Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (42)
- Zeitschriftenartikel (19)
- Beitrag zu einem Sammelband (18)
- Beitrag zu einem Tagungsband (10)
- Sonstiges (1)
- Posterpräsentation (1)
- Forschungsbericht (1)
Sprache
- Englisch (62)
- Deutsch (29)
- Portugiesisch (1)
Schlagworte
- Creep (7)
- Rafting (7)
- Ermüdung (5)
- Schädigungsmechanik (5)
- Ti-MMC (5)
- Nickel-base superalloys (4)
- Single crystal (4)
- Superalloys (4)
- Additive manufacturing (3)
- Damage analysis (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (15)
- 5.0 Abteilungsleitung und andere (11)
- 9 Komponentensicherheit (7)
- 8 Zerstörungsfreie Prüfung (4)
- 5.3 Polymere Verbundwerkstoffe (3)
- 9.5 Tribologie und Verschleißschutz (3)
- 5.2 Metallische Hochtemperaturwerkstoffe (2)
- 8.5 Röntgenbildgebung (2)
- 9.4 Integrität von Schweißverbindungen (2)
- 9.6 Additive Fertigung metallischer Komponenten (2)
Eingeladener Vortrag
- nein (42)
The influence of small rhenium additions on the lattice spacing of a nickel solid solution was investigated using a nickelrhenium single crystal with an axial macrosegregation of rhenium. The effect of rhenium on the lattice spacing of the nickel solid solution was found to be similar to that of tungsten.
Nickel-Basis-Superlegierungen: Gefüge, mechanisches Verhalten bei Hoch-temperatur, Modellierung
(2002)
Standard reference materials
(2002)
A titanium (Ti-6242) matrix composite reinforced with continuous SiC fibers was studied. The mechanical behavior of the matrix and the composite was characterized by tensile, creep and isothermal fatigue tests at room temperature and up to 550°C. The thermo-mechanical fatigue behavior under in-phase and out-of-phase conditions was investigated for the composite between 100 and 550°C. Fracture surfaces were characterized by confocal light microscopy and by scanning electron microscopy to identify the damage mechanisms.
Constitutive modelling of creep degradation due to rafting in single-crystalline Ni-base superalloys
(2009)
A constitutive model for the mechanical behaviour of single-crystalline superalloys at high temperatures has been developed. The model relies on the slip system theory and is able to predict rafting and its influence on plastic flow. The kinetics of rafting are assumed to be driven by the reduction of the internal stresses represented by the macroscopic back-stress. The rafting effect is incorporated in the model through the dependence of the Orowan stress on the channel width. The model has been validated for the alloy CMSX-4 at 950 °C. The rafting part of the model has been calibrated by measurements of the channel widths after several levels of creep strains and for several loads.
A new experimental technique (repeated load annealing of flat wedge shaped specimens) was proposed for characterization of microstructural degradation under creep conditions. This technique was applied to investigate the microstructural degradation of the nickel-base superalloy CMSX-4 in a wide range of temperatures and stress levels. The results obtained allowed to describe analytically the kinetics of rafting, which is important to predict the reduction of fatigue lifetime and yield stress.
Microstructural aspects of composites such as reinforcement particle size, shape, and distribution play important roles in deformation behavior. In addition, Fe-rich inclusions and porosity also influence the behavior of these composites, particularly under fatigue loading. Three-dimensional (3-D) visualization of porosity and Fe-rich inclusions in three dimensions is critical to a thorough understanding of fatigue resistance of metal matrix composites (MMCs), because cracks often initiate at these defects. In this article, we have used X-ray synchrotron tomography to visualize and quantify the morphology and size distribution of pores and Fe-rich inclusions in a SiC particle-reinforced 2080 Al alloy composite. The 3-D data sets were also used to predict and understand the influence of defects on the deformation behavior by 3-D finite element modeling.
