Synchrotron radiation X-ray fluorescence spectroscopy, in conjunction with atomic absorption and Raman spectroscopy, was used to analyze a set of top brand tattoo inks to investigate the presence of toxic elements and hazardous substances. The Cr, Cu, and Pb contents were found to be above the maximum allowed levels established by the Council of Europe through the resolution ResAP(2008)1 on requirements and criteria for the safety of tattoos and permanent makeup. Raman analysis has revealed the presence of a set of prohibited substances mentioned in ResAP(2008)1, among which are the pigments Blue 15, Green 7, and Violet 23. Other pigments that were identified in white, black, red, and yellow inks are the Pigment White 6, Carbon Black, Pigment Red 8, and a diazo yellow, respectively. The present results show the importance of regulating tattoo ink composition.
Increasing numbers of implant revisions are a current clinical issue. Interactions of the endoprosthesis biomaterial with the body affect implantation time by wear processes, i.e. corrosion and abrasion. Previously, cobalt-chrome implants were shown to cause high levels of cobalt ions being deposited in the bone matrix. To determine a poten- tial functional role of these ions on bone homeostasis, we have developed a non-destructive dual analysis of highly sensitive elemental analysis by synchrotron XRF directly in undecalcified histological bone thin sections (4 μm). In this study, samples from 28 bone samples from hip endoprosthesis carriers (Surface Replacement Arthroplasty, metal-on-metal bearing) with an implant lifetime of 17–1750 days were used. Results were compared to age- matched control specimens. The histological analysis identified areas of bone cell activity and assigned them for XRF measurements. Co-Cr wear particles were identified in the bone marrow. In addition, Co ions were highly enriched in the mineralized bone matrix. The cobalt deposits were not homogeneously distributed, and areas of high signal intensity were identified. Co was distinctly deposited in the newly formed osteoid layer, but also within deeper layers of the bone matrix, whereby the Co concentration increased with higher degrees of bone matrix mineralization. In the current study, we determined cobalt accumulations in the bone matrix and showed for the first time via synchrotron XRF with a high spatial resolution direct on histological slides, that cobalt deposits in the mineralized bone matrix in a mineral-specific way that is dependent upon the implant lifetime.
The precise analysis of cation diffusion profiles through corrosion scales is an important aspect to evaluate corrosion phenomena under multicomponent chemical load, as during high‐temperature corrosion under deposits and salts. The present study shows a comprehensive analysis of cation diffusion profiles by electron microprobe analysis and microbeam X‐ray absorption near edge structure (µ‐XANES) spectroscopy in mixed oxide/sulfide scales grown on Fe–Cr model alloys after exposing them to 0.5% SO2. The results presented here correspond to depth‐dependent phase identification of oxides and sulfides in the corrosion scales by µ‐XANES and the description of oxidation‐state‐dependent diffusion profiles. Scales grown on low‐ and high‐alloyed materials show both a well‐pronounced diffusion profile with a high concentration of Fe3+ at the gas and a high concentration of Fe2+ at the alloy interface. The distribution of the cations within a close‐packed oxide lattice is strongly influencing the lattice diffusion phenomena due to their different oxidation states and therefore different crystal‐field preference energies. This issue is discussed based on the results obtained by µ‐XANES analysis.
Besides conventional scanning X-ray fluorescence imaging at synchrotron sources, full-field X-ray fluorescence (FF-XRF) imaging techniques that do not implicitly require spatial scanning of the sample have become available. FF-XRF has become achievable thanks to the development of a new type of energy dispersive CCD-based 2D detector, also referred to as a 'color X-ray camera (CXC)' or 'SLcam'. We report on different imaging schemes for biological samples using FF-XRF imaging: (a) 2D 'zoom' imaging with pinhole optics using the 'camera obscura' principle; (b) 2D 'fixed magnification' imaging using magnifying polycapillary optics; and (c) 3D-FF-XRF imaging using an X-ray sheet beam or computed tomography (CT). The different FF-XRF imaging modes are illustrated using the crustacean Daphnia magna, a model organism for investigating the effects of metals on organism/ecosystem health, and foraminifera, a class of amoeboid protist. Detailed analytical characterization of the set-up is performed through analyzing various reference materials in order to determine limits of detection (LODs) and sensitivities. Experiments were performed using the BAMline at the BESSY synchrotron (Berlin, Germany) and using the P06 Hard X-ray Microprobe at the PETRAIII synchrotron (Hamburg, Germany).
In this work, a new setup for dispersive XAFS measurements is presented. This reproducible and scanningfree setup yields both time- and laterally-resolved XAFS experiments in a ‘single-shot’. It allows a straightforward adjustment for probing different elements covering many relevant applications in materials science. An incoming energetic broadband beam is diffracted by a Si (111) crystal after passing through the sample and collected by an area sensitive detector. Depending on the energy range of the incoming beam, XANES and/or EXAFS spectra can be recorded with a time resolution down to 1 s. The feasibility of this setup was demonstrated at the BAMline at BESSY II (Berlin, Germany) with reference Fe and Cu foils and the results are hereby presented and discussed. Additionally, an application where time resolution on the second scale is required is briefly evaluated. The presented example concerns studying early stages of zinc(II)2-methylimidazolate (ZIF-8) crystallization. This is particularly important for biomedical applications.