. The repeatability and effectiveness of the results are discussed. The experimental results are widely dispersed, implying a low predictive value for the self-restraint test. On the other hand, the results from the externally loaded test exhibit excellent repeatability and provide a quantitative characterization of the susceptibility of steels to hot cracking.
Digital vernetzte Sensorik für Erfassung von Prozessgrößen
- Datenbankstruktur zur Integration sämtlicher Messgrößen
- In-situ Korrelation zwischen Prozessparametern und
Schweißergebnis auf Basis künstlicher Intelligenz
- Sukzessiver Aufbau an Prozesswissen selbstlernendes
System
- Prozessregelung MSG-Engspaltschweißen
-Adaptiver Pendelwinkelkeine Vorgabe durch Anwender notwendig gleichmäßiger Flankeneinbrand
-Füllgradregelung Vorgabe einer Zielaufbauhöhe durch Anwender autarke Regelung der Prozessgrößenfür gleichmäßige Füllhöhe bei Variation der Spaltbreite
Der Beitrag stellt am Beispiel eines für adaptive MSG-Lichtbogen-Engspaltschweißungen im Dickblech-Bereich entwickelten Versuchsstandes ein Automatisierungskonzept für vernetzte kommerziell verfügbare Anlagenkomponenten über ein zentrales echtzeitfähiges Steuersystem auf Basis des EtherCAT-Protokolls vor. Der Fokus liegt hierbei auf der Eignung für Aufgaben im Bereich der Qualitätssicherung sowie Forschung und Entwicklung leistungsfähiger Algorithmen zur Prozessüberwachung und -regelung. Die sich daraus ergebende Vielzahl zu messender und steuernder Parameter stellen vor allem in Verbindung mit präzisen und hochfrequenten Messgeräten höchste Anforderungen an die Datenverarbeitung sowohl in Echtzeit als auch zur Auswertung nach dem Prozess. Die Einbindung etablierter Programmiertools wie MATLAB/Simulink in gängigen Automatisierungsstandards ermöglichen flexible und innovative Forschungsarbeit.
Durch die automatisierte Datenerfassung in einer übergelagerten Datenbank stehen die Messungen sämtlicher Schweißvorgänge jederzeit zur Entwicklung neuer Abläufe zur Prozessteuerung und -regelung oder zur Verbesserung der bestehenden Algorithmen zur Verfügung, was insbesondere den sukzessiven Aufbau komplexer Regressionsmodelle aus der Anwendung heraus ermöglicht.
Als Applikationsbeispiel wird die Entwicklung eines dynamischen Lichtbogensensors vorgestellt und diskutiert. Die Versuchsdurchführung mit dem Ziel der Ableitung nichtlinearer Regressionsmodelle erfolgt automatisiert mithilfe eines optischen Sensors. Der Vorteil dieses Verfahrens liegt dabei neben der schnellen Umsetzbarkeit in der direkten Korrelation der Messwerte zu realen physikalischen Systemgrößen und der schnellen Adaption auf unterschiedliche Schweißparameter und -prozesse.
Die Wärmeverteilung des Lasers beim Laserstrahltiefschweißen ist für die Formgebung der Dampfkapillare und für die Schweißbaddynamik entscheidend. In dieser Arbeit werden die Laserwärmeverteilung und deren Einflüsse auf die Schweißbadtiefe sowie -breite numerisch anhand des Ray-Tracing-Verfahrens analysiert. Hierbei wird der La-serstrahl in mehreren Strahlenbündeln bzw. Subrays unterteilt. Diesbezüglich soll der Pfad der Subrays präzis be-rechnet werden, um die Dynamik der Dampfkapillare und des Schweißbades eines realen Schweißprozesses rich-tig abzubilden. Zu diesem Zweck beschäftigt sich die vorliegende Arbeit mit der Genauigkeitsverbesserung der Kontaktposition und der Reflexionsrichtung der Subrays auf der freien Oberfläche anhand der Level-Set-Methode. Um die Güte dieses Simulationsansatzes zu gewährleisten, wurde eine Gegenüberstellung mit den zwei klassischen Ray-Tracing-Verfahren mittels drei verschiedenen Benchmark-Testreihen durchgeführt. Anschließend wurden die Versuchsergebnisse zur Validierung der implementierten numerischen Ansätze verwendet. Im Rahmen dieser Arbeit kann es gezeigt werden, dass unterschiedliche Wärmeverteilung aufgrund der verschiedenen Ray-Tracing-Verfahren deutlich zu erkennen ist, welche wiederum die Schweißbaddynamik sowie die lokalisierte Dampfkapil-lardynamik stark beeinflussen. Ferner wurde es bestätigt, dass die implementierte Level-Set-Methode zu einer ge-naueren Ermittlung der Kontaktposition und der Reflexionsrichtung der Subrays und somit zu einer Verbesserung der simulierten Schmelzkontur führt.
In the article considered the problem of hot cracks occurrence during laser welding process. The main reason of their appearance is strain. The optical method for measuring full field strain locally near the solidification front during laser welding process is proposed. The proposed method of optical measurement allows to determine the real values of the critical strain for various materials characterizing the occurrence of hot cracks in laser welding process.
Test procedure to characterize the cracking susceptibility of RSW-steels has been developed
During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior
With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel
Complex phase steels behavior during test procedure:
Crack length growth with increasing force could not be determined
The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case)
30
Laser hybrid welding technology provides a number of advantages, which in the previous decade have promoted its implementation in different branches of industry such as automotive manufacturing, shipbuilding and power generation. Some examples of the applications of laser hybrid welding are reviewed to demonstrate the technological and economic potential of this technology. The main objective of this chapter is to show some of the benefits and limitations of the process and to give some examples of how the number of applications could rise, taking into account the advantages of the new laser systems, optical components, arc power sources and sensor systems available nowadays.
In contrast to other simulation fields like forming simulation, welding simulation is still not widely used in industrial environments. A high user expertise, a high time-to-solution and the result accuracy are the most important problems that hinder its extensively application. Different modeling approaches influence these aspects and an analysis of their implementation is of interest especially for the automotive industry as a key user for production Simulation.
Distortion optimisation of beam-welded industrial parts by means of numerical welding simulation
(2008)
Distortion optimisation of beam-welded industrial parts by means of numerical welding simulation
(2010)
Directed energy deposition additive manufactured parts have steep stress gradients and an anisotropic microstructure caused by the rapid thermo-cycles and the layer-upon-layer manufacturing, hence heat treatment can be used to reduce the residual stresses and to restore the microstructure. The numerical simulation is a suitable tool to determine the parameters of the heat treatment process and to reduce the necessary application efforts. The heat treatment simulation calculates the distortion and residual stresses during the process. Validation experiments are necessary to verify the simulation results. This paper presents a 3D coupled thermo-mechanical model of the heat treatment of additive components. A distortion-based validation is conducted to verify the simulation results, using a C-ring shaped specimen geometry. Therefore, the C-ring samples were 3D scanned using a structured light 3D scanner to compare the distortion of the samples with different post-processing histories.
