Photo-oxidative ageing of polymers under defined exposure (UV, humidity) was investigated from two points of view: a) the ageing process Starts from the topmost surface and penetrates slowly towards bulk and b) radicals play an important role among ageing. Therefore, X-ray photoelectron (XPS) and electron spin resonance (ESR) spectroscopy were applied to show both, the progressive incorporation of oxygen during in-situ UV irradiation (XPS) and the formation of radicals (ESR) in the polymer. The intensity of ESR Signals served as measure for radical concentration. The Validation of this correlation was checked for polyethylenes (PE) equipped with different concentrations of Hostavin N30 UV stabilizer.
The outdoor weathering of polymers is mainly due to UV radiation, water, Pollution, humidity, temperature etc. To understand the effects of weathering, simulated tests need to be undertaken in lab scale. Such tests must be quite efficient and similar to the effects of natural weathering. This paper mainly focuses on the effects of UV radiation along with humidity on LDPE.
Artificial weathering of LDPE under dry conditions (<10% of relative humidity) by UV radiation was monitored
by dielectric spectroscopy. For an apolar polymer like LDPE, dielectric study yields information
about the change in structure and dynamics of the system. The fluctuations of the polar groups which
are generated as a result of photooxidation such as carbonyl groups can be monitored as characteristic
relaxation processes like the αc or β mode. The dielectric loss characterized by typical dielectric parameters
like the activation energy and dielectric strength are strongly dependent upon changes induced
by photooxidation in the amorphous and crystalline domains. This paper discusses in detail how the foil
reached its mechanical disintegration. It was found that initial stages of weathering induce chain scission
and/or crosslinking in the amorphous domains of the polymer and the motional processes in the crystalline
regions are not affected. After this induction period, an increase in the degree of crystallization was
observed by employing differential calorimetry. The increasing crystallinity is considered as one of the
reasons for embrittlement which finally leads to the complete loss of the structural integrity.
For simulation and acceleration of artificial polymer ageing, polyolefin foils were exposed to low-pressure Ar plasma. Plasma particle bombardment and irradiation induce C–C and C–H bond scissions by σ→σ* excitations on the surface and in near-surface layers. Consequently, radicals are generated. They react by recombination, cross-linking, metastable trapping of the radical site or formation of olefinic double bonds. The long-living and metastable trapped C-radicals as well as double bonds in polyolefins were immediately exposed to bromine vapour without breaking the vacuum after switching-off the plasma. These reactive sites rapidly react with the molecular bromine under formation of C–Br bonds. For 5 min of argon plasma exposure, the elemental concentration of bromine was 13% for polyethylene and 22% Br/C for polypropylene as analysed by X-ray photoelectron spectroscopy. Nevertheless, not all C radical sites have reacted with bromine. Later on, when the polyolefins brought in contact with ambient air, an additional post-plasma reaction of the remaining trapped radicals with oxygen was observed. The oxygen concentrations were lower after bromine gassing, thus repressing partially the post-plasma oxidation in the analysed layer (ca. 6 nm) by radical quenching. Such bromination took place either at the surface or in near-surface layers because the Attenuated Total Reflectance (ATR)-FTIR spectra (sampling depth ca. 2500 nm) did not show significant changes for argon plasma-treated PE foils with and without bromine vapour exposure. Further addition of bromine may also occur on C=C double bonds.