Study of effects of plasma parameters by characterization of pulse plasma deposited organic films
(2003)
Pure and PDMS contaminated PS oligomers films were investigated both by time-of-flight static secondary ion mass spectrometry (TOF-SSIMS) and X-ray photoelectron spectroscopy (XPS).
The secondary ion spectra from the PDMS contaminated PS oligomers were almost completely related to PDMS. XPS revealed a PDMS contamination characterized by a silicon surface concentration of 6 at.%. Obviously siloxane contaminants existing on the surface of a silicon wafer may diffuse towards the PS oligomers outermost surface resulting in a rather high PDMS surface concentration of about 85%. Due to the known differences in the information depth and sensitivity of SSIMS and XPS very different detection limits are to be considered.
In elimination of siloxane contaminants by ultrasonication in hexane was found to be an effective way. Another common organic cleaning procedure, which is ultrasonication in trichloroethylene (TCE), subsequently in isopropanol and finally in acetone was found to be ineffective for cleaning of PDMS contaminated silicon wafers.
Chemical properties of plasma-polymerized styrene films can be effectively controlled by the appropriate choice of external plasma parameters, such as duty cycle, power and monomer pressure. Chemical properties here are the regularity of the primary structure, the amount of long living radicals and branching or cross-linking or both in plasma polymerized styrene films, which can be indirectly monitored by X-ray photoelectron spectroscopy (XPS) and near edge X-ray absorption fine structure (NEXAFS) spectroscopy. Principally, XPS and NEXAFS spectra of plasma-polymerized styrene show all the spectroscopic fingerprints characteristic of atactic polystyrene indicating an inherent similarity of the respective primary chemical structures. There is an increase in irregularity and radical concentration for the plasma deposited films with increasing duty cycle or power. With an increase in monomer pressure, a decreased level of monomer fragmentation and, consequently, an increase in regularity must be concluded from the experimental data. The applied power regulates the fragmentation of the monomers as monitored by spectroscopic signals correlated to the aromatic rings. A trend in the extent of the post-plasma oxygen incorporation according to the variation of the various external plasma parameters was deduced, which agrees with earlier ToF-SIMS findings
Pulsed-plasma-deposited ethylene films were studied by time-of-flight static secondary ion mass spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma-deposited ethylene films was investigated. From these data, information on the chemical character of the plasma-deposited ethylene films was derived. The investigation of the effect of external plasma parameters on the chemical character of the plasma-deposited ethylene films revealed that there were some drastic changes in the secondary ion mass spectra of the films. It was found that fragmentation and re-arrangement of the monomer molecules in the plasma, which affects the chemical character of the deposited films, vary according to the external plasma parameters. When the plasma polymers are exposed to air, extensive oxygen incorporation occurs. The oxygen uptake is high at the beginning and then it levels of. Some indications for the formation and decay of peroxy radicals (COO) and, subsequently, hydroperoxides (COOH) are found. It was observed that the oxygen uptake of the plasma deposited ethylene films increase when the plasma conditions become harder.
Pulsed plasma-deposited polystyrene films were studied by time-of-flight static secondary ion mass spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma-deposited polystyrene films was investigated. From these data, information on the chemical character of the plasma polystyrene films was derived. In the range of deposition conditions applied in this study, the fragmentation of styrene is a minor process. The main process is probably the radical chain propagation to polymers. All the polystyrene plasma polymers, relying on ToF-SIMS, seem to be rather similar to a reference polystyrene oligomer sample. When the plasma polymers are exposed to air, extensive oxygen incorporation occurs. Oxygen uptake was found to alter the emission probabilities of secondary ions. A relation between the regularity of the plasma polymers and the amount of oxygen incorporation was found. The result was that the chemical regularity of the plasma polystyrene decreases when the effective power in the plasma is increased.
Static TOF-SIMS results strongly underpin earlier conclusions from ESCA, XANES, and tracer studies that the accumulation of fluorine and chlorine at the surface of chromia by a heterogeneous reaction with a chlorofluorocarbon compound results in the formation of mixed chromium oxide halide species and not in the nucleation of CrCl3 and/or CrF3 phases.