Der Beitrag der BAM zur Sicherheitstechnik am Beispiel der Schadensanalyse von Eisenbahnkomponenten
(2010)
Changes in the structure of single-crystal (SC) superalloy SRR99 during creep at 980 °C and 200 MPa were investigated. Geometrical parameters of the y/y'-microstructure, y/y'-misfit, stresses in the phases and local misorientation of the structure were determined at defined points of the dendritic structure by use of X-ray diffraction (XRD), wavelength dispersive X-ray spectroscopy (WDXS), scanning (SEM) and transmission (TEM) electron microscopy. Correlation of the microstructural period and local misorientation of the structure with creep strain were found.
Low-cycle fatigue experiments under combined axial-torsional loading have been carried out on alloy 800 H tubular specimens at room temperature. In comparison with proportional loading, an extra cyclic hardening effect produced by nonproportional loading was observed. The microstructure study highlights the fact that the dislocation arrangement under proportional loading is significantly different from that under nonproportional loading. Mechanical twinning was found in specimens cycled under axial loading and nonproportional loading. It is suggested that mechanical twinning depends not only on shear stress but also on normal stress on the plane of maximum shearing. The extra hardening can be interpreted in terms of the deformation microstructure. Fatigue cracking was initiated generally at the specimen surfaces along the plane of maximum shearing, but under nonproportional loading cracks were found also in the bulk of the specimens. Transcrystalline crack propagation was observed in the specimens after proportional and nonproportional LCF tests.
O monitoramento das estruturas de concreto possibilita que o risco de corrosão seja estimado ao longo dos anos de sua utilização. Com o conhecimento desse risco, intervenções de prevenção da corrosão ou de controle da corrosão já estabelecida podem ser programadas e realizadas em períodos adequados. Na prática, o risco de corrosão é avaliado por meio da verificação periódica do estado da armadura e das alterações nas propriedades do concreto. Isso pode ser feito por meio do embutimento no concreto de cobrimento de sensores de aquisição contínua de dados. Há diferentes tipos de sensores de aquisição contínua de dados. Um dos mais conhecidos é o sensor galvânico que consta de um conjunto de barras de aço-carbono, eletricamente isoladas. Com o embutimento do sensor, essas barras ficam posicionadas em diferentes e conhecidas profundidades do concreto de cobrimento da armadura. O risco de corrosão da armadura é monitorado com a periódica medição da corrente galvânica em cada uma das barras do sensor. Essa medição, dentre outras informações do sensor galvânico foram abordadas em artigo anterior. Além do sensor galvânico, destacam-se o sensor de umidade e o de taxa de corrosão, que monitoram parâmetros importantes relacionados ao estabelecimento e evolução de processo corrosivo das armaduras. A seguir esses sensores são apresentados, bem como o sensor de fibra óptica, o qual apresenta algumas vantagens em relação aos demais mencionados, embora ainda seja de uso restrito.
In the present study, samples fabricated by varying the deposition hatch length during selective laser melting of nickel based superalloy Inconel 718 were investigated. Microstructure and texture of these samples was characterized using scanning electron microscopy, combined with electron back-scattered diffraction, and residual stress assessment, using neutron diffraction method. Textured columnar grains oriented along the sample building direction were observed in the shorter hatch length processed sample. A ten-fold increase in the hatch length reduced the texture intensity by a factor of two attributed to the formation of finer grains in the longer hatch length sample. Larger gradients of transverse residual stress in the longer hatch length sample were also observed. Along the build direction, compressive stresses in the shorter hatch length and negligible stresses for the longer hatch length specimen were observed. Changes to the temperature gradient (G) in response to the hatch length variation, influenced the G to growth rate (R) ratio and the product G × R, in agreement with the microstructures and textures formed. For the residual stress development, geometry of the part also played an important role. In summary, tailored isotropy could be induced in Inconel 718 by a careful selection of parameters during selective laser melting.
