The long-term sealing behavior of metal seals, assembled in the lid system of casks for transportation and storage of radioactive materials, has been investigated. For that purpose, phenomenological models describing the time- and temperature dependent behavior have been introduced by BAM since 2016, e.g. by using the time-temperature superposition principle. Results have shown that these models describe the relaxation behavior adequately and are suitable for extrapolations. In this work, the applicability of these models is checked by analyzing the necessary scope of tests, which must be carried out to get sufficient information about the long-term behavior of metal seals based on short-term tests.
The safety evaluation of cask components made of ductile cast iron includes investigations to prevent brittle fracture. Generally, ductile cast iron is endangered by brittle fracture especially at low temperatures (down to -40°C) and in combination with existing crack-like material defects. An applicable method is the assessment of fracture resistance using fracture mechanics according to the IAEA guidelines. The approach is based on the prevention of fracture initiation. For application of these principles for drop loads, account must be taken both of dynamic stresses within the component and dynamic material behavior. Basically, the dynamic stress intensity factor of postulated pre-existing crack-like defects is compared with the dynamic fracture toughness of the material. Applicable numerical and experimental methods for the safety assessment of cask components are demonstrated for the case of an artificially pre-cracked cylindrical cast iron cask which undergoes dynamic loading conditions as result of the hard impact between the cask and a concrete target. The proposed evaluation procedure is a combination of numerical and experimental steps. Exemplarily, the calculated stress intensity factor is compared with measured fracture toughness values from single edge notched bending specimens.