Filtern
Dokumenttyp
- Zeitschriftenartikel (11)
- Vortrag (8)
- Beitrag zu einem Tagungsband (5)
- Posterpräsentation (4)
- Buchkapitel (2)
Schlagworte
- Computed tomography (4)
- Concrete (4)
- Faserverstärkter Beton (FRC) (3)
- Feuchtigkeitsmessung (3)
- Fire (3)
- HPC (3)
- High-performance concrete (3)
- Röntgencomputertomographie (CT) (3)
- X-ray Computed Tomography (CT) (3)
- Alkali-Silica Reaction (ASR) (2)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (22)
- 8.5 Röntgenbildgebung (21)
- 7 Bauwerkssicherheit (10)
- 7.1 Baustoffe (8)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (7)
- 7.4 Baustofftechnologie (2)
- 8.0 Abteilungsleitung und andere (1)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (1)
- 8.6 Faseroptische Sensorik (1)
Eingeladener Vortrag
- nein (8)
Fiber-reinforced concretes (FRCs) offer significant improvements in tensile strength and durability compared to most other concrete mixes.
However, for safe and efficient use of FRC in large structures, anisotropy of fiber orientation needs to be understood and properly controlled. In this project, both cored samples extracted from a FRC slab and FRC samples cast individually in molds were assessed using X-ray computed tomography (CT) and measurements of fiber orientation were extracted from the resulting CT images. These results showed that fibers within the slab were highly anisotropic in orientation while fibers in individually cast samples showed a much more heterogeneous distribution of orientations.
This indicates that fiber orientation is highly dependent on the casting process and suggests that FRC can only be safely and efficiently utilized if anisotropic fiber orientation is properly accounted for during design and optimized casting methods are used during construction.
Attenuation of ultrasonic signals in concrete has the potential to carry much information about the microstructure of the material. In this work a series of concrete specimens of varying porosities and pore size distributions were internally imaged with x-ray computed tomography (CT), and then subsequently examined with throughtransmission ultrasound. The CT images were used to quantify both capillary porosity of cement paste as well as internal interfaces that are likely to produce elastic wave scattering. Ultrasound signals were represented as a diffusion process such that absorption and scattering attenuation could be isolated. As implemented, the diffusion model was a poor predictor of capillary porosity, while diffusivity was a reasonable predictor of scattering interfaces. Diffusivity was found to scale extremely well with small scale porosity, which made it a good predictor of compressive strength.
Für die Festigkeit von faserverstärkten Betonen spielt die beim Gießvorgang hervorgerufene Faseranisotropie eine wichtige Rolle. In den computertomographischen Aufnahmen lässt sich die anhand der Eigenvektoren der Hessianmatrix an der Faser ermittelte räumliche Orientierung der Fasern berechnen und im sphärischen Koordinatensystem darstellen.
Mit für die CT-Anlagen ausgelegten Prüfeinrichtungen ist es möglich mechanische Belastungen, Wärmeeinwirkung und Feuchtetransport in Betonproben während einer CT-Messung durchzuführen. Die Analyse dieser In-situ Messungen erfordert zum Teil speziell auf die Erfordernisse angepasste Auswerteverfahren. Dazu zählen die automatische Rissdetektion oder die Korrektur der Streustrahlung bei der Wasseraufnahme.
Unilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes in moisture distribution during thermal exposure.
However, none of these methods has been able to depict the moisture distribution in three dimensions (3D), so the link between pore size, concrete micro-structure and moisture content is missing. The research project presented in this paper aims to fill this gap by developing a new multi-level test methodology to characterise non-destructively the temporal course of spatial moisture distribution during unilateral thermal exposure. The procedure used during this programme included the collection of X-ray 3D-computed tomography (CT) measurements using a miniaturised specimen subjected to in-situ thermal exposure and the comparison of those CT results with the results of one-dimensional NMR-relaxometry before and after the heating process.