Die Grundlagen der Metallographie wurden in der zweiten Hälfte des 19. Jahrhunderts von Henry Clifton Sorby in England und Adolf Martens in Deutschland gelegt. Den verfügbaren Quellen nach erfolgten diese Arbeiten unabhängig voneinander. In diesem Beitrag werden die Beiträge von Adolf Martens und Emil Heyn zur Etablierung der Metallographie als ein eigenständiges Fach im Rahmen der Metallkunde dargestellt. Dabei werden Aspekte der Werkstoffprüfung, der Fraktographie und der Schadensanalyse einbezogen. Abschließend wird die führende Rolle dieser Pioniere der Metallkunde bei der Gründung der Deutschen Gesellschaft für Materialkunde (DGM) sowie des Deutschen Verbands für Materialforschung und -prüfung (DVM) gewürdigt.
Role of materials data
(2017)
In a general sense, data are the output of experimental research work. In this workshop we will present some basic ideas concerning the reliability of experimental data; this is a central issue both for individuals or labs producing results as well as for scientists working on theoretical models and engineers designing a machine. Digitalization accelerates enormously the data exchange between these communities; however, the required level of confidence on experimental results increases in the same way. We invite all the participants to reflect upon the value of materials data for their own work.
The advent of the Industrial Revolution was accompanied by several accidents of dramatic dimensions. The analysis of these events was the fundament for the continuous improvement in the reliability of technical systems. In the year 1871 the Prussian state created a technical institution dedicated for this task – the origin of BAM. Failure analysis and prevention is until today a central objective of our institute; due to its complex nature an interdisciplinary task. In our talk we will present an overview of the activities of BAM in the area of failure analysis and prevention; especial attention will be given to the VDI Guide 3822.
The aim of this research is to study the influence of moisture absorption at low moisture contents on the creep behaviour of an epoxy adhesive in steel bonded joints. Single lap joints were manufactured using high strength steel adherends and a two-component epoxy adhesive. The single lap joints were tested at load Levels corresponding to average lap shear stresses of±5%, 15%, 30% and 45% of the dry lap shear strength in both 40 °C air and 40 °C distilled water. Specimens were not pre-aged to be able to analyse the coupled effect of moisture and loading. The test results show that an increase in the load level resulted in an increase in the instantaneous strain and in the creep strain rate. The creep strain of single lap joints loaded in water was generally larger than for the ones loaded in air. For joints loaded in water the creep behaviour was found to be dependent on the moisture concentration in the adhesive. At low moisture percentages creep was suppressed, resulting in a lower instantaneous strain. At higher moisture percentages creep was promoted, resulting in a larger strain rate. The suppression of creep at low moisture percentages is attributed to water molecules bonding to the epoxy macromolecules, resulting in a reduction in molecular mobility and a smaller creep strain. At higher moisture percentages the plasticizing effect of the water dominates, resulting in a larger creep strain. The Maxwell threeelement solid model and Kelvin-Voigt three-element solid model were used to simulate the creep behaviour of the single lap joints loaded in air and water. The models gave good representations of the creep Response across the different load levels in both water and air, they were however unable to give a correct representation of the instantaneous strain of the single lap joints loaded in water. This is attributed to the models being unable to account for the present short-term relaxation process that is dependent on the moisture concentration.
Die BAM ist nahezu über die gesamte Wertschöpfungskette hinweg wissenschaftlich tätig. Von der sicheren und effizienten Wasserstofferzeugung (POWER-to-GAS), über die (Zwischen-)Speicherung von Wasserstoff in Druckgasspeichern bis hin zum Transport bspw. mittels Trailerfahrzeug zum Endverbraucher.
Komplettiert werden die Aktivitäten der BAM durch die sicherheitstechnische Beurteilung von wasserstoffhaltigen Gasgemischen, die Verträglichkeitsbewertung von Werkstoffen bis hin zur Detektion von Wasserstoffkonzentrationen über geeignete Sensorik, auch mittels ferngesteuerter Messdrohnen (sog. UAV-Drohnen).
