The most efficient construction materials for boiler water walls and superheaters in
steam power plants are ferritic and martensitic steels. In practical operation tubes are
simultaneously exposed to combustion gas and air/steam on their opposite surfaces. The
corrosion behaviour of ferritic-martensitic steels under such dual atmospheres is nondistinctive
and has therefore been investigated in a special designed test equipment between 500 and
620°C. The power plant conditions were simulated wi th a flowing and pressurised (80 bar)
combustion gas on the inner side of the tube which mainly consists of H2O and/or CO2. On the
outer side, the tube material was exposed to air. It was discovered that under similar
temperatures the oxides formed on the air side under dual atmosphere conditions were
significantly different to the oxide scales formed when the alloy was exposed to air only. It is
assumed that the anomalous corrosion behaviour during the dual atmosphere exposure is due
to the hydrogen transport through the bulk alloy from the combustion gas side to the air side.
Basic research on the corrosive effect of flue gases has been performed at the BAM Federal Institute for Materials Research and Testing (Germany). Conditions at both high and low temperatures were simulated in specially designed experiments. Carburization occured in flue gases with high CO2 content and temperatures higher than 500 °C. In SO2 containing flue gases sulphur was detected in the oxide scale. At lower temperatures no corrosion was observed when gases with low humidity were investigated. Humidity higher than 1500 ppm was corrosive and all steels with Cr contents lower than 12% revealed corroded surfaces. At low temperatures below 10 °C a mixture of sulphuric and nitric acid condensed on metal surfaces. Acid condensation caused severe corrosion. Humidity, CO2, O2, and SO2 contents are the important factors determining corrosion. Below 300 °C acid condensation is the primary reason for corrosion. Low humidity and low temperatures are conditions which can be expected in the CO2 separation and treatment process. This work includes major conditions of the flue gas and CO2 stream in CCS plants and CCS technology.