Eingeladener Vortrag
- nein (6)
Ceramic components with complex shape cannot be produced frequently by usual ceramic forming and sintering processes. Therefore, numerous joining methods were developed and introduced in industrial scale. Nowadays, multi-stage Mo-Mn-process and active brazing are preferentially used, if temperature-stable and gastight joints are required. Unfortunately, both processes involve cost-intensive thermal processes: hydrogenous atmosphere is essential for metallization in Mo-Mn-process and active brazing takes place under vacuum. Thermal processes can be drastically simplified by using Reactive Air Brazing (RAB). Joining under air atmosphere is an interesting alternative, especially to join oxide ceramic components among themselves. So far, main disadvantage of RAB is low strength of join connections.
Aim of this investigation was the development of high-strength, thermal shock resistant and gastight ceramic-ceramic joints by RAB. Therefore,
- commercial, silver and copper oxide containing RAB soldering composition was modified by addition of ceramic particles with low thermal expansion coefficients (TEC). Hence, thermal misfit between TEC of solder and ceramic components was significantly reduced.
- RAB soldering paste was replaced with newly developed RAB composite tapes, produced by ceramic “doctor blade” technology. Thereby, improved potential exist to tailor the brazing layer relating to composition, thickness and thickness uniformity.
Gastight alumina-alumina, alumina-zirconia and zirconia-zirconia joints with strongly improved strength were produced by novel composite tapes. No strength degradation of joints was observed after thermal cycling up to 700°C.
We have studied the integration of Ni-Cu-Zn ferrite spinels as well as substituted hexagonal Co2Y-and M-type ferrites into LTCC (Low Temperature Ceramic Co-firing) modules. The cofiring behavior and the magnetic properties of these materials were investigated and evaluated for multilayer applications. Ni-Cu-Zn ferrites exhibit permeabilities of µ=300–500 for operating frequencies in the MHz range. Cu-substituted Y-type ferrites Ba2Co2-x-yZnxCuyFe12O22 in combination with sintering additives display sufficient shrinkage and densification at 900°C. A permeability of µ=10 is observed; however, substituted Co2Y-type ferrites do not exhibit long-term stability at 900°C. Co/Ti-substituted M-type ferrites BaFe12-2yCoyTiyO19 (y=1.2) with planar magneto-crystalline anisotropy exhibit excellent soft magnetic behavior. Using sintering additives, complete densification is reached at 900°C and a permeability of µ=15 and a resonance frequency of larger than 1?GHz are observed. Integration of ferrite multilayer inductor components into LTCC modules using free and constrained cofiring technologies is demonstrated.
For co-firing of MnZn-ferrite tapes and LTCC dielectric tapes, the sintering shrinkage curves and the coefficient of thermal expansion of ferrite and dielectric tapes were matched. Highly densified embedded ferrite without any cracks could be manufactured by co-firing at 900 °C in nitrogen atmosphere. However, the permeability of MnZn-ferrite co-fired between dielectric tapes is significantly reduced (µ´=100) compared to that of the separately sintered ferrite (µ´=500). Changes in the phase stability and microstructure of MnZn-ferrite were investigated to explain the permeability reduction in the embedded ferrite. It is supposed that early densification of the dielectric tapes on the top and bottom of the ferrite layer prevent the gas exchange during sintering which is necessary for (Mn,Zn)Fe2O4 spinel formation. As a result, high amount of Fe2O3 secondary phase and a Mn-rich spinel phase with low permeability remain in the embedded ferrite layer.
Co-firing of low temperature co-fired ceramics (LTCC) and functional ceramics like ferrites is a promising approach to increase the level of integration in future microsystems, and to create new applications for LTCC technology. Besides the development of compatible material combinations, the configuration of the sintering process is an important issue for successful co-firing. A method is presented to derive the linear shrinkage mismatch of a material combination based on density data calculated from the master sintering curves (MSCs) of the individual materials. The influence of the firing profile on the constraint in the combined multilayer can be anticipated using this method. To investigate and improve the co-firing of ferrite and dielectric tape, the shrinkage mismatch with respect to heating rate was studied. A significant reduction of shrinkage mismatch was found for increased heating rates. The calculated results are verified by lateral shrinkage measurements on combined laminates.
