Filtern
Dokumenttyp
- Zeitschriftenartikel (22)
- Vortrag (4)
- Posterpräsentation (3)
- Forschungsbericht (3)
- Beitrag zu einem Tagungsband (2)
Schlagworte
- Nanoparticles (17)
- EDX (6)
- SEM (6)
- T-SEM (5)
- TiO2 (5)
- High-resolution (4)
- XPS (4)
- Auger electron spectroscopy (3)
- NanoValid (3)
- SEM/EDX (3)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
Potential candidates of reference nano-materials are manufactured and systematically characterized in particular with respect to their morphology (shape, size and size distribution) in the frame of the running large European project NanoValid. By exploiting the transmission operation mode in a SEM, known as T-SEM, it is demonstrated by means of three representative examples of nanoparticles how a quick morphological inspection up to a complete, metrological characterization is feasible.
The need for a better understanding of nanoparticleprotein interactions and the mechanisms governing the resulting colloidal stability has been emphasised in recent years. In the present contribution, the short and long term colloidal stability of silica nanoparticles (SNPs) and silica–poly(ethylene glycol) nanohybrids (Sil–PEG) have been scrutinised in a protein model system. Well-defined silica nanoparticles are rapidly covered by bovine serum albumin (BSA) and form small clusters after 20 min while large agglomerates are detected after 10 h depending on both particle size and nanoparticle–protein ratio. Oppositely, Sil–PEG hybrids present suppressive protein adsorption and enhanced short and long term colloidal stability in protein solution. No critical agglomeration was found for either system in the absence of protein, proving that instability found for SNPs must arise as a consequence of protein adsorption and not to high ionic environment. Analysis of the small angle X-ray scattering (SAXS) structure factor indicates a short-range attractive potential between particles in the silica-BSA system, which is in good agreement with a protein bridging agglomeration mechanism. The results presented here point out the importance of the nanoparticle surface properties on the ability to adsorb proteins and how the induced or depressed adsorption may potentially drive the resulting colloidal stability.
Need for large-area EDS detectors for imaging nanoparticles in a SEM operating in transmission mode
(2014)
In the frame of the European project NanoValid, potential candidates of reference nanomaterials are manufactured and systematically characterized in particular with respect to their morphology (shape, size and size distribution). In this study, by exploiting the transmission operation mode in a high-resolution SEM, known as transmission SEM, the potential of this methodical approach is demonstrated by means of representative examples of nanoparticles. The method enables quick and accurate morphological inspection and systematic characterization. Energy dispersive X-ray spectroscopy imaging of single nanoparticles by using the transmission mode is demonstrated as feasible, too.
High-priority industrial nanomaterials like SiO2, TiO2, and Ag are being characterized on a systematic basis within the framework of the EU FP7 research project NanoValid. Silica nanoparticles from an industrial source have been analyzed by Auger electron spectroscopy. Point, line, and map spectra were collected. Material specific and methodological aspects causing the special course of Auger line scan signals will be discussed.
The combination of complementary characterization techniques such as SEM (Scanning Electron Microscopy), T-SEM (Scanning Electron Microscopy in Transmission Mode), EDX (Energy Dispersive X-ray Spectroscopy) and SAM (Scanning Auger Microscopy) has been proven to be a powerful and relatively quick characterization strategy for comprehensive morphological and chemical characterization of individual silica and titania nanoparticles. The selected real life test materials, silica and titania, are listed in the OECD guidance manual as representative examples because they are often used as commercial nanomaterials. Imaging by high resolution SEM and in the transmission mode by T-SEM allows almost simultaneous surface and in-depth inspection of the same particle using the same instrument. EDX and SAM enable the chemical characterization of bulk and surface of individual nanoparticles. The core–shell properties of silica based materials are addressed as well. Titania nominally coated by silane purchased from an industrial source has been found to be inhomogeneous in terms of chemical composition.
A novel Infinitesimal Columns (IC) simulation model is introduced in this study for the quantitativeanalysis of core-shell nanoparticles (CSNP) by means of XPS, which combines the advantages of exist-ing approaches. The IC model is applied to stabilised Lumidot™CdSe/ZnS 610 CSNP for an extensiveinvestigation of their internal structure, i.e. calculation of the two shell thicknesses (ZnS and stabiliser)and exploration of deviations from the idealised CSNP composition. The observed discrepancies betweendifferent model calculations can be attributed to the presence of excess stabiliser as well as synthesisresidues, demonstrating the necessity of sophisticated purification methods. An excellent agreement isfound in the comparison of the IC model with established models from the existing literature, the Shardmodel and the software SESSA.
