Filtern
Erscheinungsjahr
Dokumenttyp
Referierte Publikation
- ja (22) (entfernen)
Schlagworte
- Corrosion (5)
- Korrosion (4)
- Atmospheric corrosion (3)
- Nichtrostende Stähle (3)
- Stainless steel (3)
- Chromate (2)
- Concrete (2)
- Korrosionsschutz (2)
- Reinforcing steel (2)
- Werkstoffauswahl (2)
- Aluminium (1)
- Atmosphäre (1)
- Atmosphärische Korrosion (1)
- Auslagerungsversuche (1)
- Bauwesen (1)
- Betonstahl (1)
- Boden (1)
- Cathodic protection (1)
- Cement (1)
- Chlorid-induced corrosion (1)
- Chloride (1)
- Corrosion protection (1)
- Corrosion testing (1)
- Dauerhaftigkeit (1)
- Duplex stainless steels (1)
- Duplex-Stähle (1)
- EPR test (1)
- Electrochemical measurements (1)
- Electrochemical tests (1)
- Elektrochemische Versuche (1)
- Exposition (1)
- Exposure tests (1)
- Failure (1)
- Feuerverzinkt (1)
- Free weathering (1)
- Gabionen (1)
- Galvanized rebar (1)
- Galvanized steel (1)
- Grease (1)
- Grinding (1)
- Hydrogen evolution (1)
- Indoor swimming pools (1)
- Intercrystalline corrosion (1)
- Interkristalline Korrosion (1)
- KorroPad (1)
- Lochkorrosionspotential (1)
- Marine atmosphere (1)
- Maritime Atmosphäre (1)
- Maritime atmosphere (1)
- Nichtrostender Stahl (1)
- Passive layer (1)
- Pitting corrosion (1)
- Polarization (1)
- Potential mapping (1)
- Potentialfeldmessung (1)
- Prestressed systems (1)
- Pull-out tests (1)
- Rebar (1)
- Reinforcement (1)
- Salinization (1)
- Schäden (1)
- Spaltkorrosionspotential (1)
- Spannstahl (1)
- Sprayed zinc layer (1)
- Stahlbeton (1)
- Stainless steels (1)
- Surface finish (1)
- Surface protection system (1)
- Verbund (1)
- Versalzung (1)
- Verzinkt (1)
- Wax (1)
- Zinc (1)
- Zink-Aluminium-Überzug (1)
Organisationseinheit der BAM
Chloride-induced damage of reinforcing steel is especially for parking garages and bridges often very severe as large amounts of chlorides act on horizontal surfaces which could lead to fast ingress of these detrimental ions up to the level of the reinforcement and subsequently to high rates of corrosion.
In order to avoid the disadvantages of conventional rehabilitation (unreliable prognosis with patch repair or high costs and regular maintenance with cathodic protection using impressed current) a new combined protection system was developed where the principle of drying out the concrete (by means of a surface protection system) is combined with a temporary cathodic protection (by means of a sprayed zinc layer) during the transitional period of the drying out process.
This new system was tested both in the laboratory and on-site at a pilot application. Based on the results obtained the possibilities and limitations of the new system are discussed in this paper.
An einem Tankbehälter aus dem Werkstoff X2CrNiMo17-12-2, der zur Zwischenlagerung von Salzlake für die Käseherstellung dient, wurden trotz langjähriger positiver Erfahrungen an vergleichbaren Anlagen bereits kurze Zeit nach der Inbetriebnahme Lochkorrosionserscheinungen festgestellt. Durch entsprechende elektrochemische Laboruntersuchungen konnte gezeigt werden, dass die vorgefundene Lochkorrosion durch den Einsatz eines Oxidationsmittels zu Desinfektionszwecken verursacht wurde.
Translated Abstract
Corrosion damage at storage tanks for salt brine
A tank made of stainless steel type X2CrNiMo17-12-2 for intermediate storage of salt brine for cheese production revealed significant pitting corrosion effects shortly after commissioning although comparable units have shown positive long-term behaviour. By means of electrochemical laboratory tests it could be demonstrated that the observed pitting corrosion was caused by the use of an oxidizing agent for desinfection purposes.