Conventional concrete and UHPC performance-damage relationships identified using computed tomography
(2016)
To make significant advances in concrete engineering, it will be necessary to understand the behavior of cementitious materials at the microscale. To achieve this goal, the nature of damage initiation and growth needs to be understood at very small scales. This Research program sought to increase that understanding through the collection of microscale data using X-ray computed tomography (CT). The tensile and compression behavior of both ultra-high performance concrete (UHPC) and conventional concrete were investigated as a part of this
program. Relationships were identified between mechanical performance parameters, such as stiffness degradation and work of load, and cracking parameters, such as crack volume and crack surface area, that could be quantified mathematically and implemented into future finite element analysis (FEA) models. The results of this Research program have the potential to improve the accuracy and resiliency of numerical models and to provide insight to the materials engineering community concerning the optimal use of UHPC.
Fiber-reinforced concretes (FRCs) offer significant improvements in tensile strength and durability compared to most other concrete mixes.
However, for safe and efficient use of FRC in large structures, anisotropy of fiber orientation needs to be understood and properly controlled. In this project, both cored samples extracted from a FRC slab and FRC samples cast individually in molds were assessed using X-ray computed tomography (CT) and measurements of fiber orientation were extracted from the resulting CT images. These results showed that fibers within the slab were highly anisotropic in orientation while fibers in individually cast samples showed a much more heterogeneous distribution of orientations.
This indicates that fiber orientation is highly dependent on the casting process and suggests that FRC can only be safely and efficiently utilized if anisotropic fiber orientation is properly accounted for during design and optimized casting methods are used during construction.
With a goal to improve our understanding of the relationships between microstructural features and ultrasonic signal behavior, concrete specimens of varying water-to-cement ratio were imaged using X-ray computed tomography (CT), and subsequently subjected to ultrasonic testing. From the CT scans, measurements were made of cement paste density and number of interfaces. Ultrasonic signals produced using a through-transmission configuration were analyzed and fit to a diffusion model to separate absorption from scattering attenuation. The results showed that at the frequencies tested, ultrasonic dissipation rate correlated weakly with paste density, while diffusivity correlated well with number of interfaces, but only if entrained air is considered separately. Cement paste density was found to be very well predicted by diffusivity, leading to a clear power-law relationship between diffusivity and compressive strength.
Attenuation of ultrasonic signals in concrete has the potential to carry much information about the microstructure of the material. In this work a series of concrete specimens of varying porosities and pore size distributions were internally imaged with x-ray computed tomography (CT), and then subsequently examined with throughtransmission ultrasound. The CT images were used to quantify both capillary porosity of cement paste as well as internal interfaces that are likely to produce elastic wave scattering. Ultrasound signals were represented as a diffusion process such that absorption and scattering attenuation could be isolated. As implemented, the diffusion model was a poor predictor of capillary porosity, while diffusivity was a reasonable predictor of scattering interfaces. Diffusivity was found to scale extremely well with small scale porosity, which made it a good predictor of compressive strength.