Melamine resins were used as 50-µm-thick fire retardant coatings for polypropylene (PP). Preceding deposition, low-pressure plasma polymer films of allyl alcohol were coated onto PP to improve the adhesion between PP and melamine resin coatings. The efficiency of such fire retardant coatings was confirmed by flame tests. The plasma-deposited polymer and the dip-coated melamine resin films were characterized by Fourier transform infrared-attenuated total reflectance spectroscopy and X-ray photoelectron spectroscopy (XPS). The adhesion of coatings was measured using a 90° peel test with a doubled-faced adhesive tape. To detect the locus of failure, the peeled layer surfaces were inspected using optical microscopy and XPS. Thermal properties of PP thick melamine resin-coated films were analyzed by thermogravimetric analysis.
The adhesion of thick poly(allylamine)-polyphosphate layers (1 µm) deposited by the wet-chemical layer-by-layer technique (LbL) onto polyethylene or polystyrene (each 100 µm) was very low. To promote the adhesion of these LbL layers the polyolefin substrates were oxidized at the surface by short exposure to the oxygen plasma (2 or 5 s) and subsequently coated with an interlayer of plasma-deposited poly(allylamine) or poly(allyl alcohol) (100 nm). The plasma polymer interlayers have improved strongly the adhesion between polyolefin substrates and polyphosphate coatings. Such phosphate coatings are interesting for life sciences (nucleotide formation) but also for fire retardancy in combination with N-rich compounds such as melamine.
The intention was to prefer chemical and hydrogen bonds for adhesion promoting because of their high binding energy. Therefore, the introduced oxygen-containing groups at the polyolefin surface could interact with the OH or NH2 groups of the adhesion-promoting plasma polymer interlayer. These groups were also able to interact strongly with the poly(allylamine)-polyphosphate topcoating.
The coated polyolefins were investigated using Fourier Transform Infrared Spectroscopy in Attenuated Total Reflectance mode (FTIR-ATR), X-ray Photoelectron Spectroscopy (XPS), Thermo-Gravimetric Analyses (TGA) and Atomic Force Spectroscopy (AFM) and 90° peel test.
The thermal degradation behavior of poly(vinyl chloride) (PVC) and poly(N-vinylpyrrolidone) (PVP) blends was investigated using potentiometric measurements of the released HCl gas during the degradation process, estimating the degree of discoloration of the degraded samples and measuring the thermal stability values (Ts) values. The influence of the PVP percentage in the blend and, moreover, the addition of commercial dibasic lead carbonate stabilizer to the blend on its thermal stability was studied. It was found that the dehydrochlorination rate of the blend was promoted by increasing the PVP concentration in the blend.