Zudem untersucht die BAM proaktiv Schadensrisiken und Unfallszenarien für die Sicherheitsbetrachtung, um mögliche Schwachstellen aufzeigen und potenzielle Gefährdungen erkennen zu können.
Influence of support configurations on the characteristics of selective laser-melted Inconel 718
(2018)
Samples fabricated using two different support configurations by following identical scan strategies during selective laser melting of superalloy Inconel 718 were characterized in this study. Characterization methods included optical microscopy, electron back-scattered diffraction and x-ray diffraction residual stress measurement. For the scan strategy considered, microstructure and residual stress development in the samples were influenced by the support structures. However, crystallographic texture intensity and the texture components formed within the core part of the samples were almost independent of the support. The formation of finer grains closer to the support as well as within the columnar grain boundaries resulted in randomization and texture intensity reduction by nearly half for the sample built on a lattice support. Heat transfer rates dictated by the support configurations in addition to the scan strategy influenced the microstructure and residual stress development in selective laser-melted Inconel 718 samples.
Adolf Martens (18501914) was a pioneer of materials engineering. After his studies in Berlin he joined a railway company being responsible for the technical equipment. His interest for the basic mechanisms of mechanical strength and fracture of metallic materials led him to the development of the basic concepts for metallography; his papers published between 1878 and 1889 laid the fundament of this technique. In 1880 Martens changed to the Royal Industrial Academy in Berlin and by 1884 he was designated as director of the Materials Testing Laboratory at the Technical University Berlin. Under his guidance this institution acquired an excellent reputation in all relevant areas of the German industry, forming the nucleus of the Bundesanstalt für Materialforschung und -prüfung (BAM) – the Federal Institute for Materials Research and Testing. Martens developed equipment in many different areas as mechanical testing of metallic materials and of paper, characterization of the wear behavior of materials and viscosity of lubricants. His overwhelming contribution to materials engineering was recognized as early as 1895 by Floris Osmond, who denominated martensite a metallographical constituent resulting from quenching of steels. In 2000 ISO designated the value obtained from the instrumented indentation method as Martens Hardness – HM.
The advent of the Industrial Revolution was accompanied by several accidents of dramatic dimensions. The analysis of these events was the fundament for the continuous improvement in the reliability of technical systems. In the year 1871 the Prussian state created a technical institution dedicated for this task – the origin of BAM. Failure analysis and prevention is until today a central objective of our institute; due to its complex nature an interdisciplinary task. In our talk we will present an overview of the activities of BAM in the area of failure analysis; especial attention will be given to the corrosion aspects in the analysis of these cases.
Hot crack assessment during production and processing of metallic materials is an essential prerequisite for the safety of welded structures. The hot cracking investigations presented here were carried out as part of a study aimed at the development of Cr/Ni low transformation temperature filler materials. Low transformation temperature alloys open up the possibility for welding high strength steels. The externally loaded Modified Varestraint Transvarestraint hot cracking test was employed in the experiments described. The hot cracking resistance was evaluated with the help of light microscopy applied at the specimen surface. The proportionality between hot cracking susceptibility and Cr/Ni alloy content was explained by the altered solidification kinetics and by the enlarged solidification interval. The internal crack paths and the three-dimensional structure of the crack net in the material volume were examined using X-ray computer tomography. The total crack lengths for different material depths and circumjacent rectangular volumes, respectively, were be determined. An increasing hot cracking susceptibility with increasing Cr/Ni alloy content was also be established for the specimen volume.
Rafting during high temperature deformation in a single crystal superalloy: experiments and modeling
(2012)
Experimental characterization and mechanical modeling of creep induced rafting in superalloys
(2012)
A constitutive model has been developed for the high temperature mechanical behavior of single crystal superalloys, including rafting and its consequences. The flow stress depends on the γ channel width via the Orowan stress. An evolution equation for channel widening during high temperature straining has been derived and calibrated with measurements. Therein, rafting is assumed to be driven by the relaxation of internal stresses. The model is able to represent the mechanical softening at high stresses consecutive to rafting. The model has been applied to simulate rafting during uniaxial creep in several crystal orientations, in notched specimens as well as in cyclically loaded specimens.