In the first step, a mobile heating device was developed, built and tested. To simulate a unilaterally-heated construction component, a cylindrical specimen made of HSC (Ø = 40 mm, L = 100 mm) was cast into an impermeable glass ceramic shell. The ceramic shell ensured a one-dimensional moisture flux and limited the thermal expansion of the concrete. An additional high-temperature wool (HTW) insulating shell ensured a one-dimensional heat flux. The heating device, which operated using infrared radiation (IR), allowed the unilateral heating of the specimens up to 300 °C using variable heating regimes.
In the second step, the mobile heating device was integrated into the CT-scanner, which enabled the collection of measurements before, during and after heating. By subtraction of successive 3D-CT images, X-ray attenuation differences could be resolved three-dimensionally in the specimen and interpreted as changes in the moisture content.
Initial results show that this test methodology can monitor the 3D changes of moisture content inside the specimen during thermal exposure. It enables the researcher to visualise areas with moisture accumulation as well as dehydrated areas inside the specimen. Comparative one-dimensional NMR-relaxometry measurements confirm the results of the CT image analysis.
Intensified Alkali-Silica Reaction (ASR) damage has occurred on German roadways in recent years, leading to requirements for compulsory pre-construction investigation of aggregate alkali sensitivity using concrete tests with external alkali supply. However, since these tests are time-consuming and cost-intensive, there is interest in replacing them with a solubility test on pure aggregate in 0.1 M KOH solution at 80°C with a defined NaCl content (1wt.-%). In this context, the influence of aggregate pore structure on SiO2 and Al2O3 solubility was investigated in this project. This paper compares the results of porosity studies with X-ray Computed Tomography (3D-CT) and the Brunauer-Emmett-Teller (BET) method on individual quarried and river gravel granules of both rhyolite and greywacke. For visualization and quantification of both externally accessible and fully enclosed surfaces of granules using X-ray 3D-CT, special software tools were developed. The results demonstrated that the river gravel granules had significantly larger externally accessible surfaces than the quarried granules. BET measurements on individual stones showed, as expected, that measured surfaces were about three orders of magnitude larger than those from the X-ray 3D-CT analyses due to the higher spatial resolution of BET. There was no apparent correlation between the X-ray 3D-CT and BET surface areas. Mercury porosimetry measurements indicate that this may be due to the presence of significant porosity below the spatial resolution of the X-ray 3D-CT. A comparison of SiO2 and Al2O3 solubility measurements with the X-ray 3D-CT and BET surface area data resulted only in weak, inconclusive correlations, indicating the need for further experimental investigation.
The closure of underground nuclear waste disposal facilities requires reliable gas- and water-tight engineered barriers. In Germany, barriers made from salt concrete have been evaluated in full scale. While the barriers seem to fulfill the requirements regarding permeability, some unexpected cracks have been detected at the surface and at depth. In cooperation between the Federal Company for Radioactive Waste Disposal (BGE) and the Federal Institute for Materials Research and Testing (BAM), several experiments have been carried out to evaluate the applicability for ultrasonic measurements in crack detection and general quality assurance. Both commercial instruments and specially developed devices have been tested on site.
Using commercial ultrasonic echo devices designed for concrete inspection it was possible to detect cracks and objects in salt concrete up to a depth of 2 m. The check for delamination in shotcrete is another field of application. A unique device available at BAM, the wide aperture, deep penetration instrument LAUS, was able to locate cracks and objects up to a depth of 8 m so far, which is thought to be a record for ultrasonic echo measurements in concrete. Adapted imaging procedures, partly adopted from geophysics, helped to reveal 3D structure at depth.
