Filtern
Dokumenttyp
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (3)
- Vortrag (1)
- Posterpräsentation (1)
Sprache
- Englisch (10)
Schlagworte
- TEM (3)
- High-temperature corrosion (2)
- 12%Cr steel (1)
- AlPO4 (1)
- Alumina coating (1)
- Boehmite (1)
- Corrosion protection (1)
- CrN/NbN (1)
- Creep (1)
- Cyclic steam oxidation (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
This work investigates the distribution of Chromium and Cobalt as well as other elements and their effect on the corrosion scale formation of ferritic-martensitic alloys under single and dual conditions. For this purpose, coupons of technical VM12-SHC alloy and model Fe-13Cr alloy were annealed at 600°C for 960 h in artificial flue gas. This kind of experiment represents the classical single condition corrosion test. To realize dual condition, an experimental setup was designed in such way that each face of the specimens could be in contact with a different atmosphere.
In this presentation the comparison between single and dual conditions will be evaluated in terms of phase composition of the scale and material loss. Preliminary results show clear deviations between both conditions in the distribution of chromium, as well as the diffusion outward of cobalt in the technical alloy.
Under cyclic thermomechanical loading conditions, various effects such as strain accumulation, creep damage, ageing, fatigue etc. may occur in the material of a gas turbine blade. Depending on the loading conditions, all these effects contribute to reduce the lifetime of the component. Subject of the present work is the development of a lifetime model able to discriminate between the different damage mechanisms, as well as the development of a material model to describe the mentioned effects and thus providing the input data for lifetime prediction.
The steam side oxidation of ferritic–martensitic VM12-SHC steel was investigated under thermo-cyclic conditions in water steam at 620/320 °C and 30 bar with a focus on assessing the influence of pre-oxidation time, specimen geometry and surface finish. The specimens were pre-oxidized under isothermal conditions in water steam at 620 °C and 30 bar for 500 h or 1500 h. After pre-oxidation treatment, all specimens were subjected up to 258 thermal cycles. Three different geometries—rectangular coupons, U-shaped ring segments and ring samples—were investigated to evaluate the influence of open/closed shape, and flat/curved surface on corrosion rate. At the same time, two types of surface finish were considered: “as received” and “ground.” The formation of a protective scale by pre-oxidation was investigated. EBSD and ESMA analyses revealed that the Cr-content of the alloy appeared to be insufficient for obtaining a protective oxide scale under studied conditions, at the same time the anayses confirmed that initial oxidation depends on presence of minor alloying elements as Si and Mn, strong oxide formers which can alter the kinetics and morphology of the corrosion reaction. Moreover, rectangular coupons with small wall thickness and flat surface exhibited the highest corrosion rate, while “ground” curved samples showed only local oxidation. This indicates that for same pre-oxidation time, oxidation kinetics is controlled by curvature.
The paper presents the microstructure, chemical and phase composition of thin scale, obtained as a result of high temperature corrosion of X20Cr13 stainless steel. Samples were exposed to gas atmosphere of the following composition: 0.25 vol.% of SO2 and 99.75 vol.% of Ar at 600 °C for 5 h. As a consequence, thin compact scale was formed on steel surface.
This scale consisted of three different zones. An amorphous zone was formed close to steel surface. Then, nanocrystalline Zone could be observed. Finally, larger grains were formed during the corrosion process. The analysis of the chemical composition revealed higher concentration of chromium near steel surface. In contrast, to chromium, the content of iron, increased near the scale surface. It was found out that the (Cr, Mn, Fe)5O12 phase appeared in the thin scale.
Microstructure, smoothening effect, and local defects of alumina sol-gel coatings on ground steel
(2017)
Porous alumina films with thicknesses of a few microns were prepared via a dip-coating technique on steel P92. The coating is shown to protect the steel against massive corrosion, which is typical in the hot reactive environment of coal fired power plants. To mimic real conditions ground steel plates were coated with a boehmite-sol. This leads to an overall smoothing of the formerly rough surface. In the following short annealing step the inner porous construction with worm-like particles consisting of nano-crystallites and amorphous alumina is formed. Due to the simultaneous diffusion of chromium and iron ions out of the bulk steel material into the porous alumina coating, a dense interface with satisfactory adhesion is formed. However, the film exhibits few local defects like cracks or dense alumina nodules caused by steep edges in the ground surface or agglomeration of boehmite-sol components, respectively. Cracks especially have to be avoided. This problem can be overcome so far by slight modifications in the sol preparation process and surface treatment of the substrates. Nevertheless the results demonstrate the potential of sol-gel based alumina coatings as a time- and cost-saving protection type for commercial steel P92.
