CO2-induced corrosion of casing and tubing steels is a relevant safety issue for compressing emission gasses into deep geological layers (CCS, Carbon Capture and Storage). The influence of CO2 and pressure of the surrounding media on steels is demonstrated in laboratory experiments providing a corrosive environment similar to a geological onshore CCS-site in the Northern German Basin (T = 60 °C, p = 1 - 100 bar, Stuttgart Aquifer, CO2-flow rate of 3 l/h, 7008000 h exposure time). Corrosion kinetics and microstructures were characterized using specimens of heat treated 42CrMo4 (1.7225, casing) and soft annealed X46Cr13 (1.4034, tubing).
In the field of water pipelines, geothermal energy production as well as carbon capture and storage technology (CCS) materials have to provide a high resistance to corrosion and mechanical stress. The combination of cyclic load and corrosive aqueous environment leads to corrosion fatigue of pipes and components (e.g. pumps) and thus inevitably to the reduction of the lifetime of these components. To estimate the reliability of components from adjusted in-situ-laboratory experiments a corrosion chamber was designed and tested with CO2 saturated corrosive aqueous media flowing at a steady rate. Unique feature of this special chamber is its installation directly onto the sample and thus providing flexible usability in almost every testing machine. This allows simultaneous mechanical loading of the sample, operation at temperatures up to 100 °C and exposure to fluid flow of corrosive liquids and gases. The lifetime reduction of AISI 420C (X46Cr13, 1.4034) is demonstrated at T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2. S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue may be identified as failure cause.