Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (27) (entfernen)
Schlagworte
- Laser cleaning (5)
- Femtosecond laser (4)
- Friction (3)
- Femtosecond laser ablation (2)
- Laser (2)
- Laser-induced periodic surface structures (LIPSS) (2)
- Paper (2)
- Spectroscopy (2)
- Wear (2)
- Ablation (1)
Organisationseinheit der BAM
- 6 Materialchemie (4)
- 6.2 Material- und Oberflächentechnologien (3)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.0 Abteilungsleitung und andere (1)
- 6.3 Strukturanalytik (1)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
- 6.7 Materialsynthese und Design (1)
- 9 Komponentensicherheit (1)
Single-pulse damage thresholds of hydrogenated amorphous carbon (a-C:H) films were measured for 8-ns laser pulses at 532-nm wavelength. Layer thicknesses from below the optical penetration depth to above the thermal diffusion length (60 nm13 µm) were examined. After correction of the damage-threshold values for the fraction of energy effectively absorbed by the material, the damage threshold was found to increase linearly with the layer thickness, also for film thicknesses below the optical penetration depth of a-C:H. The threshold fluence reached the bulk value for a layer thickness equal to the thermal diffusion length. The thermal diffusion coefficient was obtained from fitting the experimental data. Several phenomena like graphitization, blistering, exfoliation, and ablation were observed for different fluence regimes and film thicknesses.
Characterization of laser-generated microparticles by means of a dust monitor and SEM imaging
(2006)
Nanosecond laser (1064 nm wavelength) cleaning of artificially soiled paper as a model sample simulating a real-world artwork was performed. During the cleaning process, the ejection of particles was monitored in situ by means of a dust monitor (8 size classes, ranging from 0.3 µm to >2 µm) and ex situ using a mini-cascade impactor (MKI, 5 stages). The cleaning result was analyzed by scanning electron microscopy (SEM) considering possible laser-induced damages to the substrate. Size distributions of emitted particles were measured depending on the processing parameters: laser fluence, F, and pulse number per spot, N. High numbers of large (>2 µm) particles were collected by the mini-cascade impactor indicating a gas dynamical liftoff process. Obviously, these particles were not affected by the laser-matter interaction. The different methods (SEM, MKI, and dust monitor) are compared with respect to their usefulness for a proper interpretation of the cleaning results.
Laser cleaning of delicate biological composite materials such as ancient parchment manuscripts from the 15th and 16th century and printed paper from the 19th century is demonstrated with an ultraviolet excimer pulsed laser at 308 nm. Laser fluence levels must stay below the ablation and destruction threshold of the parchment or paper substrate, and have to surpass the threshold of the contaminant matter. Foreign layers to be removed must exhibit a higher optical density than the artifact substrates. Synthetic carbonaceous dirt modelled by water-soluble black crayons showed a characteristically weak featureless laser-induced plasma spectroscopy spectrum near the noise limit. It turned out that laser-induced plasma spectroscopy is of limited use in monitoring halting points (or etch-stops) because it relies on the destruction not only of the laterally inhomogenously distributed contaminant but also of pigment phases on a microscopically rough parchment substrate. Laser-induced fluorescence spectroscopy, however, promises to be a valuable non-destructive testing technique for etch-stop monitoring.
A detailed diagnostic study of the interaction of nanosecond laser pulses from the near-ultraviolet to the near-infrared wavelength range with various types of contemporary and ancient parchments is presented. The advantages of laser cleaning due to the absence of chemical agents, spectroscopic selectivity, micro-precision and computer-aided handling can only be verified when physico-chemical diagnostics guarantee destructionless processing. Scanning electron microscopy data are correlated with chemical degradation and morphological changes dependent on the laser fluence and wavelength. It is also shown how transmission electron microscopy, diffuse reflectance infrared Fourier transform spectroscopy, and pyrolysis capillary gas chromatography can be employed in the chemical diagnostics of laser cleaning of parchment. This study suggests that the ageing status of parchment artefacts plays a major role in assessing the laser cleaning limits.
The applicability of excimer laser at 308 nm and Nd:YAG laser at 532 nm with fluences below 0.86 J/cm2 for cleaning of cellulose and paper materials was evaluated. The extent of degradation of purified cotton cellulose and Fabriano paper after laser treatment as well as after a period of accelerated humid oven ageing was determined by following the changes in the degree of polymerization. While irradiation of paper with the excimer laser at 308 nm results in depolymerization of cellulose accompanied by a decrease in ISO brightness, no detrimental effects of Nd:YAG laser treatments were observed.
Cleaning of artificially soiled paper using nanosecond, picosecond and femtosecond laser pulses
(2010)
Cleaning of cultural assets, especially fragile
organic materials like paper, is a part of the conservation
process. Laser radiation as a non-contact tool offers
prospects for that purpose. For the studies presented here,
paper model samples were prepared using three different paper
types (pure cellulose, rag paper, and wood-pulp paper).
Pure cellulose serves as reference material. Rag and woodpulp
paper represent essential characteristics of the basic
materials of real-world artworks. The papers were mechanically
soiled employing pulverized charcoal. Pure and artificially soiled paper samples were treated with laser pulses of
28 fs (800 nm wavelength) and 8–12 ns (532 nm) duration in
a multi pulse approach. Additionally, the cellulose reference
material was processed with 30 ps (532 nm) laser pulses.
Damage and cleaning thresholds of pure and soiled paper
were determined for the different laser regimes. Laser working
ranges allowing for removal of contamination and avoiding
permanent modification to the substrate were found.
The specimens prior and after laser illumination were characterized
by light-optical microscopy (OM) and scanning
electron microscopy (SEM) as well as multi spectral imaging
analysis. The work extends previous nanosecond laser
cleaning investigations on paper into the ultra-short pulse
duration domain.