Filtern
Dokumenttyp
- Zeitschriftenartikel (2)
- Vortrag (2)
- Posterpräsentation (2)
- Beitrag zu einem Tagungsband (1)
Schlagworte
- Concrete (2)
- SealWasteSafe (2)
- Ultrasound (2)
- Alkali-Activated Material (1)
- Alkali-Silica Reaction (ASR) (1)
- Brunauer-Emmett-Teller (BET) Method (1)
- CT (1)
- Computed tomography (1)
- Computertomographie (1)
- Crack Detection (1)
Organisationseinheit der BAM
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (7) (entfernen)
Eingeladener Vortrag
- nein (2)
With a goal to improve our understanding of the relationships between microstructural features and ultrasonic signal behavior, concrete specimens of varying water-to-cement ratio were imaged using X-ray computed tomography (CT), and subsequently subjected to ultrasonic testing. From the CT scans, measurements were made of cement paste density and number of interfaces. Ultrasonic signals produced using a through-transmission configuration were analyzed and fit to a diffusion model to separate absorption from scattering attenuation. The results showed that at the frequencies tested, ultrasonic dissipation rate correlated weakly with paste density, while diffusivity correlated well with number of interfaces, but only if entrained air is considered separately. Cement paste density was found to be very well predicted by diffusivity, leading to a clear power-law relationship between diffusivity and compressive strength.
This poster provides an overview of ultrasonic investigations of an engineered test barrier at ERAM Morsleben, which were completed as part of contractual work with the Bundesgesellschaft für Endlagerung mbH (BGE). This includes both experiments with the Large Aperture Ultrasound System (LAUS) and the ultrasonic borehole array. Also included in the poster is a description of the planned BAM thematic project “SealWasteSafe”. In particular, the proposed geopolymer materials are described and future research requirements are detailed.
The proposed BAM project SealWasteSafe will advance the state of the art for the construction and monitoring of safe sealing systems for underground repositories of radioactive or toxic waste. During this project, a novel salt concrete exhibiting neither significant cracking nor shrinkage will be optimized for use in the sealing systems. The composition of this material will be based on alkali-activated materials, which are characterized by particularly small thermal deformations during the hardening reaction. Quality assurance and continuous monitoring systems developed during this project will be demonstrated not only for high reliability, but also for resistance to highly alkaline environments and to water intrusion along cables or at sensor locations. A variety of sensors will be used in combination with wireless Radio Frequency Identification (RFID) technology to record moisture, temperature, and, if necessary, corrosion activity within the sealing system. Distributed Fibre Optic Sensor (FOS) technology will also be used for strain, temperature, and moisture content measurement. Ultrasound-based measuring methods will be utilized for the detection of cracks and delaminations. Additionally, digital image correlation and acoustic emission analysis will be used for deformation measurements and crack detection. A novel borehole probe and advanced ultrasound imaging techniques will be further developed to track cracks and delaminations within the host rock in 3D. The surface-based Large Aperture Ultrasound System (LAUS) will also be utilized to detect cracks and delaminations deep below the exterior surface of the sealing system. Although the focus of this project will be on the host rock salt, the resulting technologies will be intentionally developed in a way that facilitates their adaptation to other host rocks.
Durch den großflächigen Einsatz der Computertomographie (CT) in unterschiedlichen Industriebereichen steigen auch die Anforderungen an die quantitative Bildanalyse. Subjektive Bildwahrnehmung muss durch objektive Algorithmen ersetzt werden. In diesem Artikel stellt die Bundesanstalt für Materialforschung und -prüfung (BAM), die seit den 1980er Jahren an der Entwicklung der industriellen CT beteiligt ist, anhand ausgewählter Beispiele den aktuellen Stand ihrer Analysemethoden an verschiedenen Anwendungsbeispielen der CT vor.