Oxidation of a Fe –13Cr alloy under water vapor at 600°C produced a zone of nano-sized precipitation underneath the outside scale formed by iron oxides and Fe–Cr spinel. The majority of the spinel layer shows a fixed orientation relationship to the ferritic matrix: {1 0 0}α || {1 0 0}sp & <0 1 1>α || <0 0 1>sp . However, also the discovered precipitated particles are characterized by the same crystallographic orientation relationship to the respective ferritic parent grain. The habit of the precipitates is best described by a lath morphology with their main axis parallel to <1 0 0> of ferrite. Energy dispersive X-ray spectroscopy (EDX) and electron backscatter diffraction (EBSD) in scanning electron microscope (SEM) have been applied to characterize the oxide layer in micrometer scale. The clearly smaller precipitates were subsequently investigated by transmission electron microscopy (TEM). Specimens have been prepared by focused ion-beam (FIB) milling at an area previously characterized by EBSD. They cover the ferritic base material, but mainly the precipitation zone and the Fe–Cr spinel layer. Energy filtered selected area diffraction (SAD) in the conventional (C)TEM and high-angle annular dark field (HAADF) imaging in the scanning (S)TEM mode were employed in the characterization of the specimens.
To increase efficiency, modern steam plants are pushing their operational regime from super-critical (600 °C/300 bar) to ultra-super-critical (740/760 °C/350 bar) stretching existing turbine materials to their limits. The focus is on new generation functional materials and technologies which complement the inherent properties of existing materials.
Current work proposes a novel High Power Impulse Magnetron Sputtering (HIPIMS) Deposition technology, for the first time, for deposition of a ceramic based CrN/NbN coating with a nanoscale multilayer structure (bi-layer thickness Δ = 1.9 nm) with superior adhesion (LC2 = 80 N) to protect low Chromium P92 steel widely used in steam power plants. Thermodynamic calculations predict the equilibrium phases and aggressive gaseous compounds generated by the interaction of steam with the coating. CrN/NbN coated P92 steel samples oxidised at 600 °C in a high pressure (50 bar) 100% steam atmosphere for up to 1000 h reveal the coating's superior oxidation resistance and protective mechanisms, especially against the detrimental effect of Hydrogen. High temperature (650 °C) Tensile Strength, Low Cycle Fatigue and Creep tests confirm that, unlike other state-of-the-art PVD technologies, HIPIMS is not detrimental to the mechanical properties of the substrate material. Water droplet erosion tests confirm no measurable weight loss after 2.4 X 10⁶ impacts.
Thermal-mechanical fatigue of oxide scales in cyclic water vapor oxidation of 9-12 % Cr steels
(2017)
Ferritic-martensitic steels with 9-12 % Cr-content are widely used as high temperature construction materials in power plant due to their high temperature properties such as creep resistance, strength, and favorable oxidation resistances. However, typical operating conditions include cyclic thermal/mechanical loading, and as a result the oxide scale might fail; cracks are formed and the oxide scale is spalled off. The oxide spalls can cause steam tube blocking and local thermal stresses, which might provoke shorter component service life.
This work investigates the scale spallation behavior of ferritic-martensitic steels under cyclic load condition between 320°C and 620°C for up to 210 cycles in pure steam. All samples were isothermally pre-oxidized at 620°C for 500 h in water steam with 30 bar pressure to create an initial magnetite layer with low porosity. Different sample shapes, rectangular coupons, full rings and U-shape segments, are investigated to evaluate the impact of the geometry on these conditions. After oxidation experiments the oxidation kinetics in terms of mass change, metal loss and thickness scale is determined. In addition, the integrity of the oxide layer as well as its adherence to the matrix are characterized by modified hardness tests and scratch tests. Breakage of the layers at lower applied forces indicates a substantial loss of adhesion strength at intermediate cycle numbers.
Thin Sol-Gel Alumina Coating as Protection of a 9% Cr Steel Against Flue Gas Corrosion at 650 °C
(2018)
Samples of sol-gel alumina coated and uncoated P92 steel were exposed to flue gas at 650 °C for 300 h. As result of this treatment a 50 µm thick bi-layered oxide scale had formed on the surface of the uncoated sample. Below the scale a 40 µm thick inner oxidation zone was detected. In contrast, the porous, micron thick alumina coating enabled the formation of a chromium oxide scale with a thickness of some nanometers at the interface between steel substrate and coating. In this case high temperature corrosion of the steel was prevented so far.