Previously on sulfur determination in metal revealed a lack of traceability and inconsistent results. Solving the problems a reference procedure for sulfur measurement in metal are required to build up a reliable reference value. In this study a procedure was developed for quantification of total sulfur at low concentration (in sub ppm level) in metal using inductively coupled plasma-isotope dilution mass spectrometry (ICP-IDMS). The ion exchange method and complexing agent were applied in this procedure to avoid loading large amount of metal into the instrument. Adding ammonia as a complexing agent into sample solution to reduce sulfur-metal co-elute. The procedure shows high performance and it is expressed in % recovery of sulfur (> 90%) and % metal elimination (>99 %). Additionally, relative measurement uncertainties were calculated less than 1.5 % and the results are traceable directly to SI units. This study would establish as reference procedure for sulfur measurement in metal sample which fit for these purpose as follows; for certified reference material and assigned value for inter-laboratory comparison.
Quantification of sulphur in copper metals by isotope dilution LA-ICP-MS using polyethylene frits
(2018)
Sulphur is one of the relevant impurities in copper and its alloys affecting their material properties. To ensure the quality of copper products, fast direct solid sampling techniques are very attractive. However, for the calibration suitable matrix reference materials are required. For the certification of such reference materials appropriate, SI-traceable analytical methods are essential. Therefore, a procedure was developed to quantify total sulphur in copper by combining the classical isotope dilution (ID) technique and laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS).
Here, for the first time, polyethylene (PE) frits were used to prepare appropriate solid samples for the sulphur quantification in copper metals (alloyed/unalloyed) by isotope dilution LA-ICP-MS. The properties of the PE frit meet the requirements as porous material with high absorption efficiency, thermal and chemical resistance as well as low sulphur blank. Different copper reference materials were used to develop and validate the procedure. The copper samples were spiked with 34S, digested with nitric acid and then the digests were absorbed on PE frits. After drying, the frits were analysed by LA-ICP-IDMS using a Nd:YAG laser at 213 nm coupled to an ICP sector field mass spectrometer. It could be demonstrated, that the sample solution dispersed on the frits did not influence the 32S/34S ratio significantly even though the sulphur intensities were fluctuating along the scanned lines. Relative standard deviations of the isotope ratios were below 5 % in average between three line scans (except for the pure spike solution and procedure blank). The measurement results were validated by comparing them with the results obtained by conventional ICP-IDMS after analyte-matrix separation. Plotting the mass fraction of sulphur in copper obtained by LA-ICP-IDMS versus those obtained by ICP-IDMS yields a linear curve with a correlation coefficient of 0.9999 showing a strong agreement between both techniques.
The metrological traceability to the SI from the kg down to the sulphur mass fraction in copper is established by an unbroken chain of comparisons, each accompanied by an uncertainty budget. Thus, the measurement results are considered reliable, acceptable and comparable within the stated measurement uncertainty.