The application of lightweight materials for tanks for transportation appears promising. Besides saving weight and therefore transportation costs, new complex geometries that depart from common cylindrical shapes of steel tanks can be manufactured. For transportation of dangerous goods, fire and explosion safety must be maintained to prevent accidents with serious consequences. In this work the fire behavior of lightweight tanks made from glass fiber reinforced plastics (GFRP) with complex geometries is investigated. Pretests on intermediate scale GFRP plates are conducted to identify suitable fire protection systems and surface treatments for composite tanks. The fire resistance is shown to be improved by addition of fire protective coatings and integrated layers. Finally, a complex rectangular GFRP tank with a holding capacity of 1100 liters is fire protected with an intumescent fire coating. The tank is filled up to 80 % with water and burned under an engulfing fully developed fire. It was shown that the intumescent layer could expand before the decomposition of the resin occurred. Furthermore, the adhesion between tank surface and coating was maintained. The structure could withstand a fire for more than 20 min.
In Europe biodiesel gained from rapeseeds are considered as an alternative to common fossil fuels due to its environmental performance and its independence from import of raw materials. Biodiesel is also suitable to serve as blending component to heating oil. In that case, it must be considered that changes of fuel composition might cause material degradation.
The objective of this research was to investigate the resistance of metallic materials exposed to heating oil, heating oil blend B20 with 20 % biodiesel and pure biodiesel. Furthermore, the resistance of metals to eight-year aged B10 and six-year aged pure biodiesel was evaluated. Ageing of biodiesel forms acids and water which might propagate metal corrosion. The investigated metals (aluminium, unalloyed steel, austenitic CrNi-steel, copper, die cast zinc and brass) are commonly used for components in middle distillate facilities.
According to DIN 50905-4 the immersed metals were exposed in a climate chamber at 50°C for 4 weeks. The metallic materials were evaluated as resistant if the annual corrosion rate due to uniform corrosion remained under 0.1 mm/year and no localized corrosion in the form of pitting occurred.
The corrosion rates of the exposed materials stayed far below the limit of 0.1 mm/year for all tested fuels. An exception was die cast zinc ZP0410 in eight-year aged B10; a corrosion rate up to 0.3 mm/year due to uniform corrosion was measured. In no case localized corrosion occurred. Copper and brass caused discolouration of biodiesel from yellow to green.
In conclusion, the tested metallic materials were resistant in heating oil, heating oil blend B20 and pure biodiesel at 50 °C. Even the metals exposed to six-year aged biodiesel and eight-year aged B10 showed no uniform or localized corrosion; except for zinc, which was not resistant in eight-year aged B10.