The present research work encloses results of experimental investigations of the interaction between welding process parameters for laser-beam and hybrid-laser-arc as well as type of the filler metal and the achievable mechanical properties of the weld joints on steel grade X8Ni9+QT640 for cryogenic service containing 9% nickel. The results obtained contribute to the development and conversion in the industrial practice a new laser beam-based welding technology for the automated manufacturing of facilities for the liquefaction, storage and the transport of natural gases (LNG facilities). The results show, that the martensitic microstructure of the laser weld metal including low amount of retained austenite not exceeding 3.5% leads to the relatively low V-notch impact energy. The remarkable heterogeneity in the chemical composition of the weld metal through the weld thickness could be recognized in the case of hybrid-laser-arc welding with ERNiCrMo-3 austenitic filler metal, what also led to insufficient impact toughness of the weld metall. The most promising results could be achieved by using 11%Ni filler wire, which is similar to the base metal and provides a homogeneous microstructure with uniform distribution of Ni through the weld seam. It is remarkable, that a correlation between Charpy impact toughness and wire feeding speed and respectively process heat input exists. The highest toughness values were 134±58 J at -196C. The both laser as well as laser-hybrid welds passed the tensile test. The failure stress of 720±3 MPa with a fracture location in the base material was achieved for all samples tested.
The combination of laser powder bed fusion (LPBF), known for its geometrical freedom and accuracy, and the nozzle-based laser metal deposition process (LMD), known for its high build-up rates, has great potential to reduce the additive manufacturing times for large metallic parts. For the industrial application of the LPBF-LMD hybrid process chain, it is necessary to investigate the infuence of the LMD process on the LPBF substrate. In addition, the build plate material also has a signifcant impact on the occurrence of distortion along the additive manufacturing process chain. In the literature, steel build plates are often used in laser-based additive manufacturing processes of Inconel 718, since a good metallurgical Bonding can be assured whilst reducing costs in the production and restoration of the build plates. This paper examines the distortion caused by LMD material deposition and the infuence of the build plate material along the hybrid additive manufacturing process chain. Twin cantilevers are manufactured by LPBF and an additional layer is subsequently deposited with LMD. The distortion is measured in the as-built condition as well as after heat treatment. The efect of diferent LMD hatch strategies on the distortion is determined. The experiments are conducted using the nickel-base alloy Inconel 718. The results show a signifcant infuence of LMD path strategies on distortion, with shorter tool paths leading to less distortion. The remaining distortion after heat treatment is considerably dependent on the material of the build plate.
Despite the advances in hardware and software techniques, standard numerical methods fail in providing real-time simulations, especially for complex processes such as additive manufacturing applications. A real-time simulation enables process control through the combination of process monitoring and automated feedback, which increases the flexibil- ity and quality of a process. Typically, before producing a whole additive manufacturing structure, a simplified experiment in form of a bead-on- plate experiment is performed to get a first insight into the process and to set parameters suitably. In this work, a reduced order model for the transient thermal problem of the bead-on-plate weld simulation is devel- oped, allowing an efficient model calibration and control of the process. The proposed approach applies the proper generalized decomposition (PGD) method, a popular model order reduction technique, to decrease the computational effort of each model evaluation required multiple times in parameter estimation, control and optimization. The welding torch is modeled by a moving heat source, which leads to difficulties separating space and time, a key ingredient in PGD simulations. A novel approach for separating space and time is applied and extended to 3D problems allowing the derivation of an efficient separated representation of the tem- perature. The results are verified against a standard finite element model showing excellent agreement. The reduced order model is also leveraged in a Bayesian model parameter estimation setup, speeding up calibrations and ultimately leading to an optimized real-time simulation approach for welding experiment using synthetic as well as real measurement data.
Fusion welding is widely used in the automotive industry to join metal structures. It is well-known that distortions and residual stresses occur during and after the welding process. Many procedures exist to decrease these negative heat effects of welding, but are often coupled with highly cost intensive experiments. The implementation of a welding Simulation tool to reduce this very expensive experimental procedures is therefore of high interest. Despite the fact that the automotive industry is a key sector for Simulation procedures, welding Simulation Software is nevertheless not yet widely implemented. This is mainly due to the complexity of the Simulation tools requiring expert users and the resulting high time to Solution.
In this study, a new fast thermo-mechanical Simulation of a complex and large laser beam welded automotive sheet metal assembly with several non linear welds is simulated. Assumptions and simplifications of the complex physical welding phenomenon, which are made to keep the computational cost and the complexity of the Simulation in an industrial frame, are discussed. The calibration time of the phenomenological heat source model has been optimized with a very fast analytical thermal model and the resulting simulated temperature fields match perfectly with the measured ones. Additionally, the user experience and the time-to-solution are kept within a reasonable time frame for arr industrial environment. All Simulation results are validated with experimental results.
Schweißeigenspannungen - im Besonderen infolge von Strahlschweißprozessen - annähernd der werkstoffspezifischen Streckgrenze können durch eine mögliche Spannungsrelaxation oder verstärkte Spannungsrisskorrosion lebensdauerreduzierende Konsequenzen mit sich ziehen. Aus diesem Grund wurden viele Verfahren entwickelt, welche diese Eigenspannungen reduzieren können. Jedoch sind diese Verfahren kostenintensiv oder nur für breite Schweißnähte und einfache Bauteilgeometrien anwendbar. Die in dieser Arbeit dargestellte Methode nutzt den Schweißstrahl für den Schweißprozess sowie in defokussierter Form für eine thermische Nachbehandlung des Bauteils. Hierfür läuft der defokussierte Strahl durch hochfrequente Strahlablenkung beidseitig der Schweißnaht mit einer bestimmten zeitlichen Distanz dem Schmelzbad nach und wird zum Aufheizen dieser Materialbereiche genutzt. Mit dieser Prozedur ist es möglich die Spannungen in schmalen Schweißnähten mit großen Spannungsgradienten im Vergleich zu anderen spannungsreduzierenden Verfahren ohne Kontaktflächen oder zusätzlichem Equipment effizient zu reduzieren. Abhängig von der Bauteilgeometrie und der Strahlleistung können unterschiedliche Prozessparameter für dieses Verfahren angewandt werden. Es werden die Mechanismen der Eigenspannungsreduzierung in diesem Prozess und deren Abhängigkeit von den Prozessparametern anhand von Ergebnissen aus FEM-Simulationen diskutiert. Zudem wird in einer Reihe von experimentellen Ergebnissen die Anwendbarkeit von bereits für lineare Schweißnähte ermittelte Verfahrensparameter auf axiale und radiale Rundnähte nachgewiesen. Hierbei zeigen die besten experimentellen Ergebnisse für Elektronenstrahl- sowie für Laserstrahlschweißnähte Spannungsreduktionen größer als 90 %.
