Saprotrophic basidiomycetes decompose wood in aerobic environments and can cause economic damage. The availability of nitrogen is determining for decomposition, and diazotrophic bacteria might enhance the nitrogen availability by fixation of atmospheric N2. Simultaneous decomposition by basidiomycetes and diazotrophs may intensify decomposition, because N2 fixation requires ATP, which could be provided during cellulose decomposition. In this study, the interaction was analysed by measurements of the nitrogen content and the δ15N values in biomass. Besides, the activity of basidiomycetes, influenced by different nitrogen sources, was determined. The analysis of the nitrogen content in biomass of Oligoporus placenta and Trametes versicolor proved the efficient uptake of organic nitrogen by wood-decomposing fungi even if only traces were available. In the presence of urea and ammonium chloride, the growth of T. versicolor was intensified. At cultivations in a 15N2/O2 atmosphere, the diazotrophic bacteria Azotobacter croococcum, Beijerinckia acida and Novosphingobium nitrogenifigens covered 1 to 13% of the nitrogen in their biomass by N2 fixation. If basidiomycetes and diazotrophs were co-cultivated, only B. acida fixed N2 and transferred it to both fungi. A. croococcum and N. nitrogenifigens did not coexist with the fungi. The effects of the nitrogen sources, i.e., organic nitrogen in the medium, organic nitrogen in sapwood and N2 from air, on the biomass of the mentioned basidiomycetes were determined in experiments according to full-factorial experimental plans. Organic nitrogen in the medium increased the growth of both basidiomycetes significantly. In additional experiments, the nitrogen source in the medium was replaced by an inoculum of B. acida. Then, atmospheric N2 supported the bacterial growth, which caused a significant decrease of basidiomycetal biomass compared to N2-free conditions. The presence of B. acida increased the biomass of T. versicolor to a low extent, but had no effect on the biomass of O. placenta. In contrast to the previously mentioned organisms, Hypholoma fasciculare and proteobacteria occur together in nature. In experiments, the growth of biomass of H. fasciculare and proteobacteria was supported by organic nitrogen, urea and ammonium chloride. The N2 fixation of the bacteria was significant but amounted to a low extent and was therefore explained by adsorption and not by nitrogenase activity. Competition between H. fasciculare and proteobacteria for the same nitrogen sources appeared more probable than N enrichment by diazotrophic activity.
Carbon nanofibers (CNFs) were functionalized by a multistage process including oxidation, reduction and silanization. The chemical modifications were examined by Fourier transform infrared spectroscopy, X-ray photoelectron spectrometry, Raman spectroscopy and thermogravimetric analysis. The silanized CNFs were then added into an epoxy resin (EPON 828) to study the effect of the surface modification of CNFs on the properties of nanocomposites. For comparison, nanocomposites containing original unmodified CNFs were also investigated. Scanning electron microscopy indicates better dispersion of modified fibers in the epoxy polymer matrix; the mechanical and thermal properties of composites are also improved; the electrical conductivity of the composites is reduced.
Carbon nanofibers (CNFs) were functionalized with 3-glycidoxypropyltrimethoxysilane and dispersed into epoxy resin. The chemical modification of CNFs was confirmed by FTIR, SEM, EDX and TGA measurements. After silanization, FTIR showed the existance of epoxy ring; EDX detected Si element; while TGA indicated 1.1 wt.% Si on CNFs. Mechanical properties were analyzed by DMA. Silanized CNFs/epoxy composites demonstrated improved dispersion of CNFs in the matrix, and an enhancement of storage modulus for about 20% compared to the neat matrix, which indicated that the modification of CNFs improved the adhesion between fillers and matrices. DC electrical conductivity of CNFs was reduced about 7-fold compared to the original CNFs due to the silane coating. Accordingly, the composites containing silanized CNFs also had lower electrical conductivity than those containing original CNFs. In spite of decreased electrical conductivity, thermal conductivity of silanized CNFs/epoxy composites was increased due to the surface modification of CNFs.