The accurate determination of wear volumes is a prerequisite for the study of numerous tribological phenomena. Wear volumes can be measured with different techniques or else be calculated starting from some quantities measured from the wear scar. Advantages and drawbacks of the measuring techniques are shown by means of wear scars and calottes resulting from ball-on-plane tests with 100Cr6 specimens. When measuring wear volumes, white light interferometry results to be one of the most suitable techniques. When wear volumes are calculated, errors result mainly from two sources: (1) the arbitrary choice of one or few line profiles for the determination of the width and of the planimetric wear, and (2) approximations in the calculation, which are even necessary when values of the wear volumes of the single tribological partners and not only the total volume are of interest. The effect of both error sources on the accuracy in the determination of wear volumes is characterized and elucidated by examples. It is found that errors due to approximations are negligible when compared to errors due to the arbitrary choice of one line profile.
The influence of relative humidity on friction and wear is subject of several studies in the last decades. A comprehensive understanding of physical and chemical phenomena affecting the tribology is hampered by the lack of reproducible experimental results, by the large number of variables, and by several difficulties in the detection of tribochemical processes and products.
In the present work, we analyze the wear coefficient and the wear volumes of 686 unlubricated tests performed on different oscillating tribometers with 100Cr6 balls on 100Cr6 planes at different relative humidity.
Aim of this work is to assess the repeatability and reproducibility of data, to determine the dependence of the wear coefficient on the relative humidity, to understand the underlying physicochemical phenomena and to build three dimensional maps of the wear coefficient as a function of both humidity and the product of normal force and sliding distance.
Die vorliegende Doktorarbeit handelt von der Bestimmung und der Untersuchung vom Verschleißvolumen und vom Verschleißkoeffizienten bei ungeschmierten Modellversuchen an 100Cr6-Ebenen und -Kugeln unter Schwingungsbeanspruchung. Die experimentelle Arbeit wurde mittels statistischer Auswertung einer großen Menge von eigenen und früheren Versuchsdaten an fünf Tribometern bei umfangreicher Variation der Beanspruchungsparameter durchgeführt. Ziel war es, die Wiederholbarkeit und Reproduzierbarkeit der experimentellen Ergebnisse zu überprüfen sowie das Archard-Gesetz zu verifizieren. Des Weiteren wurde der Einfluss der Luftfeuchtigkeit auf den Verschleiß untersucht.
Considerable scattering of experimental wear results affects seriously the evaluation of repeatability and reproducibility of tribological measurements and hampers detecting, studying, and verifying tribological laws. An accurate characterization of the statistics of results, the detection of the influence of operating parameters, and the verification of equations describing tribological phenomena can be achieved only through the analysis of large datasets with wide variation of parameters. Taking advantage of more than 400 experiments performed with the same material pairing under the same conditions on four different tribometers, the repeatability and reproducibility of volumetric wear measurements has been evaluated using Welch's test.
By testing Archard's law over seven orders of magnitude of sFN, it was found that this law is not universally valid and that, under certain conditions, the wear coefficient depends on sFN itself.
Wear test results exhibit often large scattering. Hence, the study of spreading of experimental results requires big datasets.
In various studies, wear coefficients were found to have lognormal distributions. Therefore, it was supposed that the wear coefficient is affected by two normally distributed variables, which combine through a product.
In the present study, we demonstrate that a lognormal distribution may arise from a nonconstant wear coefficient, too, i.e., when a system does not follow Archard’s law.
We show for the first time tribotests performed with self-mated 100Cr6 steel, taking advantage of an AFM, employed as a tribometer for the tribotests as well as for the inspection of wear of both tribopartners. Emphasis is put on the morphology of the scars, on wear particles, and on wear of the “colloidal” particles glued on the AFM cantilever. Measurements demonstrate the possibility of characterizing single asperity events leading to very small wear. We highlight several phenomena, which are elementary key constituents of tribological processes. Such phenomena, probably occurring also at the macroscale, can be detected, identified, and characterized with high spatial and time resolution only at the nanoscale, thus giving insight into conditions and causes of their emergence.
Friction at the microscale during reciprocal sliding tribotests was studied for the first time with self-mated steel (100Cr6/AISI 52100) taking advantage of an atomic force microscope (AFM). To this aim, microsized steel particles were glued to the AFM-cantilever and employed as colloidal tips to perform tribotests on a steel disc. The torsion of the cantilever, which correlates with the friction force, was measured during the tests. Few tests with the same load did not yield any wear and show that the load and adhesion contributions to friction stay constant when the shape of the test particle does not change. Most of the presented tribotests engendered wear. For those tests, the increase of friction during the tribotests was attributed to the emerging plowing contribution. Furthermore, analysis of both torsion and local slope gives information on the creation of wear particles and their influence on friction.