Ob in der Automobilindustrie, beim Rohrleitungs- oder beim Kraftwerksbau – anspruchsvolle und hochwertige Fügeverbindungen entscheiden oft über die Qualität des Endproduktes. Um z. B. das Verzugsverhalten von Karosseriebauteilen vorab einschätzen zu können, setzen Hersteller auf die numerische Simulation der geschweißten Komponenten. Besondere Aufmerksamkeit gilt hier den Fügestellen. Da diese oft nur wenige Millimeter klein sind, kommen konventionelle Prüfverfahren wie der Zugversuch hier jedoch nicht ohne weiteres in Frage.
Forscher des Fraunhofer IPK untersuchen deshalb eine alternative Methode, um die negativen Begleiterscheinungen des thermischen Schweißens im Vorfeld am PC zu analysieren und nötige Gegenmaßnahmen ableiten zu können.
Der Absorptionsgrad metallischer Werkstoffe spielt bei Fügeprozessen mit einer Strahlungsquelle wie dem Hochleistungslaserstrahltiefschweißen eine bedeutende Rolle. Dieser beeinflusst die Menge der absorbierten Laserenergie, welche zum Aufschmelzen sowie zur lokalen Verdampfung des zu verbindenden Materials führt. Die Laserstrahlabsorption wird von vielen physikalischen Faktoren, z.B. Laserprofil, Laserwellenlänge, Materialeigenschaft sowie Temperatur, entschieden. Dennoch wird die Temperaturabhängigkeit in vielen Simulationsarbeiten häufig ignoriert und stattdessen ein empirisch angepasster Parameter zur Kalibrierung der Ergebnisse implementiert. Diese Vorgehensweise wirkt sich negativ auf die Zuverlässigkeit des numerischen Modells sowie auf die Vorhersagbarkeit der Simulationsergebnisse aus. In der vorliegenden Arbeit wird die Temperaturabhängigkeit des Laserabsorptionsgrades in ein selbstkonsistentes zweiphasiges Modell unter Berücksichtigung der gekoppelten 3D-Fluidströmung und Wärmeübertragung einbezogen. Die berechnete Laserstrahlabsorption wird durch die temperaturabhängigen Materialeigenschaften, die Lasercharakteristik und den Einfallswinkel des Laserstrahls bestimmt. Die freie Oberfläche jeder Phase wird mithilfe der Volume-of-Fluid Methode (VOF), berechnet und die Laser-Material-Wechselwirkung wird durch ein implementiertes Ray-Tracing-Verfahren modelliert, welches auf einem lokalisierten Level-Set-Algorithmus basiert. Anschließend wird die transiente Wärmeeinbringung und die Geometrie der Schweißnaht analysiert und mit dem temperaturunabhängigen Absorptionsmodell verglichen. Es wurde festgestellt, dass die Temperaturabhängigkeit der Laserabsorption entscheidend für die genaue Bestimmung der Wärmeeinbringung und der Schmelzbadgeometrie ist. Das entwickelte Modell wurde anhand der experimentellen Untersuchungen validiert und die Bedeutung der Temperaturabhängigkeit bei der Laserstrahlabsorption wurde für die Simulation des Laserstrahltiefschweißens quantifiziert.
In einem Forschungsvorhaben wurde der Einfluss von fertigungsbedingten Spalten von bis zu 3 mm auf das Tragverhalten der Widerstandspunktschweißverbindungen aus Stählen am Beispiel von HX340LAD+Z (Werkstoffnummer 1.0933), HCT780X+Z (1.0943), HCT980C (1.0955) und 22MnB5+AS140 untersucht. Neben spaltabhängigen Schweißbereichen wurden auch statische Festigkeit, dynamische Festigkeit sowie Schwingfestigkeit betrachtet. Schließlich wurden ein Prozesssicherheitskoeffizient sowie eine Prozess-Festigkeits-Kenngröße abgeleitet, mit deren Hilfe der Anwender das Verhalten der Punktschweißverbindungen unter Spalteinfluss beurteilen kann.
Die Beschichtung hochfester Stahlfeinbleche beeinflusst das Auftreten von flüssigmetallinduzierter Rissbildung (LME). Daher wurden in dieser Arbeit industrieübliche Beschichtungen bei gleichem Grundwerkstoff hinsichtlich ihres Aufbaus und chemischer Zusammensetzung charakterisiert und bezüglich ihrer LME Anfälligkeit untersucht. Aus dieser vergleichenden Untersuchung heraus wurden Potentiale für die Widerstandsfähigkeit gegen LME identifiziert. Diese Potentiale werden experimentell durch den Einsatz einer von der Forschungsstelle entwickelten Methode überprüft. Gegenstand der Untersuchungen waren neben unbeschichteten Proben industrieübliche Zinküberzüge wie Elektrolytisch verzinkt, Feuerverzinkt, Galvannealed und Zink-Magnesium Beschichtungen.
Die LME Anfälligkeit dieser unterschiedlichen Überzüge wird mit einem Schweißen unter Zugbelastung Versuchsaufbau untersucht. Dabei ergibt sich die resultierende Anfälligkeit aus den auftretenden Risslängen und der Auftrittswahrscheinlichkeit von LME bei den einzelnen Versuchen. Es konnte eine LME Anfälligkeits-Rangfolge für die Zinküberzüge festgestellt werden. Zink-Magnesium Beschichtungen galten als besonders LME Anfällig, gefolgt von Feuerverzinkt und Galvannealed. Die größte LME Resistenz wurde bei elektrolytisch verzinkten Proben festgestellt.
Aus den Ergebnissen werden Handlungsempfehlungen zur Erhöhung der Verarbeitungssicherheit bzw. Schweißpunktqualität abgeleitet.
