Two methods were employed to prepare hyperbranched polyamine ester (HPAE)/kaolinite (Ka) nanocomposites resulting in different morphologies. In the case of the in situ polymerization, diethanolamine is inserted as monomer between the Ka layers and polymerized with methyl acrylate to prepare HPAE/Ka–DEA nanocomposites. For the ex situ method, Ka is modified with dodecylamine and solution-blended with HPAE. The former method leads to an intercalated morphology where the latter approach results in an exfoliated structure, as proofed by SAXS and TEM. A complementary combination of methods like differential scanning calorimetry (DSC), broadband dielectric relaxation (BDS), and specific heat spectroscopy (SHS) was used to investigate both kinds of nanocomposites in detail. Above Tg, the dielectric spectra are dominated by the conductivity contribution while the segmental dynamics is retrieved by SHS. A comparison of the temperature dependencies reveals a decoupling of segmental dynamics and conductivity, which becomes weaker with decreasing fragility.
Hyperbranched PAMAM/ Kaolinite Nanocomposites: Decoupling phenomenon and conductivity mechanism
(2018)
Increasing demands of the daily life requires a continuous discovering of new and tailored properties of materials that can be utilized in covering the requirements in several fields. Hyperbranched polymers (HBPs) are macromolecules that are characterized by a highly branched structure and multiplicity of reactive end groups, which could be promising for numerous applications. Here, hyperbranched poly(amidoamine) (HPAMAM)/ Ka nanocomposites was prepared via an in-situ polymerization and an ex-situ method. The latter approach leads to a partly intercalated structure of the nanocomposites, while the former method results in an exfoliated morphology. Α combination of different techniques such as broadband dielectric spectroscopy (DBS), SXAS, FTIR, TEM, and DSC are employed to study the prepared samples. For the HPAMAM/ Ka-DCA nanocomposites (an ex-situ samples), the results indicated that the dc conductivity is increased by 4 orders of magnitude, with increasing concentration of the Ka-DCA. As an interesting result is that a significant decoupling between the characteristic time for conductivity relaxation and the segmental dynamics was observed, which depends on the concentration of the nanofiller. For the HPAMAM/ EDA nanocomposites (an in-situ polymerization), the dc conductivity is also increased with increasing the concentration of the Ka-EDA. The decoupling phenomenon and conductivity mechanism are discussed in detail.
Hyperbranched polyamine ester (HPAE)/ kaolinite nanocomposites were papered via an ex situ (solution-based) method. The kaolinite has been modified by dodecylamine (DCA). SAXS measurements revealed that the Ka interlayer space increased from 0.71 to 3.6 nm-1. A partly exfoliated structure of the HPA/Ka-DCA nanocomposites was proved by SAXS and TEM. By a combination of BDS and SHS, the relaxation properties of the nanocomposites were investigated in dependence on frequency and temperature. The activation energies of γ-relaxation for the nanocomposites were lower than the values found for the pure HPAE. The segmental dynamics (α- relaxation) was found to be screened out by the conductivity contribution. While it is retrieved by SHS employing AC-chip calorimetry. A systematic change of the dynamic glass transition estimated by AC-chip calorimetry was observed, which is in agreement with a behavior expected for a confined sample. The confinement effect of the Ka-DCA nanofillers reduces the glass transition temperature Tg and enhances, meanwhile, the electrical conductivity of the polymer. By comparing the temperature dependence of the dynamic glass transition measured with SHS and that of the dc conductivity measured by dielectric spectroscopy, a decoupling in their temperature dependencies was found.
With increasing concentration of the nanofiller, which results in a stronger glass-formation behavior, this decoupling becomes weaker.
Hyperbranched poly(amidoamine)/kaolinite nanocomposites: Structure and charge carrier dynamics
(2017)
An ex-situ approach was applied to prepare nanocomposites from hyperbranched poly(amidoamine) and modified kaolinite (Ka-DCA). The structure of the polymer and the corresponding nanocomposites was investigated by FTIR, DSC, SAXS and TEM. SAXS might suggest a partly exfoliated structure of the nanocomposites, which was supported by TEM. The molecular dynamics was studied by means of broadband dielectric spectroscopy (BDS). The dielectric spectra are dominated by a conductivity
contribution at higher temperatures for all samples investigated. The obtained results further indicated that DC conductivity is increased by 4 orders of magnitude with increasing concentration of Ka-DCA nanofiller. Further, a significant separation between the conductivity relaxation time and that of segmental dynamics was observed. The decoupling phenomenon and the conductivity mechanism were discussed in detail. This study provides insights about the influence of the nanofiller on the structure and the conductivity contribution of nanocomposites of hyperbranched polymers including the decoupling phenomenon and fragility.