Thin poly(acrylic acid) PAA films were deposited by pulsed plasma polymerization on different organic and inorganic substrates. The structureproperty relationships of the deposited acrylic acid polymers were studied in dependence on the monomer pressure by various techniques and probes. The surface and bulk properties of the plasma deposited films were investigated by X-ray photoelectron spectroscopy, attenuated total reflection infrared, and broad band dielectric spectroscopy. The experimental infrared frequencies of PAA films are compared with those predicted from quantum mechanical calculation. The concentration of the COOH groups in the film (stored in ambient air) decreased by about 15 % compared to the as-prepared sample. The plasma deposited PAA probably form a highly branched product. However, the dielectric measurements show that in addition to the hydrogen bonds, self condensation process was able to hinder the localized fluctuation as well. These processes lead to form a cross-linked network polymer film. Nevertheless, a low energy is sufficient to break these processes during heating at atmospheric pressure. Therefore, homogenized samples with free branches (functional group) were obtained after a first heating with structures close to conventional polymerized acrylic acid. Thus, a thermally stable product was obtained.
A novel mixed matrix composite has been prepared using solution-casting method at different volume concentrations of polyvinyl alcohol; PVA (50, 67, 75 and 80 %) and fixed amount of Dimethoxydimethylsilane in air atmosphere. The hydrolyzed dimethyldisilanol acts as in-situ cross linker through a wet-out condensation between the hydroxyl moieties of SiOH and PVAOH. Such process improves the mechanical properties of composite membranes as compared to pristine PVA which has been determined as function of varied membrane components to evaluate the structure/property relationships.
Furthermore, DFT (B3LYP)/6-31G(d) geometry and frequency computations were carried out for the suggested dimeric PVA structures via 1,3-diol linkage followed by condensation and hydrogen bonding interaction. Vibrational interpretations of composite membranes were proposed based on the computed wavenumbers, Cartesian coordinates displacements for the suggested hydrolyzed products involving the dominant PVA/SiOH/SiOC/SiOSi functional groups compared with those given in literatures. FTIR and EDX provide clear evidences for incorporating silicon to 3D network. Meanwhile, the infrared de-convoluted spectral interpretations ensure 17-30% cross-linked SiOC within the network of Composite membranes.