In geothermal power plants materials e.g. pumps are exposed to extremely corrosive thermal water. This results in corrosion fatigue and so inevitably the reduction of the lifetime of these components. Also in the field of the carbon dioxide storage technology (carbon capture and storage CCS) components are exposed to a corrosive environment and mechanical stress. In order to gain knowledge upon the corrosion fatigue strength of materials a corrosion chamber for "in situ" conditions was designed and successfully applied.Two different steels X46Cr13 and X5CrNiCuNb16-4 have been tested and their corrosion fatigue behavior was compared. To simulate the frequency of operating pumps (30 – 40 Hz) a resonant testing machine was used. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h to keep stable environmental conditions. The samples have a surface roughness of Rz = 4 to simulate technical machined surfaces. The calculated tensile strength of X46Cr13 with soft annealed microstructure (coagulated cementite in ferrite-perlite matrix) is about 680 MPa and the yield strength is about 345 MPa. The tensile strength of X5CrNiCuNb16-4 is about 1078 MPa and the yield strength about 928 MPa. Testing parameters are: corrosion media: saline aquifer water (Stuttgart Aquifer) temperature of the brine at 60 °C and load ratio of R=-1. For X46Cr13 a stress amplitude between 160 MPa to 270 MPa and for X5CrNiCuNb16-4 a stress amplitude between 150 to 500 was chosen. Cycles until crack initiation differ strongly and were found to start at 5 x 104 up to 12.5 x 106 cycles.X46Cr13 has reached a maximum number of cycles (12.5 x 106) at a stress amplitude of 173 MPa. X5CrNiCuNb16-4 has reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa. The range of scatter for X5CrNiCuNb16-4 is very high (1:34) in comparison the range of scatter for X46Cr13 (1:3.5).
Die klassische Metallographie basiert auf Abbildungen einzelner Schliffebenen und kann auf räumliche Formen und Anordnungen des Gefüges nur bedingt schließen. Die Idee, aus metallographischen Serienschliffen dreidimensionale Gefügestrukturen zu rekonstruieren, ist daher naheliegend und nicht neu. Allerdings ist der Aufwand, in Handarbeit viele Einzel-Schliffe zu präparieren und zu Bildstapeln zusammenzusetzen, sehr hoch und steht einer häufigen Anwendung entgegen.
Deshalb wird an der BAM ein Roboter-gestütztes 3D-Metallographie-System entwickelt, das an einer Schliffprobe die Schritte Präparation und Bildeinzug vollautomatisch mit vielen Wiederholungen ausführt. Die Präparation umfasst Schleifen, Polieren und optional Ätzen der Schlifffläche, der Bildeinzug autofokussierte lichtmikroskopische Aufnahmen bei mehreren Vergrößerungsstufen. Der erhaltene Bildstapel wird anschließend vorverarbeitet, segmentiert und in ein 3D-Modell umgesetzt, das einer mikrotomographischen Aufnahme ähnelt, allerdings mit besserer lateraler Auflösung bei großem Volumen. Im Gegensatz zu tomographischen Verfahren besteht die Möglichkeit der Kontrastierung durch klassische chemische Ätzung. Die Integration eines REMs ist geplant. Bislang durchgeführte Arbeiten verdeutlichen die Möglichkeiten der Darstellung von Heißgas-Korrosionsschichten, Grauguss-Werkstoffen und Keramik-basierten mikroelektronischen Strukturen (Vias).
Design of a high pressure system for in-situ tests on the corrosion fatigue of metallic materials
(2014)
In geothermal power plants pumps are exposed to corrosive and oscillating loads. This leads to corrosion fatigue and reduces the lifetime of certain components. Usually underwater power pumps are placed inside the borehole. In this case an installation depth of 600 to 800 meters below ground level is typical. In these depths an additional load due to high pressure and high temperature is introduced which is based on geothermal brine. Therefore the material which is used for the pump is steel.For fatigue testing at loads existing in deep geological layers an appropriate system for fatigue tests under in-situ conditions was set up. The requirements of the design are: temperature of the corrosion medium of 200 °C pressure of 200 bars and the complete immersion of the specimen in flowing corrosion medium containing mixtures of corrosive gasses during the entire test period.The test system has three main components the corrosion chamber the heating module and the reservoir. It is important that the corrosion chamber is only fixed onto the specimen which allows for highest flexibility of the test system operational in many different test machines. The heating module heats the corrosion medium up to 200 °C. The reservoir make sure that the volume of the corrosion medium satisfies requirements of the DIN 50905 Part 1 is conformed providing minimum required corrosive medium of 10 ml/cm² in relation to the sample surface.This innovative fatigue test system aims at performing in- situ fatigue corrosion tests simultaneously at high pressure and high temperature in liquid and gaseous corrosive environment. Results from the tests will allow determining the fatigue life of several materials influenced by pressure and temperature under corrosive conditions.
