We report the results of a Versailles Project on Advanced Materials and Standards interlaboratory study on the intensity scale calibration of x-ray photoelectron spectrometers using low-density polyethylene (LDPE) as an alternative material to gold, silver, and copper. An improved set of LDPE reference spectra, corrected for different instrument geometries using a quartz-monochromated Al Kα x-ray source, was developed using data provided by participants in this study. Using
these new reference spectra, a transmission function was calculated for each dataset that participants provided. When compared to a similar calibration procedure using the NPL reference spectra for gold, the LDPE intensity calibration method achieves an absolute offset of ∼3.0% and a systematic deviation of ±6.5% on average across all participants. For spectra recorded at high pass energies (≥90 eV), values of absolute offset and systematic deviation are ∼5.8% and ±5.7%, respectively, whereas for spectra collected at lower pass energies (<90 eV), values of absolute offset and systematic deviation are ∼4.9% and ±8.8%, respectively; low pass energy spectra perform worse than the global average, in terms of systematic deviations, due to diminished count rates and signal-to-noise ratio. Differences in absolute offset are attributed to the surface roughness of the LDPE induced by sample preparation. We further assess the usability of LDPE as a secondary reference material and comment on its performance in the presence of issues such as variable dark noise, x-ray warm up times, inaccuracy at low count rates, and underlying spectrometer problems. In response to participant feedback and the results of the study, we provide an updated LDPE intensity calibration protocol to address the issues highlighted in the interlaboratory study. We also comment on the lack of implementation of a consistent and traceable intensity calibration method across the community of x-ray photoelectron spectroscopy (XPS) users and, therefore, propose a route to achieving this with the assistance of instrument manufacturers, metrology laboratories, and experts leading to an international standard for XPS intensity scale calibration.
(1) First results show the suitability of IL as reference for quantification of XPS (at least for organic materials).
(2) Different quantification methods lead to similar results (with a slight advantage for “background method”).
(3)Promising reference material for a better understanding and traceable protocols for the quantification of organic materials with XPS.
X-ray photoelectron spectroscopy (XPS) is widely used for characterising the chemistry of graphene-related two-dimensional materials (GR2M), however the careful preparation of the sample for analysis is important in obtaining representative quantifications. We report an investigation by three laboratories showing that the preparation method for oxygen-functionalised graphene nanoplatelet (GNP) powders has a significant effect on the homogeneous-equivalent elemental composition measured in XPS. We show that pressing GNP powders onto adhesive tapes, into recesses, or into solid pellets results in inconsistencies in the XPS quantification. The measured oxygen-to-carbon atomic ratio from GNP pellets depends upon the die pressure used to form them and the morphology of the GNPs themselves. We recommend that powder samples of GR2Ms are pelletised prior to XPS analysis to improve repeatability and reproducibility of measurements.
The principles of (Hard) X-ray photoelectron spectroscopy and some application in the field of (core-shell) nanoparticles will be presented. The presentation should answer hoe to get reliable results. Furthermore, examples of the correlation between physical-chemical measurments and toxicological results are given which are crucial for the risk assessment of nanoparticles.
International standards describing reliable protocols will facilitate the commercialization of graphene and related 2D materials. One physico-chemical key property next to flake size and thickness is the chemical composition of the material. Therefore, an ISO standard is under development with X-ray photoelectron spectroscopy having a prominent role. With its information depth of around 10 nm which is the similar length scale as the thickness as of particles of 2D materials consisting of a few monolayer XPS seems to be highly suitable for this purpose. Different sample preparation methods like pressing the powders onto adhesive tapes, into recesses, or into solid pellets result in inconsistencies in the quantification. For the validation of the quantification with XPS an interlaboratory comparison was initiated under the auspice of the “Versailles Project on Advanced Materials and Standards” (VAMAS). First results confirm that the sample preparation method (pellet vs. powder) influences the quantification results clearly.
The passivation behavior of alloy 31 was investigated as a function of passivation potential in a green-death solution at 40 °C. The alloy 31 surface is in a stable passive state during cyclic potentiodynamic polarization. In potentiostatic polarization of alloy 31, passive current density increases with an increase in the passivation potential. Electrochemical impedance spectroscopy (EIS) and Mott–Schottky (M–S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The increase of the applied potential is considered to be a reason for the change in passive film stability.
Lead(II) is a toxic pollutant often found in metalcontaminated soils and wastewaters. In acidic aqueous environments, Pb(II) is highly mobile. Chemical treatment strategies of such systems therefore often include neutralization agents and metal sorbents. Since metal solubility and the retention potential of sorbents depend on the redox state of the aqueous system, we tested the efficiency of the naturally occurring redox-sensitive ferrous iron carbonate mineral siderite to remove Pb(II) from acidic aqueous solutions in batch experiments under oxic and anoxic conditions over a total of 1008 h. Siderite dissolution led to an increase in reactive solution pH from 3 to 5.3 and 6.9, while 90 and 100% of the initial aqueous Pb(II) (0.48 × 10−3 mol kg−1) were removed from the oxic and anoxic systems, respectively.
Scanning and transmission electron microscopy, combined with X-ray absorption and photoelectron spectroscopy, indicated that under oxic conditions, Pb(II) was consumed by cerussite precipitation and inner-sphere surface complexation to secondary goethite.
Under anoxic conditions, Pb(II) was removed by the rapid precipitation of cerussite. This efficient siderite dissolution-coupled sequestration of Pb(II) into more stable solid phases demonstrates this potential method for contaminated water Treatment regardless of the redox environment.
The recent development of x-ray photoelectron spectroscopy using excitation sources different from the usual lab-source Mg Kα and Al Kα and spectrometers with more sophisticated lens systems requires flexible approaches for determining the transmission function. Therefore, the approach using quantified peak areas (QPA) was refined.1 A new algorithm allows a more precise estimation of the transmission function which could be shown by comparing the results obtained with the new version with former calculations. Furthermore, next to the established reference materials Cu, Ag and Au, ionic liquids can be used for estimating the transmission function at beamlines with variable excitation energies. Comparison between the measured and stoichiometric composition shows that a transmission function was determined which allows a reasonable quantification.