Multilayer ceramic devices based on low-temperature co-fired ceramics (LTCC) materials provide a very promising technology. Most LTCC tapes available today contain considerable fractions of glass powders to lower the sintering temperature. However, the glassy phases offer more possibilities to set a proper sintering behavior, on the one hand, and to tailor the desired properties of the final LTCC substrate, on the other. The exploitation of demixing and subsequent crystallizing glass compositions was shown on an example of a low-permittivity (4.4)low-loss (1.5 × 103) LTCC with a high quartz content. In another LTCC material, undesired demixing could be restricted and the crystal phase anorthite could be triggered by partial dissolution of alumina in the liquid phase during sintering. To estimate the effect of silver diffusion in the latter material, the surroundings of a pure silver via were studied. A silver-contaminated range of 50 µm was detected. Using model glasses containing silver oxide, a strong influence of dissolved silver on viscosity and crystallization behavior of the liquid phase was demonstrated. The dielectric properties of the sintered substrates were not degraded.
New applications of low-temperature co-fired ceramics (LTCC), such as pressure sensors or integrated functional layers, require materials that possess higher coefficients of thermal expansion (CTE). To fabricate LTCC with elevated CTE, two methods of material design are examined: firstly, glass ceramic composites (GCC), which consist of >50 vol% glass in the starting powder, and, secondly, glass-bonded ceramics (GBC), where glass is added as a sintering aid only. The CTE of GBC is mainly determined by the crystalline component. For GCC, the CTE can be well predicted, if CTE and elastic data of each phase in the microstructure are known. A nonlinear characteristic of the CTE versus phase composition was found with increasing Ecrystals/Eglass ratio and absolute CTE difference between the components. The glass composition and glass amount can be used to compensate the fixed properties of a crystalline material in a desired way. However, because the CTE and permittivity of a glass cannot be chosen independently, an optimum glass composition has to be found. For a given LTCC, it is possible to control the devitrification by shifting the glass composition. In this way, the resulting CTE values can be predicted more exactly and tailoring becomes possible. Different LTCC materials, based on the crystalline compounds Ba(La,Nd)2Ti4O12, ZrO2 (Y-TZP), SiO2 (quartz), and specially developed glasses, possessing an elevated CTE of around 10 × 10-6 K-1 while showing permittivity εr between 6 and 63, are introduced.