The paper presents the microstructure, chemical and phase composition of thin scale, obtained as a result of high temperature corrosion of X20Cr13 stainless steel. Samples were exposed to gas atmosphere of the following composition: 0.25 vol.% of SO2 and 99.75 vol.% of Ar at 600 °C for 5 h. As a consequence, thin compact scale was formed on steel surface.
This scale consisted of three different zones. An amorphous zone was formed close to steel surface. Then, nanocrystalline Zone could be observed. Finally, larger grains were formed during the corrosion process. The analysis of the chemical composition revealed higher concentration of chromium near steel surface. In contrast, to chromium, the content of iron, increased near the scale surface. It was found out that the (Cr, Mn, Fe)5O12 phase appeared in the thin scale.
Thin Sol-Gel Alumina Coating as Protection of a 9% Cr Steel Against Flue Gas Corrosion at 650 °C
(2018)
Samples of sol-gel alumina coated and uncoated P92 steel were exposed to flue gas at 650 °C for 300 h. As result of this treatment a 50 µm thick bi-layered oxide scale had formed on the surface of the uncoated sample. Below the scale a 40 µm thick inner oxidation zone was detected. In contrast, the porous, micron thick alumina coating enabled the formation of a chromium oxide scale with a thickness of some nanometers at the interface between steel substrate and coating. In this case high temperature corrosion of the steel was prevented so far.