Selective Catalytic Reduction of Nitric Oxide by Ammonia over Egg-Shell MnOx/NaY Composite Catalysts
(2002)
A novel composite catalyst system for the selective catalytic reduction (SCR) of NOx by NH3 is described operating at temperatures lower than 470 K in the presence of water with NO conversions of 80100% at space velocities of 30,00050,000 h-1. The catalyst is prepared by egg-shell precipitation of MnO2 on the external surface of zeolite NaY. Structural and thermal stability of precipitated MnO2 as well as of the MnO2/NaY composite catalyst were characterized by N2 adsorption, X-ray diffraction, laser Raman spectroscopy, temperature-programmed reduction, and electron microscopy. MnO2 precipitated on zeolite NaY (15 wt% loading) retained its amorphous state up to calcination temperatures of 775 K. The zeolite component remained structurally intact. Calcination at higher temperatures destroyed the zeolite structure and transformed MnO2 into Mn3O4. DRIFT spectroscopic investigations revealed the presence of symmetric O=NON=O species formally corresponding to N2O3 on the composite catalyst after contact with NO. Catalytic measurements under integral flow conditions showed that the catalyst performance is associated with a close coupling of nitrite formation and its drain off from equilibria with NO/NO2 and nitrate by ammonia. Several results are in line with the diazotation mechanism, including NH3 protonation to NH4+, whereas prevailing Lewis acid sites should enable NH3 activation via amide species, thus leading to a parallel amide/nitrosamide SCR reaction route. The activity-temperature profile fulfills the requirements of a low-temperature NOx reduction catalyst for mobile diesel engines if an ammonia supply is implemented on board, e.g., by urea decomposition.
The morphology and thermal behaviour of polypropylenegraftmaleic anhydride (PPgMA) layered silicate (montmorillonite) nanocomposites were investigated using X-ray diffraction, transmission electron microscopy, differential scanning calorimetry and thermogravimetry. The study focuses on the influence of the presence of oxygen during the preparation of PPgMAnanocomposite using two different modified clays. The nanocomposites show tactoid, intercalated and exfoliated structures side by side with different dominant states depending on the clay used and on the processing conditions. The systems are described as multi-component blends rather than binary blends since the organic ions do not only change the mixing behaviour, but also influence material properties. Beside the physical barrier property of the clay layers also chemical processes were found to play an important role.
Aluminas with Fe2O3 particles finely divided in the Al2O3 matrix were prepared via a crystalline precursor derived from ammonium dawsonite and its calcination. The precursors with Fe content between 1 and 10 wt% were synthesized by reaction of ammonium hydrogen carbonate with mixtures containing aluminium ammonium sulfate and ferric ammonium sulfate. The characterization of the as-synthesized and calcined products by chemical analysis, XRD, EPR, Mössbauer, TEM and adsorption measurements shows that all the Fe3+ ions are incorporated into the structure of dawsonite when the Fe content is low and that the calcined materials with micropores and mesopores (maximum 3040 Å) also contain very small Fe2O3 particles (<10 nm) at higher Fe contents.
Influence of Sb on the structure and performance of Pd-based catalysts: An X-ray spectroscopic study
(2017)
Combined X-ray photoelectron and absorption fine spectroscopy (XAFS) investigations on 10 wt % Pd–16 wt % Sb/TiO2 catalyst allow new insight into the impact of the co-component Sb on the active Pd species, which catalyzes the gas-phase acetoxylation of toluene to benzyl acetate. Ex situ Pd 3d XPS and Pd L-edge XANES studies indicate the presence of an excess electron charge on metallic Pd species (more 4d electrons than in Pd metal) formed after several hours of stream. This observation was explained by the electron transfer from metallic Sb incorporated into the Pd bulk to the neighboring Pd atoms. TEM-EDX analysis confirms the presence of intermixed Pd–Sb particles with an atomic ratio of between 5 and 6 in the most active catalysts and of 3 in deactivated samples. In situ Sb-K-edge XAFS investigations provide evidence that the Pd–Sb interaction is more pronounced under reaction feed than in the ex situ samples.
Improved large mesoporous ordered molecular sieves - Stabilization and acid/base functionalization
(2010)
The preparation of nanoporous materials with enhanced stability using an improved synthesis route using reactive inorganic silica and alumina species is reported. This way improved mesoporous molecular sieves were obtained. The synthesized aluminum substituted mesoporous molecular materials (Al-MMS) contain very large pores of 50200 Å size combined with an improved pore wall thickness. Increased wall thickness and Al substitution lead to an improved chemical stability against alkaline solution. The textural, structural and acid properties are investigated by physico-chemical methods. The catalytic performance acidic materials was tested in the benzoylation reaction; amino functionalized materials were studied in the base catalyzed Michael addition.
Dye activation of heterogeneous Copper(II)-Species for visible light driven hydrogen generation
(2019)
Heterogeneous Cu catalysts are widely used in photocatalytic hydrogen generation. The typical working mode includes the transfer of photo-induced charges from a semiconductor to CuO which itself is reduced to Cu2O to initiate the catalytic cycle. In this contribution a photosensitizer (dye), excited by visible light absorption, was used to transfer an electron to the CuO which after reduction catalyzes the water reduction to hydrogen. Several copper(II)-catalysts on high surface silica were prepared by impregnation or precipitation and applied in photocatalytic water reduction. The best catalyst CuO(Cl0.1)/SiO2, synthesized via incipient wetness impregnation of CuCl2 in MCM-41 and a following precipitation with NaOH, achieved a 6 times higher activity (1702 mmol h-1 g-1) compared to a previously investigated copper system (280 mmol h-1 g-1 for CuI) under the same reaction conditions. All materials were fully characterized by XRD, TEM and N2 sorption and further by magnetic resonance and X-ray methods EPR, ASAXS and XAS. In situ measurements evidenced a reduction of the initial Cu(II)-species, which confirms the (proposed) photocatalytic mechanism.