Integration of magnetic functional components in LTCC circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of µ = 900 were fully densified at the standard LTCC sintering temperature of 900°C. Co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal contraction during the cooling period – especially in the temperature range below the transformation point of the glass phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer laminates composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found using microprobe analysis. Pure ferrite laminates show homogeneous microstructure with large grains up to 50 µm in diameter. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between permeability and volume fraction of large ferrite grains. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, that is a decrease of more than 50%.
Integration of magnetic functional components in LTCC Circuit boards calls for co-firing of dielectric and ferrite tapes. Ni-Cu-Zn ferrites with permeability of p=900 were developed which can be fully densified at the Standard LTCC sintering temperature of 900 °C. Successful co-firing of this ferrite with dielectric tapes requires the adaptation of the shrinkage behavior of the materials as well as the thermal expansion during the cooling period - especially in the temperature range below the transformation point of the glassy phase of the dielectric tape. To match these preconditions, a new dielectric LTCC material with steep sintering curve and high thermal expansion coefficient was designed. Sintered multilayer composed of Ni-Cu-Zn ferrite and tailored dielectric tapes are free of cracks and possess no open porosity. No significant interdiffusion between the ferrite and dielectric tapes was found by EDX measurements. Compared to pure ferrite laminates the permeability of co-sintered Ni-Cu-Zn ferrite layers is drastically reduced to 400, i.e. a decrease of more than 50 %.
To investigate the origin of this permeability reduction, Ni-Cu-Zn ferrite laminates were sintered separately, and in combination with alumina release tapes or dielectric tapes, respectively. SEM and EDX analysis of co-fired laminates reveal differences in the ferrite grain growth behavior. Ferrite laminates with homogeneous microstructure and grain size up to 50 pm exhibit large permeability. However, growth of ferrite grains does not take place near the interface between ferrite and release or dielectric tapes. There is a strong correlation between high permeability and volume fraction of large ferrite grains. Regions of fine and coarse grains inside the ferrite layers show different bismuth concentration; the Bi-content is larger in regions of fine ferrite grains.
Further miniaturization of electronic packaging calls for integration of magnetic functional components into LTCC modules. For integration of magnetic function into LTCC, low fired MnZn- and NiCuZn-ferrites which can be fully densified at the standard LTCC sintering temperature of 900°C were developed. To co-fire these ferrite tapes with dielectric tapes the sintering shrinkage and the coefficient of thermal expansion of ferrite and dielectric tapes must be matched. For each ferrite material a new LTCC dielectric material was designed. The embedded ferrite tapes into new LTCC dielectric tapes can be sufficiently densified during co-firing at 900°C without any cracking. Compared to separately sintered ferrites the permeability of embedded ferrite tapes is reduced. For embedded NiCuZn ferrites permeabilities between 230 and 570 (at 2 MHz) according to the thickness of the embedded ferrite layer were measured. For embedded MnZn ferrites a permeability of 300 was measured.
The sintering temperature of BaTiO3 powder was reduced to 900 °C due to the ZnO-B2O3-Li2O-Nb2O5-Co2O3 addition. Excellent densification was achieved after sintering at 900 °C for 2 h. The low sintering temperature of newly developed capacitor materials allows a co-firing with pure silver electrodes. The dielectric constant and the temperature stability of the dielectric constant are strongly correlated with the composition of the ZnO-B2O3-Li2O additives. A high dielectric constant up to 3000 and a dielectric loss less than 0.024 were measured on multilayer capacitors sintered at 900 °C with silver inner electrodes.
By addition of LiF-containing sintering additives to commercial BaTiO3 powder, more than 98% of the theoretical density was reached at a sintering temperature of 900 °C both on powder compacts and laminates. Dielectric measurements were performed on ceramic samples in the temperature and frequency ranges from -20 °C to 125 °C and from 103 to 106 Hz, respectively. High relative permittivity (εr ~ 3160) and low dielectric loss (tan δ ~ 0.014) were measured for tapes of the favoured material. The breakdown strength for tapes with a thickness of about 80 µm is 30 kV/mm. The microprobe analysis showed, that no interfacial reaction between the dielectric layer and the Ag-electrode had occurred.
The newly developed barium titanate ceramics completely densifying at 900 °C turned out to be promising for integration of buried capacitors in LTCC multilayers.