Development of adapted GMR-probes for automated detection of hidden defects in thin steel sheets
(2016)
Thin steel sheets with a thickness of 0.3 mm and less are the base materials of many everyday life products (cans, batteries, etc.). Potential inhomogeneities such as non-metallic inclusions inside the steel can lead to a rupture of the sheets when it is formed into a product such as a beverage can. Therefore, there is a need to develop automated NDT techniques to detect hidden defects and inclusions in thin sheets during production. For this purpose Tata Steel Europe and BAM, the Federal Institute for Materials Research and Testing (Germany), collaborate in order to develop an automated NDT-system. Defect detection systems have to be robust against external influences, especially when used in an industrial environment. In addition, such a facility has to achieve a high sensitivity and a high spatial resolution in terms of detecting small inclusions in the μm-regime. In a first step, we carried out a feasibility study to determine which testing method is promising for detecting hidden defects and inclusions inside ferrous thin steel sheets. Therefore, two methods were investigated in more detail – magnetic flux leakage testing (MFL) using giant magneto resistance sensor arrays (GMR) as receivers [1,2] and eddy current testing (ET). The capabilities of both methods were tested with 0.2 mm-thick steel samples containing small defects with depths ranging from 5 μm up to 60 μm. Only in case of GMRMFL-testing, we were able to detect parts of the hidden defects with a depth of 10 μm trustworthily with a SNR better than 10 dB. Here, the lift off between sensor and surface was 250 μm. On this basis, we investigated different testing scenarios including velocity tests and different lift offs. In this contribution we present the results of the feasibility study leading to first prototypes of GMR-probes which are now installed as part of a demonstrator inside a production line.
Evaluation of high spatial resolution imaging of magnetic stray fields for early damage detection
(2016)
Metal magnetic memory (MMM) technique with associated ISO 24497-1:3 is gaining considerable interest in the magnetic NDT community. In contrast to traditional Magnetic Flux Leakage (MFL) testing, the inspection objects are not intentionally magnetized by an external magnetic field. Due to the physical coupling between mechanical stress and magnetization of ferromagnetic materials, it is assumed that the distribution of the residual MFL correspond to the internal stress of the specimen, or in the most general sense, to a degradation of the material.
Usually, MMM measurements are performed by relatively bulky magnetic inspection sensors. The evaluation of local magnetic field distribution is limited thereby. Highprecision GMR (Giant Magneto Resistance) measurements in the micrometer regime can provide a higher degree of information due to better spatial resolution.
We present a concise summary of studies on the correlation of magnetic structure and microstructure of steels. In particular, we compare residual stress measurements in S235JRC steel welds by means of neutron diffraction with high resolution magnetic field mappings. Results indicate a qualitative correlation between residual stresses and local stray field variation. In addition, stray field measurements of plastically deformed specimens for quasi-static and cyclic loading cases are discussed. The present study concludes that GMR sensors can detect inhomogeneous plastic deformations of S235JR steel in a very early stage, without specific signal processing according to the ISO 24497-1:3.