An experimental setup to integrate laser sensor into conventional GMAW setups via a unified control architecture is described. The setup is used to automate and monitor narrow-gap GMAW. A way to develop GMAW arc-sensors using artificial neural networks using the setup is shown.
The control system is connected to a relational database to store various process measurements. The database can be accessed to filter previous weldments by numerous criteria which allows modelling of process parameter correlation among vast datasets. Such models can be used for process monitoring and control in future applications.
Die in dieser Studie vorgestellte einfache Probengeometrie zeigt sich in Verbindung mit der
angewandten Versuchs- und Auswertemethodik geeignet, um den umwandlungsplastischen (TRIP)-Parameter K unter Verwendung des thermomechanischen Simulators Gleeble® 3500 experimentell zu bestimmen.
Der TRIP-Parameter K wurde für die Grundwerkstoffe S355J2+N und S960QL, sowie für den hochlegierten Zusatzwerkstoff CN13-4 -IG bestimmt.
Die numerische Einflussanalyse zeigt, dass bei der Berechnung von (Oberflächen-)Schweißeigen-spannungen die Vernachlässigung des TRIP-Effektes kaum einen Einfluss auf die Längseigenspannungen hat. Im Gegensatz da zu resultieren gegenüber dem Referenzfall signifikante Abweichungen der
Quereigenspannungen im und um den Schweißnahtbereich.
Die Verdopplung des TRIP-Parameters K gegenüber dem Referenzfall hat nur einen vernachlässigbaren Einfluss auf die Längs- sowie Quereigenspannungen auf der Oberfläche.
Für eine qualitative und quantitative numerische Nachbildung der experimentell bestimmten Längs- und Quereigenspannungen ist die Berücksichtigung der Größenordnung des material-abhängigen TRIP-Parameters K notwendig.
The application of welded aluminum constructions has increased over the last decades due to the high demand for lightweight design. In this context aluminum alloys have a significant importance especially the heat treatable Al-Mg-Si alloys. With regards to welding the heat input causes the dissolving of the precipitates yielding a degradation of the strength properties. Furthermore, there is the risk of solidification cracking during welding for Al-Mg-Si alloys, especially AW 6082-T6. As a consequence Al-Mg-Si alloys are welded using a dissimilar filler material based on 5xxxx aluminum alloys that yields a reduction of resulting strength properties in comparison to the base material. Therefore, the paper presents the application of a novel massive filler wire for Al-Mg-Si alloys. The wire consists of AW 6082 with additionally added AlTi5B1 master alloy fostering the grain refinement of the weld metal. Exemplarily for the base material AW 6082-T6 GMA welding experiments are performed using the novel filler wire 6082TiB. It could be shown that solidification cracks could totally be avoided. The tensile strength of the welded joints are evaluated and compared with weldments using a conventional 5183 filler wire. Artificial aging is performed after welding in order to improve the strength properties by solution hardening showing the potential of these alloys.
Numerical Sensitivity Analysis of TRIP-Parameter K on Weld Residual Stresses and Weld Distortion
(2016)
A combined experimental numerical approach is applied for a sensitivity analysis of the transformation induced plasticity (TRIP)-parameter K on welding residual stresses and welding distortion for the welding of the low-alloyed high-strength S960QOL with the high-alloyed hig-strength filler material CN13-4-IG. A thermo-mechanical FE model of a real GMA welding process was experimentally validated against termperature field, X-Ray stress measurments and optical distortion measurement. Within the sensititvity analysis K was varied and the influence on the calculated welding residual stresses and welding distortion is evaluated by performing corresponding FEA. The correct order of K magnitude is necessary in order to reproduce the residual stresses qualitatively and quantitatively. For the sufficient reproducing of the welding distortion the transformation induced plasticity can be neglected.