Direct energy deposition additive manufacturing technologies utilizing an electric arc offer a great potential in generating large volume metal components. However, the selection of process parameters that yield the desired near net shape design as well as the requested mechanical component behavior is not a trivial task due to the complex relationship. Exemplarily for additive manufacturing of high-strength precipitation hardening AlMgSi-aluminum alloy this paper shows the application of a newly developed matching solid welding wire doped with TiB as grain refiner. The correlation between process parameters and component quality is examined analyzing the size and distribution of pores as well as the grain morphology. Furthermore, the influences of different post-weld heat treatments are evaluated to meet the reference mechanical properties of the corresponding wrought material. Finally, the digital integration of the entire additive manufacturing chain enables an overall traceability of the relevant process steps which is the basis for a reliable subsequent quality assessment.
The application of welded aluminum constructions has increased over the last decades due to the high demand for lightweight design. In this context aluminum alloys have a significant importance especially the heat treatable Al-Mg-Si alloys. With regards to welding the heat input causes the dissolving of the precipitates yielding a degradation of the strength properties. Furthermore, there is the risk of solidification cracking during welding for Al-Mg-Si alloys, especially AW 6082-T6. As a consequence Al-Mg-Si alloys are welded using a dissimilar filler material based on 5xxxx aluminum alloys that yields a reduction of resulting strength properties in comparison to the base material. Therefore, the paper presents the application of a novel massive filler wire for Al-Mg-Si alloys. The wire consists of AW 6082 with additionally added AlTi5B1 master alloy fostering the grain refinement of the weld metal. Exemplarily for the base material AW 6082-T6 GMA welding experiments are performed using the novel filler wire 6082TiB. It could be shown that solidification cracks could totally be avoided. The tensile strength of the welded joints are evaluated and compared with weldments using a conventional 5183 filler wire. Artificial aging is performed after welding in order to improve the strength properties by solution hardening showing the potential of these alloys.