The effect of the composite plasma parameter P/F, where P is the plasma power and F is the monomer flow rate, on the chemical character of pulsed plasma deposited allyl alcohol films was investigated by ToF-SSIMS. Information on the unsaturated character, the cross-linked and/or branched character of the plasma polymer films was derived in detail. The problem of the retention of OH groups in plasma deposited allyl alcohol films was elucidated in detail using SSIMS data. The lowest conversion rate from the monomer's hydroxyl groups to other oxygen functionalities in the plasma was concluded for the plasma polymer film produced at a P/F ratio of 0.05 W · sccm-1. It was found that the overall oxygen content of the films decreased vs. increasing P/F ratio. Because the freshly prepared films were investigated without air exposure, ageing on ambient air could be studied in detail. It was found that in the case of plasma deposited allyl alcohol films the ageing on air is probably based on two competing processes which are discussed in detail. Additionally, a review of literature data on the characterization of plasma deposited allyl alcohol films is given.
XPS and NEXAFS spectroscopy were used for the chemical characterization of pulsed plasma-deposited ethylene films before and after exposure to ambient air. The influence of external plasma parameters on the spectroscopic results was investigated. Information on the chemical character of the plasma-polymerized films, such as the regularity of the primary structure, the amount of long-living radicals, and branching or cross-linking or both was derived from this data. Irregularity and radical concentration for post-plasma reactions of the plasma-deposited films increased with the duty cycle or power. A decreased level of monomer fragmentation and, consequently, an increase in regularity is partially concluded from the experimental data when the monomer pressure is increased. The concentration of surface radicals available for post-plasma reactions also increased with monomer pressure. The correlation found between the degree of the post-plasma oxygen incorporation and the variation of the various external parameters agreed with earlier ToF-SSIMS findings.
Pulsed plasma deposited styrene and ethylene films were studied by Time of Flight Static Secondary Ion Mass Spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma deposited films was investigated. Approaches for the interpretation of SSIMS spectra of organic materials were reviewed and applied to the evaluation of SSIMS data of plasma deposited films. From these data, information on the chemical character of the plasma deposited films was derived.
When the plasma polymers are exposed to air oxygen incorporation occurs. The oxygen uptake is high at the beginning and then it levels of.
A relation that higher the regularity of the film lower is the oxygen uptake was found. Harder plasma conditions, which could be obtained by applying higher plasma power or lower monomer flow rate, result in higher oxygen uptake and vice versa.
Plasma polymerised films of acrylic acid, allyl alcohol and allyl amine were prepared and studied by XPS (X-ray photoelectron spectroscopy) and XAS (X-ray absorption spectroscopy). The influence of external plasma parameters on certain chemical aspects of the films was investigated. The use of XPS and NEXAFS (near edge X-ray absorption fine structure) as complimentary tools in the surface characterisation of thin films has been highlighted. Certain chemical aspects of the plasma polymerised films such as presence of ROCdouble bond; length as m-dashO in the case of plasma polymerised acrylic acid films, presence of RCdouble bond; length as m-dashO and RCOR bonds in case of plasma polymerised allyl alcohol films and presence of RCdouble bond; length as m-dashN and C?N in case of plasma polymerised allyl amine films were studied. The concentration of ROCdouble bond; length as m-dashO species was found to decrease with increase in r.f. duty cycle in the case of plasma polymerised acrylic acid films. In case of plasma polymerised allyl alcohol films there is a decrease in the concentration of RCdouble bond; length as m-dashO species and increase in the concentration of RCOR species at higher pressures, while in the case of plasma polymerised allyl amine films the concentration of RCdouble bond; length as m-dashN and C?N increases at higher powers, with an increase in C?N more pronounced at higher powers.