Bei hochfesten austenitischen Stählen können unter den Produktionsbedingungen in der Rohkarosseriefertigung schweißbedingte Risse beim Widerstandspunktschweißen entstehen. Der Einfluss solcher Risse auf die dynamische Festigkeit ist derzeit nicht hinreichend bekannt. Im Rahmen dieser Arbeit wurden daher Schweißrisse verschiedener Lage und Ausbildung hinsichtlich ihrer Wirkung auf die Festigkeit und das Bruchverhalten von Widerstandspunktschweißverbindungen im Hochgeschwindigkeitsscherzug untersucht. Dabei konnte durch die Analyse der Kraft-Weg-Verläufe, der Scherzugfestigkeit und des Energieaufnahmevermögens nachgewiesen werden, dass Oberflächenrisse im Übergangsbereich und im Randbereich des Elektrodeneindrucks bei den hier vorliegenden Bedingungen keinen negativen Einfluss auf die dynamische Festigkeit haben. ----------------------------------------------------------------------------------------------------------------------------------------------------------------------------------
In the case of high-strength austenitic steels, welding-induced cracks may arise during resistance spot welding in the rough conditions of body shell fabrication. The influence of such cracks on the dynamic strength is not sufficiently well-known at present. Within the framework of this paper, welding cracks in various positions and with various formations were therefore investigated with regard to their effect on the strength and fracture behaviour of resistance-spot-welded joints subjected to high-speed shear tension. In this respect, the analysis of the force/displacement courses, the tensile shear strength and the energy absorption capacity served to prove that surface cracks in the interfacial region and in the peripheral region of the electrode indentation do not have any negative influence on the dynamic strength for the tested circumstances.
Unter den rauen Bedingungen in der Automobilkarosseriefertigung lassen sich schweißbedingte Imperfektionen wie Risse beim Widerstandspunktschweißen von hochfesten Stählen nicht immer vermeiden. Dabei ist der Einfluss solcher Risse auf die Schwingfestigkeit insbesondere von modernen hochfesten austenitischen Stählen derzeit nicht hinreichend bekannt. Im Rahmen dieser Arbeit wurde daher der Einfluss von Schweißrissen verschiedener Lage und Ausbildung untersucht. Dabei konnte durch die Analyse der normierten Steifigkeitsverläufe von Proben sowie durch die Gegenüberstellung der Versagensschwingspielzahlen nachgewiesen werden, dass die spritzerfrei erzeugten Oberflächenrisse im Zentrum, im Übergangsbereich sowie im Randbereich der Schweißlinse keinen negativen Einfluss auf die Schwingfestigkeit des hier untersuchten hochfesten austenitischen Werkstoffs haben. Proben, die mit Schweißspritzern hergestellt wurden und Risse im Randbereich aufweisen, zeigen deutliche höhere Versagensschwingspielzahlen als rissfreie Referenzproben. ----------------------------------------------------------------------------------------------------------------------------------------------
In the rough conditions in the fabrication of automobile bodies, it is not always possible to avoid welding-induced imperfections such as cracks during the resistance spot welding of highstrength steels. In this respect, the influence of such cracks on the fatigue strength particularly of modern high-strength austenitic steels is not sufficiently well-known at present. The influence of welding cracks with various positions and formations was therefore investigated within the framework of this paper. In this case, the analysis of the standardised stiffness courses of specimens and the comparison of the numbers of failure stress cycles served to prove that the surface cracks produced without any spatter in the centre, interfacial region and peripheral region of the weld nugget do not have any negative influence on the fatigue strength of the high-strength austenitic material investigated here. Specimens which were manufactured with welding spatter and exhibit cracks in the peripheral region show considerably higher numbers of failure stress cycles than crack-free reference specimens.
Diese Arbeit zeigt erstmals die Anwendung einer elektromagnetischen Schmelzbadsicherung beim einlagigen MSG-Schweißen von dickwandigen Stählen. Die innovativen Entwicklungen im Bereich des Lichtbogenschweißverfahrens ermöglichen eine Erhöhung der Abschmelzleistung, um die Einschweißtiefe zu steigern. Somit kann die Lagenanzahl reduziert und die Produktivität gesteigert werden. Allerdings besteht insbesondere beim einlagigen Schweißen von dickwandigen Bauteilen in PA-Position ein erhöhtes Risiko für das gravitationsbedingte Austropfen der Schmelze an der Wurzel. Zur Verhinderung werden Badsicherungen eingesetzt, die mechanisch angebracht und nach dem Schweißen entfernt werden müssen, was zeit- und kostenintensiv ist.
Die im Rahmen dieser Studie eingesetzte elektromagnetische Schmelzbadsicherung wirkt dem gravitationsbedingten Austropfen der Schmelze entgegen und kompensiert den hydrostatischen Druck. Sie wirkt kontaktlos, was im Gegensatz zu herkömmlichen Badsicherungen vorteilhaft ist, so dass auf eine zeit- und kostenintensive Nachbearbeitung der Schweißnahtwurzel verzichtet werden kann. Das auf extern angelegten oszillierenden Magnetfeldern beruhende Verfahren wird dabei unterhalb des zu schweißenden Bauteils positioniert. Die Magnetfeldlinien sind quer zur Schweißrichtung ausgerichtet, sodass längs zur Schweißrichtung Wirbelströme im Werkstück und eine stets nach oben gerichtete Lorentzkraft generiert werden. Mit Hilfe der elektromagnetischen Badsicherung konnten beim einlagigen MSG-Schweißen von bis zu 10 mm dicken Blechen die Tropfenbildung vermieden werden. Die innovative Technologie ermöglicht es, dickwandige Bauteile einlagig zu schweißen und reduziert die Nachbearbeitungszeiten und -kosten deutlich.
Der Fokus des vorliegenden Beitrages liegt in der Anwendung der numerischen Schweißsimulation zur Berechnung des schweißbedingten Verzugs an industriellen Bauteilen. Anhand einiger Applikationsbeispiele werden die Möglichkeiten und Einschränkungen am Markt verfügbarer Softwareprodukte aufgezeigt. Hierbei liegt die Gewichtung in einer qualitativ korrekten Abbildung der zu analysierenden Phänomene. Diese stellt die Basis für nachfolgende Parameterstudien dar, welche signifikante Einflussgrößen auf die Verzugsausbildung detektieren. Der Vorteil derartiger simulationsgestützter Analysemethoden gegenüber rein experimentellen Ansätzen wird diskutiert. Aufgrund der heutigen Verfügbarkeit spezialisierter anwenderfreundlicher Schweißsimulationssoftware und günstiger Rechenressourcen macht die Industrie in den letzten Jahren immer mehr von den zahlreichen Vorteilen einer virtuellen Prozessauslegung mit Hilfe der Schweißsimulation Gebrauch. Komplexe Praxisanwendungen können heutzutage innerhalb von 1-2 Wochen unter Berücksichtigung aller Arbeitsschritte bearbeitet werden. Die Anforderungen an den Anwender seitens der Numerik und Materialmodellierung hat sich drastisch verringert, wohingegen ein gewisses Maß an Wissen und Erfahrung vom simulierten Prozess weiterhin entscheidend für den Erfolg der Simulation ist. Am Beispiel des Einspritzventils konnte das Potential einer virtuellen Prozessauslegung anschaulich aufgezeigt werden.