Creep damage of single-crystal nickel base superalloys: mechanisms and effect on low cycle fatigue
(2010)
The main mechanisms of creep damage of single-crystal nickel-base superalloys are the loss of the interface coherency, coarsening of the γ / γ'-microstructure, precipitation of topologically closed packed phases and growth of porosity. This degradation deteriorates the mechanical properties such as yield stress, creep lifetime and especially low-cycle fatigue life, which can be reduced nearly by a factor of 10. The degradation kinetics during creep was characterised quantitatively on the superalloy CMSX-4. A new non-destructive testing technique was applied to cover a wide test parameter range with few specimens in a relatively short time: repeated load annealing of wedge shaped specimens.
The use of high niobium alloyed cast iron alloys is a relatively new approach in which the niobium addition intends to improve the properties of the material by the precipitation of hard niobium carbides during solidification. Steels can be replaced by ductile cast iron in some rolling applications, such as gears and cams, in order to reduce material costs. The aim of this work is to evaluate ductile iron alloyed with 1 weight percent (wt.%) niobium for the as cast specimens and with 1.8 wt.% and 2.4 wt.% niobium for the austempered specimens under lubricated slip-rolling tests using mixed/boundary conditions in an Amsler-type machine. Austempered ductile iron (ADI) alloyed with 1 wt.% chromium, or Carbidic ADI, was tested for comparison. For the as cast conditions, the niobium addition resulted in an increase of wear resistance owing to the low contact pressure of these tests. However, for the austempered specimens, the best performance was found for unalloyed ADI. The main factor acting in the initiation and propagation of cracks in ductile iron is the presence of the graphite nodules. The coarse carbides also contributed to the initiation of cracks and spalling of the material.
Carbidic Austempered Ductile Iron (CADI) microstructures containing eutectic carbides can be produced by the addition of carbide stabilizing elements, such as chromium. Carbides formed from the addition of Cr are eutectic of M3C type. The presence of such hard phases can enhance the abrasion wear resistance of ductile iron. A new CADI can be produced by the addition of Nb. Niobium carbide particles are formed in the beginning of solidification and remain stable once they are insoluble in solid iron matrix. The dry sand abrasive wear resistance of ductile irons alloyed with 1.0, 1.8, and 2.4 wt% Nb were tested in both “as-cast” and “heat treated” conditions using standard ASTM G65. Results were compared to abrasive wear data obtained on ductile iron alloyed with 1 wt% Cr, CADI (1 wt% Cr), and the basic composition of iron without carbide stabilizing elements. In the “ascast” condition, the addition of Nb did not lead to a reduction in wear, while CADI with Nb is a promising substitute for CADI with Cr addition, because both materials showed very similar values of abrasion resistance.
Micro-ploughing and micro-cutting mechanisms were observed on the worn surfaces of ductile irons. Abrasive wear resistance of these alloys was correlated with the volume fraction of carbides.
Fraktographischen Daten aus Schadensanalysen, Vergleichsversuchen und Vorhaben könnten der Fachöffentlichkeit im Bereich Fraktographie zur Verfügung gestellt werden, sofern das Urheberrecht es zulässt und außerdem ein geeignetes Medium existiert. Ein solches Medium könnte eine offene fraktographische online-Datenbank sein. Eine solche wird im Rahmen der AG Fraktographie im DVM-DGM Gemeinschaftsausschuss "Rasterelektronenmikroskopie in der Materialprüfung" zurzeit erarbeitet.
In this presentation we discuss the online monitoring of metallic AM parts produced by the Laser Powder Bed Fusion (LPBF) process by using optical, thermographic and electromagnetic methods. In a first approach we present the detection of defects generated during the process and discuss how to improve these methods for the optimization of design and production of metallic AM parts.
