Due to addition of minor amounts of suitable additive combinations to BaTiO3 powder the sintering temperature was reduced to 900 °C. Excellent densification (more than 98% of theoretical density) and good dielectric properties were achieved after sintering at 900 °C for 2 hours. Dielectric properties can be improved by modifying the composition of sintering additives and additon of further dopants. The low sintering temperature of newly developed capacitor material allows a co-sintering with pure silver electrodes. No interfacial reaction between silver electrodes and ceramics was observed by microprobe analysis. The dielectric constants of about 1200 to 3000 and the dielectric losses of about 0.008 to 0.02 were measured (f = 1 kHz, T = 25 °C). The temperature dependency of dielectric constant for new capacitor materials is low, almost X7R characteristics. Furthermore, the densification and the dielectric properties of embedded capacitors in LTCC were investigated.
Further miniaturization of electronic packaging calls for integration of magnetic functional components into LTCC modules. For integration of magnetic function into LTCC, low fired MnZn- and NiCuZn-ferrites which can be fully densified at the standard LTCC sintering temperature of 900°C were developed. To co-fire these ferrite tapes with dielectric tapes the sintering shrinkage and the coefficient of thermal expansion of ferrite and dielectric tapes must be matched. For each ferrite material a new LTCC dielectric material was designed. The embedded ferrite tapes into new LTCC dielectric tapes can be sufficiently densified during co-firing at 900°C without any cracking. Compared to separately sintered ferrites the permeability of embedded ferrite tapes is reduced. For embedded NiCuZn ferrites permeabilities between 230 and 570 (at 2 MHz) according to the thickness of the embedded ferrite layer were measured. For embedded MnZn ferrites a permeability of 300 was measured.
Silver in LTCC - Interfacial reactions, transport processes and influence on properties of ceramics
(2009)
Integration of magnetic functional components in LTCC Circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of p=900 were developed which can be fully densified at the Standard LTCC sintering temperature of 900 °C. Successful co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal expansion during the cooling period - especially in the temperature range below the transformation point of the glassy phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found by EDX measurements. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, i.e. a decrease of more than 50 %.
To investigate the origin of this permeability reduction, Ni-Cu-Zn ferrite laminates were sintered separately, and in combination with alumina release tapes or dielectric tapes, respectively. SEM and EDX analysis of co-fired laminates reveal differences in the ferrite grain growth behavior. Ferrite laminates with homogeneous microstructure and grain size up to 50 pm exhibit large permeability. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between high permeability and volume fraction of large ferrite grains. Regions of fine and coarse grains inside the ferrite layers show different bismuth concentration; the Bi-content is larger in regions of fine ferrite grains.
We have studied the integration of Ni-Cu-Zn ferrite spinels as well as substituted hexagonal Co2Y-and M-type ferrites into LTCC (Low Temperature Ceramic Co-firing) modules. The cofiring behavior and the magnetic properties of these materials were investigated and evaluated for multilayer applications. Ni-Cu-Zn ferrites exhibit permeabilities of µ=300–500 for operating frequencies in the MHz range. Cu-substituted Y-type ferrites Ba2Co2-x-yZnxCuyFe12O22 in combination with sintering additives display sufficient shrinkage and densification at 900°C. A permeability of µ=10 is observed; however, substituted Co2Y-type ferrites do not exhibit long-term stability at 900°C. Co/Ti-substituted M-type ferrites BaFe12-2yCoyTiyO19 (y=1.2) with planar magneto-crystalline anisotropy exhibit excellent soft magnetic behavior. Using sintering additives, complete densification is reached at 900°C and a permeability of µ=15 and a resonance frequency of larger than 1?GHz are observed. Integration of ferrite multilayer inductor components into LTCC modules using free and constrained cofiring technologies is demonstrated.