Die experimentellen Untersuchungen innerhalb dieses Berichtes zeigen die erfolgreiche Anwendung einer elektromagnetischen Schmelzbadstütze beim Laser-strahl(hybrid)schweißen von ferromagnetischen Stäh-len mit einer Werkstückdicke von bis zu 20 mm. Bis-lang wurde dieses System zur Kompensation des hydrostatischen Druckes von Aluminiumlegierungen und austenitischen Stählen eingesetzt. Zunächst wur-den die Versuche an Duplexstählen vorgenommen, die jeweils zur Hälfte aus Austenit und Ferrit bestehen. Im Anschluss daran wurden die Versuche auf bis zu 20 mm dicke Werkstücke aus Baustahl erweitert. In-nerhalb der Versuchsreihen wurden die AC-Leistung sowie die Oszillationsfrequenz variiert. Für Werk-stückdicken von 15 mm war eine AC-Leistung von ca. 1 kW notwendig, um die Wurzelüberhöhung in die Bewertungsgruppe B der für laserstrahlgeschweißten Stähle gültigen DIN EN ISO 13919-1:1996-09 einord-nen zu können. Mit zunehmender AC-Leistung wird die Wurzelüberhöhung sukzessive reduziert. Nach erfolg-reicher Erweiterung auf ferromagnetische Werkstoffe wurde die Anwendung der Technologie für das Laser-strahlhybridschweißen demonstriert, indem praxisrele-vante Y-Nähte an 20 mm dicken Baustählen ohne Wurzelüberhöhung einlagig in Wannenlage geschweißt wurden. Trotz der Beeinflussung des Lichtbogens durch das oszillierende Magnetfeld sowie des zusätz-lich zum hydrostatischen Druck zu berücksichtigenden Lichtbogendruckes wurde eine ideale Kompensation auf der Wurzelseite erzielt.
Die Erweiterung des Anwendungsspektrums der elekt-romagnetischen Schmelzbadstütze auf ferromagneti-sche Werkstoffe sowie auf das Laserstrahlhybrid-schweißen eröffnet für zukünftige industrielle Anwen-dungen ein großes Potenzial. Das einlagige Schwei-ßen dickwandiger Bauteile mittels Hochleistungslasern wird in Kombination mit der elektromagnetischen Schmelzbadstütze attraktiver. In nachfolgenden Un-tersuchungen wird der Einsatz der elektromagneti-schen Schmelzbadstütze beim Laserstrahlhybrid-schweißen von Pipelinestählen angestrebt, v. a. im Hinblick auf die Spaltüberbrückbarkeit und der me-chanisch-technologischen Eigenschaften der Schweißverbindungen. Zudem ist beim Schweißen von Duplexstählen der Einsatz von Zusatzwerkstoffen zu berücksichtigen, um das Gleichgewicht zwischen austenitischer und ferritischer Phasen zu stabilisieren.
An oscillating (AC) magnet field was used to suppress porosity formation and to stabilize the surface of the weld pool in bead-on-plate partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 plates in PA position. The magnet was mounted on the laser welding head. The magnet field (up to 0.4 T and 10 kHz) was oriented perpendicular the welding direction.
The analysis of the weld cross-sections and x-ray images shows a drastic reduction (up to 90%) of porosity contents in the welds. The observed effects can be explained in terms of electromagnetically (EM)
induced 'Archimedes' forces as well as the EM stirring flow in the weld pool. Moreover, usage of AC magnetic fields results in a significant reduction (up to 50%) of the surface roughness of the welds. This effect can be explained in terms of electromagnetic (EM)
contribution to the surface tension (the Garnier-Moreau effect)
The present paper investigates the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm aluminum die casting AlSi9MnMg. Applying an electromagnetic field, a significant reduction of the porosity as well as smoothing of the surface of aluminum die casting can be observed. Starting from the reference case without an electromagnetic support, the porosity was reduced by 76 %. Especially big pores can be removed from the weld pool effectively due to their beneficial volume-to-area ratio whereas very small metallurgical pores tend to remain within the weld pool even when higher magnetic flux densities are applied.
Elektromagnetische Porenreduktion beim Laserstrahlschweißen von Aluminium-Druckgusslegierungen
(2019)
Innerhalb der vorliegenden Untersuchung wurde ein elektromagnetisches Schmelzbadbeeinflussungssys-tem zur Reduktion des Porenanteils beim Laserstrahlschweißen von Aluminium-Druckguss verwendet. Hierbei wird der Unterschied der elektrischen Leitfähigkeiten zwischen Gas- bzw. Lufteinschlüssen und geschmolzenem Aluminium gezielt genutzt, um die im Schmelzbad eingeschlossenen Poren während des Laserstrahlprozesses zur Oberfläche zu verdrängen. Die dafür erforderlichen Lorentzkräfte werden durch ein oszillierendes Magnetfeld erzeugt. Bei den Laserstrahlschweißversuchen handelt es sich um Ein-schweißungen in Wannenlage (PA-Position) von 6 mm dickem Aluminium-Druckguss AC-AlSi9MnMg. Über einen zuvor optimierten Laserschweißprozess wurde durch zusätzlichen Einsatz eines elektromag-netischen Feldes dessen Wirkung hinsichtlich des Porengehaltes und der Oberflächenrauheit untersucht. Die Auswertung der Schweißnähte erfolgte anhand von Querschliffaufnahmen, Röntgenbildern sowie Computer-Tomographie (CT) Aufnahmen. In Abhängigkeit von der verwendeten magnetischen Fluss-dichte konnte eine Reduktion des Porenanteils von bis zu 75 % erzielt werden, wobei vor allem großvolu-mige Poren erfolgreich aus dem Schmelzbad entfernt werden konnten. Zudem konnte eine Reduktion der Oberflächenrauigkeit von ebenfalls bis zu 75 % erreicht werden.
