Alkali-activated materials are ideal for the repair of concrete structures in harsh environmental conditions due to their high durability in chemically aggressive environments. However, slag-based mortars, in particular, are prone to shrinkage and associated cracks. In this respect, the application of steel fibres is one solution to reduce the formation of shrinkage induced cracks and to improve post cracking behaviour of these mortars. This study investigated the influence of two different types of steel fibres on the tensile properties of two alkali-activated mortars. Direct tensile tests and single fibre pull-outs were performed to analyse the determining failure modes both on macro and micro scale. Mechanical testing was accompanied by non-destructive testing methods such as digital image correlation and acoustic emission for a detailed analysis of the fracture process.
Since ancient times, marble has been the preferred material for monuments, sculptures, Ornaments and architecture. Though the stone is often a Chosen material, long-term exposure of marble results in cumulative deterioration of the rock fabric. The rate and extent of deterioration depends on the rock fabric and the climatic conditions. Besides the thermal vulnerability of marble, a combination of thermal and hygric fluctuation accelerates the deterioration process. The weathering sensitivity of marbles can be characterised by the irreversible length change of samples after heating under thermohygric conditions as residual strain. This residual strain is a non-reversible deterioration and caused by microcracking induced by a pronounced anisotropy of the thermal dilatation coefficient of calcite.
In brittle materials like marble, cracking and crack growth or friction on crack surfaces are accompanied by release of acoustic waves. The analysis of these acoustic emissions can give a deeper insight into the deterioration mechanism of marble.
In this study, acoustic emissions of thermohygric treated marble were analysed and correlated with ultrasonic velocities, thermal dilatation and residual strains. Therefore, different types of calcitic marble were cyclically heated from 20 °C to 90 °C and after equilibration of the samples cooled down again to 20 °C. While the first cycles were performed under dry conditions, the following were
executed in a humid environment. The analysis of acoustic emissions enables one to determine when cracking occurs during the thermal treatment. It is also possible to differentiate microcracking from internal friction. Furthermore, the evolution of Deterioration can be estimated based on ultrasonic velocities. The combination of acoustic Methods and strain measurement gives an insight into the disintegration mechanism and Supports the development of prevention strategies.
SENSO JOINT - An innovative sensor system for a sustainable joint design of concrete pavements
(2020)
Inacceptable capability and durability of joint sealing systems but also inadequate traffic performance (noise emission; overrolling comfort) up to traffic safety aspects reflect the still enormous demand for data-based description of concrete pavements performance under heavy loading conditions. Especially the deformation behavior of concrete pavement slabs in the joint region in consideration of new pavement construction types and improved concrete mixtures meanwhile established but also under the steeply rising traffic loads is not sufficiently explored. To create a data basis for advanced design rules, evaluation methods and product standards - and with it to improve quality, durability and finally sustainability of pavements - an innovative 3-D sensor system SENSO JOINT adapted to german roadworking requirements and suitable for heavy-duty operating conditions was developed. The contribution introduced describes the development of an extensive technical solution based on the analysis of decisive loads, interactions and boundary conditions. Based on calibration data, results of laboratory testing and finally field-testing on different concrete pavement construction types the outcome of a multi-level evaluation process shall introduce the potential of the new sensor system.
The long-term exposure of marble objects leads to a successive deterioration of the rock fabric and may cause severe damage on cultural heritage objects. The magnitude of disintegration depends on the rock fabric as well as on the climatic conditions. Some types of marble show no considerable damage even if they have been exposed in northern Europe for several decades or centuries. In contrast, other marble varieties are showing severe damage after a few years of weathering. The present study shows that marble decay, along with the initial thermal degradation, is mainly influenced by the hygric and thermo-hygric load, respectively.
The influence of the rock fabric on the resistivity against weathering is also documented. The factors causing marble decay were compared to extensive climate data, which were collected during a scientific project that was started with the aim to develop a covering system for marble sculptures in Berlin. Based on the hygrothermal material properties of the marble and on the climatic conditions, the heat and moisture Transport inside the material and hence the hygrothermal load changes were calculated with a high spatial resolution. The calculations showed that the temperature and moisture fluctuations inside the material are mainly controlled by the dimensions and orientation of the sculptural elements.
The current state of preservation was investigated by two-dimensional ultrasonic tomography. The results show a good correlation to the calculated distribution of the hygrothermal load. Based on this finding, requirements on a protective winter shelter system for the sculptures were defined.
The project results show that in addition to protective covers, regular inspection and maintenance combined with regular cleaning ensures an effective and sustainable protection of marble objects in northern Europe.