Laser based powder bed fusion additive manufacturing offers the flexibility to incorporate standard and userdefined scan strategies in a layer or in between the layers for the customized fabrication of metallic components. In the present study, four different scan strategies and their impact on the development of microstructure, texture, and residual stresses in laser powder bed fusion additive manufacturing of a nickel-based superalloy Inconel 718 was investigated. Light microscopy, scanning electron microscopy combined with electron backscatter diffraction, and neutron diffraction were used as the characterization tools. Strong textures with epitaxially grown columnar grains were observed along the build direction for the two individual scan strategies. Patterns depicting the respective scan strategies were visible in the build plane, which dictated the microstructure development in the other planes. An alternating strategy combining the individual strategies in the successive layers and a 67◦ rotational strategy weakened the texture by forming finer microstructural features. Von Mises equivalent stress plots revealed lower stress values and gradients, which translates as lower distortions for the alternating and rotational strategies. Overall results confirmed the scope for manipulating the microstructure, texture, and residual stresses during laser powder bed fusion additive manufacturing by effectively controlling the scan strategies.
The mechanical behavior of fiber reinforced composites with polymer matrix is governed by several mechanisms operating at different length scales. In this contribution we describe first non-destructive techniques which are adequate for the characterization of the fiber-matrix interphase at a microscopic level. In a second step we describe on a mesoscopic level the influence of manufacturing related elements on the mechanical properties of rotor blades for wind turbines. We concentrate on thermography, laminography and ultrasound in connection with mechanical testing systems. Finally we present methods for monitoring rotor blades by using embedded optical fibers.
Die Bereitstellung von zuverlässigen Werkstoffdaten stand für die Werkstoffprüfung seit dem 19. Jahrhundert in zentraler Stelle. Mit der zunehmender Digitalisierung unserer Gesellschaft gewinnt das Datenmanagement insbesondere im Hinblick auf die Modellierungs- und Simulationsaktivitäten an Bedeutung.
In unserem Beitrag beschreiben wir die gegenwärtigen Aktivitäten in Deutschland – insbesondere die NFDI-MatWerk und die BMBF-Initiative MaterialDigital – sowie in Europa und Übersee. Abschließend heben wir die Auswirkungen auf die technische und akademische Aus- und Weiterbildung.
In diesem Beitrag werden am Beispiel von Gasturbinen Verfahren zur Charakterisierung des werkstoff-mechanischen Verhaltens sowie der Gefügeentwicklung von Bauteilen für Anwendungen bei hohen Temperaturen aufgezeigt. Gasturbinen sind technisch gesehen sehr interessante Systeme, die in der Energietechnik und in der Luftfahrt von hoher wirtschaftlicher Relevanz sind. Seit Jahrzehnten gelten Gasturbinen als klassische Innovationstreiber, für ihre Entwicklung wurden bereits maßgebliche Erneuerungen im Bereich der Aerodynamik und der Werkstofftechnik hervorgebracht.
Additive manufacturing (AM) processes allow a high level of freedom in designing and producing components for complex structures. They offer the possibility of a significant reduction of the process chain. However, the large number of process parameters influence the structure and the behavior of AM parts. A thorough understanding of the interdependent mechanisms is necessary for the reliable design and production of safe AM parts.
In this presentation we discuss the online monitoring of metallic AM parts produced by the Laser Powder Bed Fusion (LPBF) process by using optical, thermographic and electromagnetic methods. In a first approach we present the detection of defects generated during the process and discuss how to improve these methods for the optimization of design and production of metallic AM parts.
