A combined XPS, NEXAFS, and ToF-SIMS chemical surface characterization of carbohydrate-functionalized gold and glass surfaces is presented. Spot shape and chemical composition across a spot surface are provided by surface-sensitive methods as ToF-SIMS and XPS, used in their imaging modes. Moreover, the feasibility of this multimethod approach to control relevant production steps of a carbohydrate microarray prototype is demonstrated.
Carbohydrate films on gold based on dimannoside thiols (DMT) were prepared, and a complementary surface chemical analysis was performed in detail by X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), near-edge X-ray absorption fine structure (NEXAFS), FT-IR, and contact angle measurements in order to verify formation of ω-carbohydrate-functionalized alkylthiol films. XPS (C 1s, O 1s, and S 2p) reveals information on carbohydrate specific alkoxy (C–O) and acetal moieties (O–C–O) as well as thiolate species attached to gold. Angle-resolved synchrotron XPS was used for chemical speciation at ultimate surface sensitivity. Angle-resolved XPS analysis suggests the presence of an excess top layer composed of unbound sulfur components combined with alkyl moieties. Further support for DMT attachment on Au is given by ToF-SIMS and FT-IR analysis. Carbon and oxygen K-edge NEXAFS spectra were interpreted by applying the building block model supported by comparison to data of 1-undecanethiol, poly(vinyl alcohol), and polyoxymethylene. No linear dichroism effect was observed in the angle-resolved C K-edge NEXAFS.
We investigated the ageing of amine-terminated
self-assembled monolayers (amine-SAMs) on different silica
substrates due to exposure to different ambient gases,
pressures, and/or temperatures using time-of-flight secondary
ion mass spectrometry (ToF-SIMS) with principal component
analysis and complementary methods of surface
analysis as X-ray photoelectron spectroscopy (XPS) and
near edge X-ray absorption fine structure (NEXAFS). The
goal of this study is to examine the durability of primary
amine groups of amine-SAMs stored in a user laboratory
prior to being used as supports for biomolecule immobilization
and other applications. We prepared amine-SAMs on
the native oxides of silicon wafers and glass slides using 3-
aminopropyl triethoxysilane, by using optimized conditions
such as anhydrous organic solvent and reaction time scale of
hours to avoid multilayer growth. Selected commercial
amine-SAM slides have been investigated, too. When the
amine-SAMs are exposed to air, oxygen incorporation
occurs, followed by formation of amide groups. The formation
of oxygen species due to ageing was proved by ToFSIMS,
XPS, and NEXAFS findings such as CNO- secondary
ion emission at m/z 42, observation of the N 1s HNC=O
component peak at 400.2400.3 eV in XPS, and, last but not
least, by formation of a π*(HNC=O) resonance at 401 eV in
the N K-edge X-ray absorption spectrum. It is concluded
that the used multi-method approach comprising complementary
ToF-SIMS, XPS, and NEXAFS analyses is well
suited for a thorough study of chemical aspects of ageing
phenomena of amine-SAM surfaces.