In addition, we have developed ultrasonic probes to be deployed in boreholes, currently at up to 20 m depth. They can collect information on cracks and other features in a radius of about 1.5 m around the borehole in the current version and might be used in echo or transmission mode. Evaluation experiments have been performed at an experimental barrier at the ERAM site in Morsleben, Germany. The results showed several empty and injected cracks as well as built-in instrumentation. The results have been verified using borehole endoscopy as well as core examination and will be used to set up a reliable quality assurance system for engineered barriers. All instruments are based on ultrasonic shear wave transducers with a frequency range between 25 kHz and 100 kHz. Current research focuses on the improvement of the hardware (e. g. optimization of array characteristics) and imaging techniques such as Reverse Time Migration, both aiming at the improvement of depth of penetration, resolution and probability of detection.
Conventional concrete and UHPC performance-damage relationships identified using computed tomography
(2016)
To make significant advances in concrete engineering, it will be necessary to understand the behavior of cementitious materials at the microscale. To achieve this goal, the nature of damage initiation and growth needs to be understood at very small scales. This Research program sought to increase that understanding through the collection of microscale data using X-ray computed tomography (CT). The tensile and compression behavior of both ultra-high performance concrete (UHPC) and conventional concrete were investigated as a part of this
program. Relationships were identified between mechanical performance parameters, such as stiffness degradation and work of load, and cracking parameters, such as crack volume and crack surface area, that could be quantified mathematically and implemented into future finite element analysis (FEA) models. The results of this Research program have the potential to improve the accuracy and resiliency of numerical models and to provide insight to the materials engineering community concerning the optimal use of UHPC.
In this work, which is part of a larger research program, a framework called “virtual data fusion“ was developed to provide an automated and consistent crack detection method that allows for the cross-comparison of results from large quantities of X-ray Computed Tomography (CT) data. A partial implementation of this method in a custom program was developed for use in research focused on crack quantification in Alkali-Silica Reaction (ASR)-sensitive concrete aggregates. During the CT image processing, a series of image analyses tailored for detecting specific, individual crack-like characteristics were completed. The results of these analyses were then “fused” in order to identify crack-like objects within the images with much higher accuracy than that yielded by any individual image analysis procedure. The results of this strategy demonstrated the success of the program in effectively identifying crack-like structures and quantifying characteristics, such as surface area and volume. The results demonstrated that the source of aggregate has a very significant impact on the amount of internal cracking, even when the mineralogical characteristics remain very similar. River gravels, for instance, were found to contain significantly higher levels of internal cracking than quarried stone aggregates of the same mineralogical type.
This paper focuses on the experimental evaluation of one of the key microstructural Parameters of a short-fiber reinforced composite – the orientation distribution of fibers. It is shown that computed tomography (CT) produces results suitable for reconstruction of the orientation distribution function. This function is used for calculation of the effective elastic properties of polymer-fiber reinforced concrete. Explicit formulas are derived for overall elastic moduli accounting for orientation distribution in the frameworks of the noninteraction approximation, the Mori–Tanaka–Benveniste scheme, and the Maxwell scheme.
The approach illustrated can be applied to any kind of composite material.
The benefits of including fibers in ultra-high performance concrete (UHPC) are attributed to their good bond with the matrix and, hence, an optimal utilization of their properties. At the same time, though, fiber reinforcement may contribute to anisotropy in the composite material and induce weak areas. The influence of the fibers’ orientation on the material properties is a matter of current scientific discourse and it is known to play a vital role in structural design. In the case studies presented herein, mechanical laboratory tests using pulsating load regimes on UHPC with a strength of more than 200 MPa were simulated by use of finite element models. The orientations of the fibers were measured for each test sample prior to failure using an X-ray computed tomography (CT) scanner, and these orientations are explicitly implemented into the model. The paper discusses the methodology of merging data retrieved by CT image processing and state-of-the-art FE simulation techniques Moreover, the CT scanning was carried out throughout the testing procedure, which further enables the comparison of the mechanical tests and the FE models in terms of damage propagation and failure patterns. The results indicate that the overall fiber configuration and behavior of the samples can be realistically modelled and validated by the proposed CT-FE coupling, which can enhance the structural analysis and design process of elements produced with steel fiber reinforced and UHPC materials.