Die technischen Entwicklungen in der Lasertechnologie in den letzten Jahrzehnten haben eine neue Generation von Hochleistungslasersystemen im Leistungsbereich bis zu 100 kW auf den Markt gebracht. Dennoch ist die industrielle Anwendung des Hochleistungslaserstrahlschweißens auf bis zu 15 mm dicke Bleche beschränkt. Mögliche Ursachen der Einschränkungen des Verfahrens sind z.B. die Sensibilität des Verfahrens auf Fertigungstoleranzen wie Spalt und Kantenversatz, die erhöhte Tropfenbildung bei höheren Blechdicken und eine inhomogene Verteilung des Zusatzwerkstoffes beim Laserhybridschweißen. In dieser Studie wird ein auf extern angelegte Magnetfelder basierte elektromagnetische Schmelzbadstütze eingesetzt, um die Grenzen des Verfahrens zu erweitern und die Herausforderungen zu minimieren. Der wesentliche Vorteil der elektromagnetischen Schmelzbadstütze ist, dass sie berührungslos arbeitet. Mit Hilfe der elektromagnetischen Schmelzbadstütze konnten bei 20 mm dicken Proben aus S355J2 die Tropfenbildung an der Wurzel vermieden werden. Zudem wurde der Einfluss der Kantenqualität auf die Schweißnahtqualität untersucht, wobei verschiedene Schneidverfahren zur Kantenvorbereitung eingesetzt wurden, wie z.B. Plasma-, Brenn- oder Laserschneiden. Es konnte gezeigt werden, dass auch bei schlechteren Kantenvorbereitung im Gegensatz zu gefrästen Bauteilen die Werkstoffe einlagig mittels Laserhybridschweißen bei einer hohen Schweißnahtqualität gefügt werden konnten. Bei plasmageschnittenen Proben wurden zudem eine Spaltüberbrückbarkeit bzw. Kantenversatz von bis zu 2 mm sicher überbrückt. Des Weiteren war es mit Hilfe der externen Magnetfelder möglich, die Durchmischung des Zusatzwerkstoffes über die gesamte Schweißnahttiefe deutlich zu homogenisieren.
The paper deals with the integration of a light emitting diode (LED) into an additive manufactured metal component. Selective laser melting (SLM) and laser metal deposition (LMD) are used. The material used is the chrome-nickel steel 316L. The basic component is manufactured by means of SLM and consists of a solid body and an area with grid structure. The solid body includes a duct in the shape of a groove with a recess for the positioning of the power cable. The LED is embedded in the grid structure via an inlet from the solid body. In further processing, the groove is filled with LMD. Two strategies with different parameter combinations were investigated. It shows that a high energy input near the power cable leads to its destruction. By using multiple parameter combinations during the manufacturing process, this destruction can be prevented. There was a comparison of both strategies with regard to the necessary number of tracks and duration of welding time.
Dieser Beitrag stellt Ergebnisse der Untersuchungen zum Auftragschweißen als Plasma-Laserstrahl-Hybrid-Prozess dar. Es hat sich gezeigt, dass ein Laserstrahl, der in einer gemeinsamen Prozesszone mit einem Plasma-Pulver-Auftragschweißprozess vorlaufend angeordnet ist, diesem Prozess eine erhebliche Geschwindigkeitssteigerung sowie eine Verbesserung der Stabilität ermöglicht. Der Hybrid-Prozess konnte mit Verschleißschutzwerkstoffen
sowie dem Korrosionsschutzwerkstoff Inconel 625 bei Vorschubgeschwindigkeiten von bis zu 10 m/min erfolgreich validiert werden.
Im Hinblick auf die aktuellen Entwicklungen zu Hochgeschwindiglceits-Laserstrahlauftragschweißen kann der Plasma-Laserstrahl-Hybrid-Prozess
zwischen diesen und den konventionellen Verfahren eingeordnet werden.
Die stetig zunehmenden Anforderungen hinsichtlich geringeren Kraftstoffverbrauchs, verminderter Schadstoffemission sowie der Erhöhung der passiven Sicherheit haben die Automobilindustrie vor Herausforderungen gestellt, denen nur durch einen konsequenten Einsatz moderner Stahlwerkstoffe zu begegnen ist. Die komplexe Gefügestruktur sowie die besonderen mechanischen Eigenschaften dieser Werkstoffe verursachen jedoch eine erhöhte Neigung zur Ausbildung von Rissen insbesondere bei Widerstandspunktschweißverbindungen.Insbesondere für kleine und mittelständische Unternehmen, die keine zeitaufwendigen und teuren Voruntersuchungen bezüglich der Rissanfälligkeit von Stählen während des Widerstandspunktschweißens durchführen können, ist zum Erhalt der Wettbewerbsfähigkeit die Kenntnis der Rissanfälligkeit einer von ihnen zu verarbeitenden Materialkombination von erheblicher Bedeutung. Durch eine einfach durchzuführende, werkstoffunabhängige Methode zur Bestimmung der Rissanfälligkeit beim Widerstandspunktschweißen, kann den KMUs die Möglichkeit zur schnellen und kostengünstigen Bewertung der Verarbeitungssicherheit zu verarbeitender Materialverbindungen bereitgestellt werden. Ziel des Forschungsvorhabens ist daher die Entwicklung einer einfachen und fertigungsnahen Methode zur Bestimmung der Rissanfälligkeit hochfester Stähle während des Widerstandspunkschweißens, die auf der gezielten, reproduzierbaren Erzeugung von Rissen basiert. Es wurde eine solche Prüfmethodik entwickelt, die auf einfach durchzuführenden experimentellen Versuchen basiert. Zu untersuchende Proben werden während des Schweißvorgangs mit einer Zugkraft belastet. Hierfür wird eine hydraulische Vorrichtung genutzt, die taillierte Flachzugproben mit definierter Kraft beaufschlagt. Infolge dessen stellt sich ein Spannungszustand ein, der die Rissbildung begünstigt. Somit können ausreichende Rissentstehungsraten erzielt werden, die eine vergleichende Beurteilung der resultierenden Risslängen zwischen den Werkstoffen zulassen. Die einfache, mobile Zugvorrichtung ermöglicht eine Nutzung der bestehenden Anlagentechnik. Durch eine Normierung der resultierenden Risslängen auf die Streckgrenze des Werkstoffs und die belastete Querschnittsfläche lassen sich ein Werkstoffranking beziehungsweise eine Klassifizierung der Rissanfälligkeit der untersuchten hochfesten Materialkombinationen erstellen. Auch zukünftig entwickelte Stahlwerkstoffe potentiell höherer Festigkeiten können untersucht werden. Weiterhin kann die entwickelte Methode als Grundlage für die Gewinnung von Basisdaten zur Untersuchung verschiedener Rissentstehungsarten während des Widerstandspunktschweißens eingesetzt werden.
Entwicklung eines Verfahrens zur Untersuchung der Heißrissresistenz lasergeschweißter Verbindungen
(2016)
In den letzten Jahrzehnten hat sich die Strahlschweißtechnik signifikant weiterentwickelt und als effizientes und wirtschaftliches Werkzeug in der Industrie etabliert. Für die Untersuchung der Heißrissresistenz verschiedener Werkstoffe existieren zahlreiche eigen- und fremdbeanspruchende Tests. Diese wurden aber speziell für andere Schweißverfahren, insbesondere das Lichtbogenschweißen, konzipiert.