The physico-chemical characteristics of TiO2 coatings can greatly influence their final performance. In SETNanoMetro, different deposition procedures are being set for applying films of TiO2 NPs with defined and homogenous thickness on supports of interest for the applications studied in the project. The selected substrates are the following: (i) Silica glasses for photocatalytic measurements, (ii) Ti-alloys for orthopedic and/or dental prostheses, and for cell cultures, and (iii) Conductive glasses (e.g. Fluorine doped Tin Oxide, FTO) for dye-sensitized solar cells. From the different film deposition procedures studied within the project Self-assembly of TiO2 NPs in multiple layers was selected. For this, surface modification of the substrate and of TiO2 nanoparticles (NPs) with e.g. silane coupling agents is a prerequisite. First attempts to prepare the self-assembled coating on the functionalized glass substrates seem to indicate that the functionalized NPs adhere to the substrates, even if the final coatings were not homogenous and presented agglomerates. ToF-SIMS results support this outcome.
In order to use the layer-by-layer deposition technique for the formation of TiO2 films by controlled self-assembly of the TiO2 NPs, the proper complementary moieties for the functionalization of the NPs were chosen. A first set of NPs has been produced by reaction with (3-aminopropyl)phosphonic acid (APPA) in order to functionalize the surface with free amino-groups. Then, the complementary NP set can be obtained from an aliquot of the first one, through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde. A proper approach for the functionalization of two types of TiO2, commercial P25 (Evonik) and SETNanoMetro-sample labelled UT001, with APPA was developed. A second set of NPs consisting of three types of TiO2 NPs, P25 and SETNanoMetro NPs (TiO2 NPs with high specific surface area > 150 m2/g and TiO2 NPs with low size < 20 nm) was functionalized with (3-aminopropyl)triethoxysilane (APTS). As for the previous set of NPs, the complementary NP set was obtained through the conversion of free surface amino-groups to aldehydes by reaction with glutaraldehyde. EDX, AES and ToF-SIMS spectra were collected and analyzed to demonstrate the presence of the surface functionalization of the different types of TiO2 NPs.
The interest in nanoparticles remains at a high level in fundamental research since many years and increasingly, nanoparticles are incorporated into consumer products to enhance their performance. Consequently, the accurate and rapid characterization of nanoparticles is more and more demanded. Electron microscopy (SEM, TSEM and TEM) is one of the few techniques which are able to image individual nanoparticles. It was demonstrated recently that the transmission electron microscopy at a SEM can successfully be applied as a standard method to characterize accurately the size (distribution) and shape of nanoparticles down to less than 10 nm.
The certified reference material BAM-L200, a nanoscale stripe pattern for length calibration and specification of lateral resolution, is described. BAM-L200 is prepared from a cross-sectioned epitaxially grown layer stack of AlxGa1–xAs and InxGa1–xAs on a GaAs substrate. The surface of BAM-L200 provides a flat pattern with stripe widths ranging down to 1 nm. Calibration distances, grating periods and stripe widths have been certified by TEM with traceability to the length unit. The combination of gratings, isolated narrow stripes and sharp edges of wide stripes offers plenty of options for the determination of lateral resolution, sharpness and calibration of length scale at selected settings of imaging surface-analytical instruments. The feasibility of the reference material for an analysis of the lateral resolution is demonstrated in detail by evaluation of ToF-SIMS, AES and EDX images. Other applications developed in the community are summarized, too. BAM-L200 fully supports the implementation of the revised International Standard ISO 18516 (in preparation) which is based on knowledge outlined in the Technical Report ISO/TR 19319:2013.
In this work, sample losses of silver nanoparticles (Ag NPs) in asymmetrical flow field-flow fractionation (AF4) have been systematically investigated with the main focus on instrumental conditions like focusing and cross-flow parameters as well as sample concentration and buffer composition. Special attention was drawn to the AF4 membrane. For monitoring possible silver depositions on the membrane, imaging laser ablation coupled to inductively coupled plasma mass spectrometry (LA-ICP-MS) was used. Our results show that the sample residue on the membrane was below 0.6% of the total injected amount and therefore could be almost completely avoided at low sample concentrations and optimized conditions. By investigation of the AF4 flows using inductively coupled plasma mass spectrometry (ICP-MS), we found the recovery rate in the detector flow under optimized conditions to be nearly 90%, while the cross-flow, slot-outlet flow and purge flow showed negligible amounts of under 0.5%. The analysis of an aqueous ionic Ag standard solution resulted in recovery rates of over 6% and the ionic Ag content in the sample was found to be nearly 8%. Therefore, we were able to indicate the ionic Ag content as the most important source of sample loss in this study.