Das hochaktuelle Thema der Integration und Wiederverwendung von Wissen und Daten aus Herstellung, Bearbeitung und Charakterisierung von Materialien ('Digitalisierung von Materialien') wird in den Projekten Innovationsplattform MaterialDigital (PMD, materialdigital.de) und Materials-open-Lab (Mat-o-Lab, matolab.org) adressiert. In diesem Beitrag werden die Weiterentwicklungen in diesen Projekten hinsichtlich der Speicherung von Zugversuchsdaten gemäß einer normenkonformen (DIN EN ISO 6892-1:2019-11) ontologischen Repräsentation vorgestellt. Das umfasst den Weg von der Entwicklung einer Ontologie nach Norm, der Konvertierung von Daten aus Standardtests in das interoperable RDF-Format bis hin zur Verknüpfung von Ontologie und Daten. Letztendlich können die entsprechenden Daten in einem Triple Store abgelegt und abgefragt werden.
Suitable material solutions are of key importance in designing and producing components for engineering systems – either for functional or structural applications. Materials data are generated, transferred, and introduced at each step along the complete life cycle of a component. A reliable materials data space is therefore crucial in the digital transformation of an industrial branch.
A great challenge in establishing a materials data space lies in the complexity and diversity of materials science and engineering. It must be able to handle data from different knowledge areas over several magnitudes of length scale.
The Platform MaterialDigital (PMD) is expected to network a large number of repositories of materials data, allowing the direct contact of different stakeholders as materials producers, testing labs, designers and end users. Following the FAIR principles, it will promote the semantic interoperability across the frontiers of materials classes. In the frame of a large joint initiative, PMD
works intensively together with currently near 20 research consortia in promoting this exchange (www.material-digital.de).
In this presentation we will describe the status of our Platform MaterialDigital. We will also present in more detail the activities of GlasDigital, one of the joint projects mentioned above dealing with the digitalization of glass design and manufacturing.
(https://www.bam.de/Content/EN/Projects/GlasDigital/glasdigital.html)
The digitalization of materials science and engineering (MSE) is currently leading to remarkable advancements in materials research, design, and optimization, fueled by computer‐driven simulations, artificial intelligence, and machine learning. While these developments promise to accelerate materials innovation, challenges in quality assurance, data interoperability, and data management have to be addressed. In response, the adoption of semantic web technologies has emerged as a powerful solution in MSE. Ontologies provide structured and machine‐actionable knowledge representations that enable data integration, harmonization, and improved research collaboration. This study focuses on the tensile test ontology (TTO), which semantically represents the mechanical tensile test method and is developed within the project Plattform MaterialDigital (PMD) in connection with the PMD Core Ontology. Based on ISO 6892‐1, the test standard‐compliant TTO offers a structured vocabulary for tensile test data, ensuring data interoperability, transparency, and reproducibility. By categorizing measurement data and metadata, it facilitates comprehensive data analysis, interpretation, and systematic search in databases. The path from developing an ontology in accordance with an associated test standard, converting selected tensile test data into the interoperable resource description framework format, up to connecting the ontology and data is presented. Such a semantic connection using a data mapping procedure leads to an enhanced ability of querying. The TTO provides a valuable resource for materials researchers and engineers, promoting data and metadata standardization and sharing. Its usage ensures the generation of finable, accessible, interoperable, and reusable data while maintaining both human and machine actionability.
Gußeisen mit Kugelgraphit und ferritischer bzw. ferritisch-perlitischer Matrix gehören zu einer Werkstoffgruppe, die ausreichende Festigkeiten mit hohen Duktilitäten verbindet. Mit der vorliegenden Arbeit wurden die Kenntnisse über die Zusammenhänge zwischen der chemischen Zusammensetzung, der Gefügeausbildung und den mechanischen Eigenschaften erweitert. Dabei wurden sowohl unterschiedliche Gießverfahren (Sand- und Kokillenguß) in der Herstellung, als auch die Auswirkungen von Umwandlungsprozessen im Gefüge infolge von Wärmebehandlungen diskutiert. Die statistische Auswertung von Einzelergebnissen aus der qualitätssichernden Begutachtung von Lager- und Transportbehältern für radioaktive Stoffe wurden durch mechanische und bruchmechanische Untersuchungen an 24 Werkstoffsorten aus Gußeisen mit Kugelgraphit ergänzt.