Daher besteht die Notwendigkeit eines geeigneten Heißrisstests, bei dem Werkstoffe realen Strahlschweißbedingungen ausgesetzt werden können. Die Entwicklung sowie die Standardisierung einer aussagekräftigen experimentellen Methode stellen einen wichtigen Schritt auf dem Weg zur Vermeidung von Heißrissen und damit für die Gewährleistung der Sicherheit von gefügten Bauteilen dar. Ziel der Forschungsarbeiten ist es, einen geeigneten Test zur effektiven Untersuchung der Heißrissanfälligkeit von lasergeschweißten Verbindungen zu konzipieren und zu entwickeln.
•Main Welding Technologies in the Automotive: RSW and laserbeam welding
•Light Weight Design leads to increasing use of AHSS and UHSS which results in higher demands for the joining technology
•Joining Multi-Material Structures offers opportunities for “new” Thermal-Mechanical Joining Processes and Hybrid Processes
•In the coming years a trend towards sustainable manufacturing can be seen. Comparison between laserbeam and RSW will be a tight match!
This study presents mechanisms of the evolution of a narrowed region in the weld pool center during deep penetration laser beam welding. In numerous numerical studies presented in this study, it was also found that the local reduction of the weld pool size can cause detrimental effects on the melt flow behavior and the resulting properties of the welds. A particularly large influence of this effect was identified in three aspects. Firstly, the local variation of the solidification sequence of the weld pool causes an increase in the hot-cracking susceptibility due to a locally delayed solidification. Secondly, it was proven that a change in the local length and width of the weld pool is associated with an adverse impact on the potential flow routes of the molten material that induces stronger local variations of its solidification. Thus, the element mixing, e.g. during the welding with filler materials, is blocked. This leads to a non-homogeneous chemical composition of the final weld and can cause undesired effects on the final material properties. Finally, another observed effect is related to the reduced ability of process pores to reach the top surface. As this type of porosity is usually produced around the keyhole tip, the change of the fluid flow regime above this area plays a significant role in determining the final path of the pores until the premature solidification in the middle of the weld pool captures them. This study summarizes mainly numerical results which were supported by selected experimental validation results.
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
The magnetohydrodynamic (MHD) technology is recognized as a promising approach for improving the quality of deep penetration laser beam welding. This study employs experimental and numerical methods to investigate the effects of an auxiliary oscillating magnetic field on reducing porosity in the laser beam welding of 5754
aluminum alloy. The experimental results clearly demonstrate a significant reduction of 97% in the porosity ratio of the welded joints applied with an oscillating magnetic field compared to those without magnetic field, thereby validating the efficiency of applying MHD technology in mitigating porosity during the laser beam welding process. In addition, a transient 3D multi-physical model has been developed, integrating the MHD model and metal vapor plume, to gain a more comprehensive understanding of the porosity suppression mechanism. The weld pool shape is significantly widened and enlarged because of the Lorentz force, which facilitates the escape of gas bubbles. Meanwhile, the introduction of an oscillating magnetic field generates a time-averaged downward Lorentz force. This averaged downward Lorentz force, in turn, enhances and stables the downward fluid flow, which hinders the bubble backward movement. Meanwhile, this averaged downward Lorentz force induces an upward electromagnetic expulsive force on the bubble, which effectively increases the upward escape velocity of bubbles in the weld pool. The simulation results agree well with the experimental results.
Through experimental observation and auxiliary numerical simulation, this investigation studies the different types of grain refinement of 5754 aluminum alloy laser beam welding by applying a transverse oscillating magnetic field. Scanning electron microscope results have proved that the application of a magnetic field can reduce the average crystal branch width and increase its number. The interaction between the induced eddy current generated by the Seebeck effect and the applied external magnetic field produces a Lorentz force, which is important for the increase in the number of crystal branches. Based on the theory of dendrite fragmentation and the magnetic field-induced branches increment, the grain size reduction caused by the magnetic field is studied. Furthermore, the effects of the magnetic field are ana lyzed by combining a phase field method model and simulations of nucleation and grain growth. The grain distribution and average grain size after welding verify the reliability of the model. In addition, the introduction of a magnetic field can increase the number of periodic three-dimensional solidification patterns. In the intersection of two periods of solidification patterns, the metal can be re-melted and then re-solidified, which prevents the grains, that have been solidified and formed previously, from further growth and generates some small cel lular grains in the new fusion line. The magnetic field increases the building frequency of these solidification structures and thus promotes this kind of grain refinement.
Through experimental observation and auxiliary numerical simulation, this investigation studies the different types of grain refinement of 5754 aluminum alloy laser beam welding by applying a transverse oscillating magnetic field. Scanning electron microscope results have proved that the application of a magnetic field can reduce the average crystal branch width and increase its number. The interaction between the induced eddy current generated by the Seebeck effect and the applied external magnetic field produces a Lorentz force, which is important for the increase of the number of crystal branches. Based on the theory of dendrite fragmentation and the magnetic field-induced branches increment, the grain size reduction caused by the magnetic field is studied. Furthermore, the effects of the magnetic field are analyzed by combining a phase field method model and simulations of nucleation and grain growth. The grain distribution and average grain size after welding verifies the reliability of the model. In addition, the introduction of a magnetic field can increase the number of periodic three-dimensional solidification patterns. In the intersection of two periods of solidification patterns, the metal can be re-melted and then re-solidified, which prevents the grains that have been solidified and formed previously from further growth and generates some small cellular grains in the new fusion line. The magnetic field increases the building frequency of these solidification structures and thus promotes this kind of grain refinement.
Experimental investigation of the laser-plume interaction during high power fiber laser welding
(2011)
The effect of the well-known plasma absorption and refraction in CO2-laser metal welding plumes is in case of high power solid state laser welding negligibly small. By contrast, the diffraction effects of shorter wavelength laser radiation are considerable. According
to the results of preliminary studies, the fine condensed metal particles in the welding plume can lead to essential worsening of the laser beam quality.
This work is devoted to the investigation of the lasermatter interaction during up to 20 kW ytterbium fiber laser welding of thick mild steel plates. The plume attenuation of a probe 1.3 µm wavelength diode laser beam as well as of continuous radiation in 250-600 nm
wavelength range was measured during welding with and without Ar shielding gas supply. The measured results allow it to calculate average size and concentration of fine condensed metal particles in
different plume areas using the multi-wavelength method and the Mie scattering theory. The plume temperature, which determines the condensation conditions, was measured by means of Fe I atom
spectral line emission registration.
The obtained results can be also of interest for remote metal treatment with high-power fiber or disc lasers.
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Experimental study and numerical simulation of hot crack formation for novel laser weldability test
(2015)
Hot cracking susceptibility in laser beam welding was assessed for several stainless steels by means of the CTW test
The strain rate has a significant influence on the formation of the hot crack
It was possible to determine the critical strain and strain rate that led to shot crack formation
A material ranking of hot cracking resistance could be made.A three-dimensional FEM using the contact element technique to simulate hot cracking during LBW under external load conditions was developed.