Advances in scanning electron microscopy (SEM) enable the high-resolution imaging of single nanoparticles (NPs) with sizes well below 10 nm. The SEM analysis in transmission mode (T-SEM) of NPs on thin film supports has many benefits when compared to the analysis of NPs on bulk substrates. The enhanced material (mass - thickness) contrast of the T-SEM imaging mode is well suited for in-depth and, particularly valuable, to very accurate, traceable, lateral dimensional measurements of NPs. Compared to samples prepared on bulk substrates, T-SEM with energy dispersive X-ray spectroscopy (EDS) achieves a drastically improved spatial resolution of the emitted X-rays. The poor signal-to-noise ratio of the X-ray spectra emitted by a single nanoparticle (NP) can be improved by the use of high-sensitivity (high collection solid angle) silicon drift (SDD), energy-dispersive X-ray spectrometers (EDS). The EDS spectral imaging of a single NP with a spatial resolution below 10 nm has become possible. This is demonstrated by means of various examples of nanostructures. Advanced data processing of T-SEM/EDS results sets the stage for the automated classification of NPs by feature analysis. This method combines the detection of morphological structures of interest by image processing of T-SEM micrographs with the chemical classification by EDS.
The characteristics of TiO2 coatings can greatly influence their final performance in large‐scale applications. In the present study, self‐assembly of TiO2 nanoparticles (NPs) in multiple layers was selected as a deposition procedure on various substrates. For this, the main prerequisite constitutes the surface modification of both NPs and substrate with, for example, silane coupling agents. A set of functionalized TiO2 NPs has been produced by reaction with either (3‐aminopropyl)triethoxysilane (APTES) or (3‐aminopropyl)phosphonic acid (APPA) to functionalize the NP surface with free amino‐groups. Then, the complementary functionalized NP set can be obtained from an aliquot of the first one, through the conversion of free surface amino groups to aldehydes by reaction with glutaraldehyde (GA). Several types of TiO2 NPs differing in size, shape, and specific surface area have been functionalized. Fourier‐transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), SEM/ energy‐dispersive X‐ray spectroscopy (EDS), XPS, Auger electron spectroscopy (AES), and Time‐of‐Flight (ToF)‐SIMS analyses have been carried out to evaluate the degree of functionalization, all the analytical methods employed demonstrating successful functionalization of TiO2 NP surface with APTES or APPA and GA.
Advances in scanning electron microscopy (SEM) enable the high-resolution imaging of single nanoparticles (NPs) with sizes well below 10 nm. The SEM analysis in transmission mode (T-SEM) of NPs on thin film supports has many benefits when compared to the analysis of NPs on bulk substrates. The enhanced material (mass – thickness) contrast of the T-SEM imaging mode is well suited for in-depth and, particularly valuable, to very accurate, traceable, lateral dimensional measurements of NPs. Compared to samples prepared on bulk substrates, T-SEM with energy dispersive X-ray spectroscopy (EDS) achieves a drastically improved spatial resolution of the emitted X-rays. The poor signal-to-noise ratio of the X-ray spectra emitted by a single nanoparticle (NP) can be improved by the use of high-sensitivity (high collection solid angle) silicon drift (SDD), energy-dispersive X-ray spectrometers (EDS). The EDS spectral imaging of a single NP with a spatial resolution below 10 nm has become possible. This is demonstrated by means of various examples of nanostructures. Advanced data processing of T-SEM/EDS results sets the stage for the automated classification of NPs by feature analysis. This method combines the detection of morphological structures of interest by image processing of T-SEM micrographs with the chemical classification by EDS.
A nanoscale boride, α-FeB, with grains of variable size and crystallinity was synthesized by precipitation from solution followed by heat treatment (450 °C, 550 °C, 750 °C, 1050 °C). Analysis of transmission electron micrographs, electron diffraction, and magnetic measurements suggests superparamagnetism at room temperature for the smaller, more disordered particles of FeB, while the larger, more crystalline particles of α-FeB, with a particle size of approximately 20 nm, display open magnetic hysteresis loops and blocking. In contrast to the soft ferromagnetism of bulk β-FeB, which was synthesized by conventional solid state reaction at 1500 °C, the sample of α-FeB annealed at 1050 °C is a harder ferromagnet, possibly due to stacking faults that pin the magnetic domains; these stacking faults are apparent in the high resolution transmission electron micrographs. The changes in magnetic behavior are visible from the varying blocking temperatures (63 K, 94 K, 150 K, and >320 K from the smallest to the largest particles) and correlate with the transformations from amorphous to α-FeB and from α-FeB to β-FeB.