Microcrack formation during gas metal arc welding of high-strength fine-grained structural steel
(2014)
The recent development of high-performance-modified spray arc processes in gas metal arc welding due to modern digital control technology and inverter power sources enables a focused spray arc, which results in higher penetration depths and welding speed. However, microcracks occurred in the weld metal while approaching the process limits of the modified spray arc, represented by a 20-mm double layer DV-groove butt-weld. These cracks were detected in structural steel exhibiting a yield strength level of up to 960 MPa and are neither dependent on the used weld power source nor a consequence of the modified spray arc process itself. The metallographic and fractographic investigations of the rather exceptional fracture surface lead to the classification of the microcracks as hot cracks. The effects of certain welding parameters on the crack probability are clarified using a statistical design of experiment. However, these microcracks do not impact the design specification for toughness in the Charpy V-notch test (absorbed energy at -40 °C for the present material is 30 J).
Die aktuelle Normung bezüglich mikroskopischer Untersuchungen von Schweißverbindungen und die Zulässigkeit von Mikrorissen sowie deren Definition ist nicht eindeutig. Nach der Darstellung derzeit gültiger Normen im Bereich der Bewertung von Schweißnähten, Qualifizierung von Schweißverfahren und Ausführung von Schweißverbindungen, wird auf Grundlage aktueller Schweißversuche an hochfesten vergüteten Feinkornbaustählen die Problematik von Mikrorissen diskutiert. Offene Punkte und Fragen bzw. Verbesserungsmöglichkeiten werden aufgezeigt und zur Diskussion gestellt. Schließlich wird auf die Klärung des Einflusses von Mikrorissen auf die mechanisch- technologischen Werkstoffkennwerte der Schweißverbindung unter statischer sowie zyklischer Beanspruchung hingewiesen. ---------------------------------------------------------------------------------------------------------------------------------------------------------------
Neither the latest standardisation with regard to microscopic investigations on welded joints nor the permissibility of microcracks and their definition are unambiguous. According to the representation of currently applicable standards in the fields of the assessment of welds, the qualification of welding processes and the execution of welded joints, the problems associated with microcracks are discussed on the basis of the latest welding tests on high-strength quenched-and-tempered fine-grained structural steels. Not only outstanding points and questions but also improvement possibilities are indicated and opened for discussion. Finally, attention is drawn to the clarification of the influence of microcracks on the mechanical- technological material parameters of the welded joint subjected to both static and cyclic stresses.
Effect of cooling rate on microstructure and properties of microalloyed HSLA steel weld metals
(2015)
Two high strength Nb/Ti microalloyed S690QL steels were welded with identical filler material, varying welding parameters to obtain three cooling rates: slow, medium and fast cooling. As cooling rate increased, the predominantly acicular ferrite in Nb weld metal (WM) is substituted by bainite, with a consequence of obvious hardness increase, but in Ti WM, no great variation of acicular ferrite at all cooling rates contributed to little increment of hardness. The transition between bainite and acicular ferrite has been analysed from the point view of inclusions characteristics, chemical composition and cooling rate. Excellent Charpy toughness at 233 K was obtained with acicular ferrite as predominantly microstructure. Even with bainite weld of high hardness, the toughness was nearly enough to fulfill the minimal requirements. WM for Ti steel showed to be markedly less sensitive to the variations of cooling rate than that for Nb steel.