Good agreement between the strain field measured using the DIC technique and the simulation results
Susceptibility to hot cracking can be predicted by using FEM with the correct mechanical and thermo-physical material properties
Experimental study and numerical simulation of hot crack formation for novel laser weldability test.
(2015)
Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials.
Die in dieser Studie vorgestellte einfache Probengeometrie zeigt sich in Verbindung mit der
angewandten Versuchs- und Auswertemethodik geeignet, um den umwandlungsplastischen (TRIP)-Parameter K unter Verwendung des thermomechanischen Simulators Gleeble® 3500 experimentell zu bestimmen.
Der TRIP-Parameter K wurde für die Grundwerkstoffe S355J2+N und S960QL, sowie für den hochlegierten Zusatzwerkstoff CN13-4 -IG bestimmt.
Die numerische Einflussanalyse zeigt, dass bei der Berechnung von (Oberflächen-)Schweißeigen-spannungen die Vernachlässigung des TRIP-Effektes kaum einen Einfluss auf die Längseigenspannungen hat. Im Gegensatz da zu resultieren gegenüber dem Referenzfall signifikante Abweichungen der
Quereigenspannungen im und um den Schweißnahtbereich.
Die Verdopplung des TRIP-Parameters K gegenüber dem Referenzfall hat nur einen vernachlässigbaren Einfluss auf die Längs- sowie Quereigenspannungen auf der Oberfläche.
Für eine qualitative und quantitative numerische Nachbildung der experimentell bestimmten Längs- und Quereigenspannungen ist die Berücksichtigung der Größenordnung des material-abhängigen TRIP-Parameters K notwendig.
Experimentelle und numerische Analyse des Geometrieeinflusses auf den Schweißeigenspannungszustand
(2009)
Die vorliegende Arbeit stellt Untersuchungen im Rahmen eines Forschungsprojektes mit Schwerpunkt in der experimentellen und numerischen Analyse schweißbedingter Eigenspannungen und Verzüge beim Mehrlagenschweißen dar. Das Auftreten von kritischen Eigenspannungszuständen und untolerierbaren Verzügen während des Fertigungsprozesses verursacht durch erforderliche Nacharbeiten, wie z.B. Richten oder Wärmenachbehandlungen, zusätzliche Kosten. Diese Nacharbeiten können vermieden werden, wenn die numerische Schweißsimulation auf der Grundlage von zuverlässigen Berechnungsergebnissen zur Optimierung angewandt wird.
Die Analyse des Eigenspannungszustandes erfolgt an 5 mm dicken Blechen des unlegierten Baustahls S355J2, wobei Stumpfnaht-Verbindungen mittels Metall-Aktiv-Gas-(MAG)-Schweißen ausgeführt worden sind. Im Zusammenhang mit den Experimenten werden sowohl Temperaturzyklen und Eigenspannungen gemessen als auch Schmelzbadgeometrie und Mikrostruktur ermittelt.
Auf der Basis eines experimentell validierten Temperaturfeldes und umfangreichen röntgenografischen Eigenspannungsuntersuchungen erfolgen numerische Strukturberechnungen. Die auftretenden Phasenumwandlungen werden in der Simulation berücksichtigt.
Die Betrachtung verschiedener Blechkonfigurationen gibt den Einfluss der Blechlänge auf das Niveau der entstehenden Eigenspannungen wieder. Es stellt sich heraus, dass sich die Quereigenspannungen in den nahtnahen Bereich mit zunehmender Blechlänge in den Druckbereich verschieben. Dieses Verhalten kann durch die experimentell validierte Struktursimulation des vorliegenden Prozesses numerisch abgebildet werden und schafft somit den Ausgangspunkt für die spätere Berechnung von mehrlagigen Schweißnähten.
Extended weldability lobes in resistance spot welding of advanced high strength steels (AHSS)
(2009)
The objective of this paper is to demonstrate a new simulation technique which allows the fast and automatic generation to temperature fields based on a combination of empirical and phenomenological modelling techniques. The automatic calibration of the phenomenological model is performed by a multi-variable global optimisation routine which yields the optimal fit between simulated and experimental weld charcteristics without the need for initial model parameters. For exemplary welding processes it is shown that linear 3D heat conduction models can approximate measured temperature fields with a high accuracy. The modelling approach presented comprises the automatic calibration against multiple experiments which permits simulating the temperature field for unknown process parameters. The validation of this composite simulation model is performed for exemplary welding processes and includes the prediction of the fusion line in the cross section and the corresponding thermal cycles.
Fast temperature field generation for welding simulation and reduction of experimental effort
(2009)
The quality of welding processes is governed by the occurring induced distortions yielding an
increase in production costs due to necessary reworking. Especially for more complex specimens
it is difficult to evaluate the optimal configuration of welding sequences in order to
minimise the distortion. Even experienced welding operators can solve this task only by trial
and error which is time and cost consuming.
In modern engineering the application of welding simulation is already known to be able to
analyse the heat effects of welding virtually. However, the welding process is governed by
complex physical interactions. Thus, recent weld thermal models are based on many simplifications.
The state of the art is to apply numerical methods in order to solve the transient heat
conduction equation. Therefore, it is not possible to use the real process parameters as input
for the mathematical model. The model parameters which allow calculating a temperature
field that is in best agreement with the experiments cannot be defined directly but inversely by
multiple simulations runs. In case of numerical simulation software based on finite discretisation
schemes this approach is very time consuming and requires expert users. The weld
thermal model contains an initial weakness which has to be adapted by finding an optimal set
of model parameters. This process of calibration is often done against few experiments. The
range of model validity is limited. An extension can be obtained by performing a calibration
against multiple experiments.
The focus of the paper is to show a combined modelling technique which provides an efficient
solution of the inverse heat conduction problem mentioned above. On the one hand the inverse
problem is solved by application of fast weld thermal models which are closed form
solutions of the heat conduction equation. In addition, a global optimisation algorithm allows
an automated calibration of the weld thermal model. This technique is able to provide a temperature
field automatically that fits the experimental one with high accuracy within minutes
on ordinary office computers. This fast paradigm permits confirming the application of welding
simulation in an industrial environment as automotive industry.
On the other hand, the initial model weakness is compensated by calibrating the model
against multiple experiments. The unknown relationship between model and process parameters
is approximated by a neural network. The validity of the model is increased successively
and enables to decrease experimental effort. For a test case it is shown, that this approach
yields accurate temperature fields within very short amount of time for unknown process parameters
as input data to the model contributing to the requirement to construct a substitute
system of the real welding process.