Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (45)
- Zeitschriftenartikel (43)
- Beitrag zu einem Tagungsband (23)
- Beitrag zu einem Sammelband (4)
- Forschungsbericht (4)
- Buchkapitel (2)
- Dissertation (1)
- Posterpräsentation (1)
- Forschungsdatensatz (1)
Sprache
- Englisch (68)
- Deutsch (54)
- Mehrsprachig (1)
- Serbisch (1)
Schlagworte
- Grain refinement (7)
- Neural networks (7)
- Welding simulation (7)
- Aluminium (6)
- Digitalisierung (6)
- Welding (6)
- Ökobilanzierung (6)
- Gründungsstrukturen (5)
- Laser beam welding (5)
- Leichtbau (5)
Organisationseinheit der BAM
- 9 Komponentensicherheit (50)
- 9.3 Schweißtechnische Fertigungsverfahren (50)
- 7 Bauwerkssicherheit (7)
- 7.2 Ingenieurbau (4)
- 8 Zerstörungsfreie Prüfung (3)
- 5 Werkstofftechnik (2)
- 5.2 Metallische Hochtemperaturwerkstoffe (2)
- 7.7 Modellierung und Simulation (2)
- 8.5 Röntgenbildgebung (2)
- 5.1 Mikrostruktur Design und Degradation (1)
Eingeladener Vortrag
- nein (45)
The application of welded aluminum constructions has increased over the last decades due to the high demand for lightweight design. In this context aluminum alloys have a significant importance especially the heat treatable Al-Mg-Si alloys. With regards to welding the heat input causes the dissolving of the precipitates yielding a degradation of the strength properties. Furthermore, there is the risk of solidification cracking during welding for Al-Mg-Si alloys, especially AW 6082-T6. As a consequence Al-Mg-Si alloys are welded using a dissimilar filler material based on 5xxxx aluminum alloys that yields a reduction of resulting strength properties in comparison to the base material. Therefore, the paper presents the application of a novel massive filler wire for Al-Mg-Si alloys. The wire consists of AW 6082 with additionally added AlTi5B1 master alloy fostering the grain refinement of the weld metal. Exemplarily for the base material AW 6082-T6 GMA welding experiments are performed using the novel filler wire 6082TiB. It could be shown that solidification cracks could totally be avoided. The tensile strength of the welded joints are evaluated and compared with weldments using a conventional 5183 filler wire. Artificial aging is performed after welding in order to improve the strength properties by solution hardening showing the potential of these alloys.
Die in dieser Studie vorgestellte einfache Probengeometrie zeigt sich in Verbindung mit der
angewandten Versuchs- und Auswertemethodik geeignet, um den umwandlungsplastischen (TRIP)-Parameter K unter Verwendung des thermomechanischen Simulators Gleeble® 3500 experimentell zu bestimmen.
Der TRIP-Parameter K wurde für die Grundwerkstoffe S355J2+N und S960QL, sowie für den hochlegierten Zusatzwerkstoff CN13-4 -IG bestimmt.
Die numerische Einflussanalyse zeigt, dass bei der Berechnung von (Oberflächen-)Schweißeigen-spannungen die Vernachlässigung des TRIP-Effektes kaum einen Einfluss auf die Längseigenspannungen hat. Im Gegensatz da zu resultieren gegenüber dem Referenzfall signifikante Abweichungen der
Quereigenspannungen im und um den Schweißnahtbereich.
Die Verdopplung des TRIP-Parameters K gegenüber dem Referenzfall hat nur einen vernachlässigbaren Einfluss auf die Längs- sowie Quereigenspannungen auf der Oberfläche.
Für eine qualitative und quantitative numerische Nachbildung der experimentell bestimmten Längs- und Quereigenspannungen ist die Berücksichtigung der Größenordnung des material-abhängigen TRIP-Parameters K notwendig.
Life Cycle Assessment (LCA) and Social Life Cycle Assessment (SLCA) are applied in evaluating possible social and environmental impacts of the state-of-art welding technologies, such as Manual Metal Arc Welding (MMAW), Manual Gas Metal Arc Welding (GMAW), Automatic GMAW and Automatic Laser-Arc Hybrid Welding (LAHW). The LCA results indicate that for 1 meter weld seam, MMAW consumes the largest amount of resources (like filler material and coating on electrodes) and energy, which contributes to comparatively higher environmental impacts in global warming potential, acidification, photochemical ozone creation potential and eutrophication than other chosen processes. With regard to social aspects, the health issues and fair salary are under survey to compare the relative potential risk on human health caused by fumes in different welding technologies, and to indicate the sufficiency of current salary of welders in Germany. The results reflect that the wage status of welders is still fair and sufficient. The manual processes bring much higher potential risk of welders health than the automatic processes, especially MMAW.
Der Fokus des vorliegenden Beitrages liegt in der Anwendung der numerischen Schweißsimulation zur Berechnung des schweißbedingten Verzugs an industriellen Bauteilen. Anhand einiger Applikationsbeispiele werden die Möglichkeiten und Einschränkungen am Markt verfügbarer Softwareprodukte aufgezeigt. Hierbei liegt die Gewichtung in einer qualitativ korrekten Abbildung der zu analysierenden Phänomene. Diese stellt die Basis für nachfolgende Parameterstudien dar, welche signifikante Einflussgrößen auf die Verzugsausbildung detektieren. Der Vorteil derartiger simulationsgestützter Analysemethoden gegenüber rein experimentellen Ansätzen wird diskutiert. Aufgrund der heutigen Verfügbarkeit spezialisierter anwenderfreundlicher Schweißsimulationssoftware und günstiger Rechenressourcen macht die Industrie in den letzten Jahren immer mehr von den zahlreichen Vorteilen einer virtuellen Prozessauslegung mit Hilfe der Schweißsimulation Gebrauch. Komplexe Praxisanwendungen können heutzutage innerhalb von 1-2 Wochen unter Berücksichtigung aller Arbeitsschritte bearbeitet werden. Die Anforderungen an den Anwender seitens der Numerik und Materialmodellierung hat sich drastisch verringert, wohingegen ein gewisses Maß an Wissen und Erfahrung vom simulierten Prozess weiterhin entscheidend für den Erfolg der Simulation ist. Am Beispiel des Einspritzventils konnte das Potential einer virtuellen Prozessauslegung anschaulich aufgezeigt werden.
Surface modification of mild steel was undertaken using two covered electrodes and two tubular electrodes. The two covered electrodes are DIN 8555: E6-UM-60 and E10-UM-60GR; however, the two tubular electrodes are E10-GF-60GR1 and E10-GF-60GR2. Chemical analysis for the weld metal and XRD of the flux covering for covered electrodes and flux core for tubular electrodes were conducted. The most important factor in determining the wear resistance is the microstructure of the deposit layers. In similar carbon equivalent electrodes E10-UM-60GR and E10-GF-60GR1, electrode E10-GF-60GR1 (tubular) shows larger carbides area fraction and better wear resistance than electrode E10-UM-60GR (covered). This could be attributed to a lower dilution associated with tubular electrode compared with covered electrode. The two tubular electrodes showed higher wear resistance than the covered electrodes which is mainly due to the larger Fe-Cr carbide precipitation area fraction.