XPS of GR2M
(2022)
(1) First results show the suitability of IL as reference for quantification of XPS (at least for organic materials).
(2) Different quantification methods lead to similar results (with a slight advantage for “background method”).
(3)Promising reference material for a better understanding and traceable protocols for the quantification of organic materials with XPS.
The composition of thin films of polymer blends in vertical direction is still under discussion. For explaining the thickness dependence of some properties like the thermal glass transition temperature, a three-layer model has been introduced consisting of an adsorbed layer with a reduced segmental mobility at the substrate, a bulk-like layer in the middle of the film and an outermost surface layer with a higher molecular mobility. X-ray photoelectron spectroscopy (ER-XPS) measurements with a varying excitation energy from 400 eV to 1486.6 eV and, herewith, an information depth from 1.5 nm to 10 nm were performed at PVME/PS films with compositions of 25/75 wt% and 50/50 wt% and thicknesses between 15 nm and 190 nm. As expected, it was found that the PVME concentration decreases with increasing information depth. Secondly, a complex correlation between the PVME concentration at the surface and the film thickness was found. The PVME concentration increases with decreasing film thickness until a maximum at 30 nm. For thinner films, the PVME concentration decreases. These data agree with previous investigations obtained with specific heat spectroscopy.
We thank BESSY II (HZB) for the allocation of beamtime at the HE-SGM beamline and for technical support. DFG (Project number 124846229) is acknowledged for financial support.
Molecular sieves as materials with defined pores offer new opportunities in the preparation of nanostructured materials for different applications in chemistry, medicine and biology. Typical examples for such materials are zeolites, porous glass, different silicas and active carbon. Introducing transition metal ions in such materials can widen the possibilities of these materials in terms of chemical activity. Especially, the opportunity to tailor the redox properties of the transition metal ions by varying the location of the ion in the sieves is a promising way to obtain catalysts with the desired properties.
For this purpose, Cu2+ ions were introduced into a SAPO-5 (silicoaluminaphosphate) by a hydrothermal method and by impregnation. As expected, the different preparation methods led to different locations of the Cu2+ ions: by the hydrothermal method the ions were incorporated in the SAPO-5 framework, by impregnation mononuclear Cu species randomly distributed in the pores of the support or CuO particles were formed depending on the Cu amount. These locations could be determined by Extended X-ray Absorption Fine Structure and Anomalous Small-Angle X-ray Scattering investigations. For investigating the redox properties of the Cu2+ ions the differently prepared sample were treated in Ar and H2 atmosphere until 550°C. X-ray Photoelectron Spectroscopy was performed to study the valence states of Cu after each of such treatment. For a definite determination of the valence states, both Cu 2p and Cu LMM spectra must be recorded. Cu2+ exhibits a clear chemical shift and a typical satellite structure in Cu2p spectra, but between mono- and zerovalent Cu a differentiation is not possible. On the other hand, these two species show a clear shift in the Auger spectra. Whereas in H2 atmosphere in any case metallic Cu was formed, the treatment in Ar showed significant differences between the samples. Cu2+ incorporated in the framework could not be reduced by this treatment. In contrast, the mononuclear Cu2+ species were reduced to stable Cu+. Likewise, the CuO nanoparticles were reduced to the monovalent Cu, but this species can be much more easily reoxidized in air. The consequences for the catalytic properties will be discussed.
International standards describing reliable protocols will facilitate the commercialization of graphene and related 2D materials. One physico-chemical key property next to flake size and thickness is the chemical composition of the material. Therefore, an ISO standard is under development with X-ray photoelectron spectroscopy having a prominent role. With its information depth of around 10 nm which is the similar length scale as the thickness as of particles of 2D materials consisting of a few monolayer XPS seems to be highly suitable for this purpose. Different sample preparation methods like pressing the powders onto adhesive tapes, into recesses, or into solid pellets result in inconsistencies in the quantification. For the validation of the quantification with XPS an interlaboratory comparison was initiated under the auspice of the “Versailles Project on Advanced Materials and Standards” (VAMAS). First results confirm that the sample preparation method (pellet vs. powder) influences the quantification results clearly. Considering this effect, a good agreement of the results from the different participants were observed. Similar results were observed for raw, N- and F-functionalized graphene.
International standards describing reliable protocols will facilitate the commercialization of graphene and related 2D materials. One physico-chemical key property next to flake size and thickness is the chemical composition of the material. Therefore, an ISO standard is under development with X-ray photoelectron spectroscopy having a prominent role. With its information depth of around 10 nm which is the similar length scale as the thickness as of particles of 2D materials consisting of a few monolayer XPS seems to be highly suitable for this purpose. Different sample preparation methods like pressing the powders onto adhesive tapes, into recesses, or into solid pellets result in inconsistencies in the quantification. For the validation of the quantification with XPS an interlaboratory comparison was initiated under the auspice of the “Versailles Project on Advanced Materials and Standards” (VAMAS). First results confirm that the sample preparation method (pellet vs. powder) influences the quantification results clearly.