CO2-induced corrosion of casing and tubing steels is a relevant safety issue for compressing emission gasses into deep geological layers (CCS, Carbon Capture and Storage). The influence of CO2 and pressure of the surrounding media on steels is demonstrated in laboratory experiments providing a corrosive environment similar to a geological onshore CCS-site in the Northern German Basin (T = 60 °C, p = 1 - 100 bar, Stuttgart Aquifer, CO2-flow rate of 3 l/h, 7008000 h exposure time). Corrosion kinetics and microstructures were characterized using specimens of heat treated 42CrMo4 (1.7225, casing) and soft annealed X46Cr13 (1.4034, tubing).
With CO2 being one reason for climate change carbon capture and storage (CCS) is discussed to mitigate climate change. When emission gases are compressed into deep geological layers CO2-corrosion can easily cause failure of injection pipes. Different steels 42CrMo4, X46Cr13 and X20Cr13 were tested as well as X35CrMo17 and X5CrNiCuNb16-4 in a laboratory Environment similar to the conditions of the CCS engineering site at the Northern German Bassin. Samples were exposed to synthetic aquifer water saturated with technical CO2 at a flow rate of 3 NL/h.
Corrosion rates obtained via mass loss vary in a wide range (0,005 to 2.5 mm/year). The precipitations within the corrosion scale revealed a complicated multiphase layer containing siderite FeCO3, goethite α-FeOOH, lepidocrocite γ-FeOOH, mackinawite FeS and akaganeite Fe8O8(OH)8Cl1,34 and spinelphases of various compositions.
The lifetime reduction of cyclically loaded AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2-saturated hot thermal water is demonstrated in in situ-laboratory experiments (60 °C, brine: Stuttgart Aquifer, flowing CO2: 30 L/h). SN plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion and corrosion fatigue behavior. Maximum number of cycles (here 12.5 × 106 cycles to failure) is reached at σa = 173 MPa. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists and pit corrosion prior to crack initiation may be identified as failure cause.
The appropriate strength of steels used for saline aquifer carbon capture and storage sites (CCS) is usually achieved by applying heat treatments. Thus, heat treatment influences the corrosion resistance for injection pipe steels with 13% chromium and different carbon content: 1.4034/X46Cr13 and 1.4021/X20Cr13 in CO2 saturated saline aquifer water at 60 °C, 1 and 100 bar. X46Cr13 shows better corrosion resistance with respect to corrosion rate, number of pits and maximum intrusion depth. Low corrosion rates are obtained for steels with martensitic microstructures exposed to supercritical CO2 at 100 bar, whereas normalized steels show better corrosion resistance at ambient pressure.
The nucleophilic thiol–ene (thia-Michael) reaction between molecular rods bearing terminal thiols and bis-maleimides was investigated. The molecular rods have oligospiroketal (OSK) and oligospirothioketal (OSTK) backbones. Contrary to the expectations, cyclic oligomers were always obtained instead of linear rigid-rod polymers. Replacing the OS(T)K rods with a flexible chain yielded polymeric products, suggesting that the OS(T)K structure is responsible for the formation of cyclic products. The reason for the preferred formation of cyclic products is due to the presence of folded conformations, which have already been described for articulated rods.
Corrosion fatigue (CF) of duplex stainless steel (DSS) X2CrNiMoN22-5-3 was investigated in in-situ geothermal conditions of the Northern German Basin (NGB). The influence of the load type on CF behavior of the alloy was examined by applying push/pull and rotating bending cyclic load to failure. The hour-glass shaped specimens with both polished and precisely turned surface finish were tested in corrosion chambers allowing for the permanent circulation of Northern German Basin electrolyte heated to 369 K. Additionally, the influence of a protective cathodic potential on the CF life expectancy was investigated by employing a potentiostat. The rotating bending cyclic load led to a higher CF life expectancy, which decreased with increasing duration of the experiment due to a higher deterioration rate of the material. The application of a cathodic potential caused a significant increase of the CF lifespan from 4.7 x 105 (open-circuit potential (OCP)) to 107 cycles (preset threshold cycle number) for the potential range from USHE = – 450 to – 900 mV. Microstructural analysis of the CF damage revealed horizontal grain attack within corrosion pit cavities, multiple fatigue cracks and preferable deterioration of the austenitic phase.
The process chain for Carbon Capture and Sequestration (CCS) includes tubing for injection of CO2 into saline aquifers. The compressed CO2 is likely to contain specific impurities; small concentrations of SO2 and NO2 in combination with oxygen and humidity are most harmful. In addition, CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection has to ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. In this comprehensive paper the investigated materials range from low-alloy steels and 13% Cr steels up to high-alloy materials. Electrochemical tests as well as long term exposure tests were performed in CO2, in brine and combination of both; pressure was up to 100 bar, temperature up to 60 °C. Whereas the CO2 stream itself can be handled using low alloy steels, combinations of CO2 and brine require more resistant materials to control the strong tendency to pitting corrosion. The corrosion behavior of heat-treated steels depends on factors such as microstructure and carbon content. For different sections of the injection tube, appropriate materials should be used to guarantee safety and consider cost effectiveness.