The closure of underground nuclear waste disposal facilities requires reliable gas- and water-tight engineered barriers. In Germany, barriers made from salt concrete have been evaluated in full scale. While the barriers seem to fulfill the requirements regarding permeability, some unexpected cracks have been detected at the surface and at depth. In cooperation between the Federal Company for Radioactive Waste Disposal (BGE) and the Federal Institute for Materials Research and Testing (BAM), several experiments have been carried out to evaluate the applicability for ultrasonic measurements in crack detection and general quality assurance. Both commercial instruments and specially developed devices have been tested on site.
Using commercial ultrasonic echo devices designed for concrete inspection it was possible to detect cracks and objects in salt concrete up to a depth of 2 m. The check for delamination in shotcrete is another field of application. A unique device available at BAM, the wide aperture, deep penetration instrument LAUS, was able to locate cracks and objects up to a depth of 8 m so far, which is thought to be a record for ultrasonic echo measurements in concrete. Adapted imaging procedures, partly adopted from geophysics, helped to reveal 3D structure at depth.
In addition, we have developed ultrasonic probes to be deployed in boreholes, currently at up to 20 m depth. They can collect information on cracks and other features in a radius of about 1.5 m around the borehole in the current version and might be used in echo or transmission mode. Evaluation experiments have been performed at an experimental barrier at the ERAM site in Morsleben, Germany. The results showed several empty and injected cracks as well as built-in instrumentation. The results have been verified using borehole endoscopy as well as core examination and will be used to set up a reliable quality assurance system for engineered barriers. All instruments are based on ultrasonic shear wave transducers with a frequency range between 25 kHz and 100 kHz. Current research focuses on the improvement of the hardware (e. g. optimization of array characteristics) and imaging techniques such as Reverse Time Migration, both aiming at the improvement of depth of penetration, resolution and probability of detection.
Intensified Alkali-Silica Reaction (ASR) damage has occurred on German roadways in recent years, leading to requirements for compulsory pre-construction investigation of aggregate alkali sensitivity using concrete tests with external alkali supply. However, since these tests are time-consuming and cost-intensive, there is interest in replacing them with a solubility test on pure aggregate in 0.1 M KOH solution at 80°C with a defined NaCl content (1wt.-%). In this context, the influence of aggregate pore structure on SiO2 and Al2O3 solubility was investigated in this project. This paper compares the results of porosity studies with X-ray Computed Tomography (3D-CT) and the Brunauer-Emmett-Teller (BET) method on individual quarried and river gravel granules of both rhyolite and greywacke. For visualization and quantification of both externally accessible and fully enclosed surfaces of granules using X-ray 3D-CT, special software tools were developed. The results demonstrated that the river gravel granules had significantly larger externally accessible surfaces than the quarried granules. BET measurements on individual stones showed, as expected, that measured surfaces were about three orders of magnitude larger than those from the X-ray 3D-CT analyses due to the higher spatial resolution of BET. There was no apparent correlation between the X-ray 3D-CT and BET surface areas. Mercury porosimetry measurements indicate that this may be due to the presence of significant porosity below the spatial resolution of the X-ray 3D-CT. A comparison of SiO2 and Al2O3 solubility measurements with the X-ray 3D-CT and BET surface area data resulted only in weak, inconclusive correlations, indicating the need for further experimental investigation.
Attenuation of ultrasonic signals in concrete has the potential to carry much information about the microstructure of the material. In this work a series of concrete specimens of varying porosities and pore size distributions were internally imaged with x-ray computed tomography (CT), and then subsequently examined with throughtransmission ultrasound. The CT images were used to quantify both capillary porosity of cement paste as well as internal interfaces that are likely to produce elastic wave scattering. Ultrasound signals were represented as a diffusion process such that absorption and scattering attenuation could be isolated. As implemented, the diffusion model was a poor predictor of capillary porosity, while diffusivity was a reasonable predictor of scattering interfaces. Diffusivity was found to scale extremely well with small scale porosity, which made it a good predictor of compressive strength.