Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (38)
- Beitrag zu einem Tagungsband (18)
- Beitrag zu einem Sammelband (17)
- Forschungsbericht (8)
- Vortrag (4)
- Handbuch (3)
- Sonstiges (3)
Sprache
- Deutsch (44)
- Englisch (42)
- Mehrsprachig (5)
Schlagworte
- Korrosion (21)
- Corrosion (15)
- Concrete (8)
- Stahlbeton (7)
- Kathodischer Korrosionsschutz (5)
- Nichtrostender Stahl (5)
- Spannstahl (5)
- Alkali-activated materials (4)
- Atmospheric corrosion (4)
- Betonstahl (4)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
Prestressing steels can be exposed in prestressed concrete structures in construction stage (ungrouted duct) to environmental conditions causing formation and growth of hydrogen induced cracks with brittle fracture of the steel. The risk of this hydrogen induced stress corrosion cracking can be minimized by appropriate treatment, but there is a requirement for construction to approve only prestressing steel having no enhanced susceptibility to stress corrosion cracking. The paper describes the historical development of the different test methods proposed in the past and gives an overview on the general requirements for a suitable test method to assess the hydrogen-induced stress corrosion susceptibility of prestressing steels.
Since 1982, based on investigations on construction sites and transfer of the results into laboratory tests, a test method is available enabling realistic estimation of suitable application possibilities of prestressing steels. This so called DIBt-test is approved to distinguish between prestressing steels susceptible to hydrogen induced stress corrosion cracking and those suitable and therefore approvable steels at practical environmental conditions. Furthermore the test enables estimation of corrosion risk for newly developed prestressing steels with higher strength.
Translated Abstract
Beurteilung der Prüfverfahren zur Untersuchung der Spannungsrisskorrosionsempfindlichkeit von Spannstählen
Spannstähle können in Spannbetonbauwerken im Bauzustand (unverpresstes Hüllrohr) Umgebungsbedingungen ausgesetzt sein, die zur Bildung und Ausbreitung wasserstoffinduzierter Risse mit Sprödbruch des Stahles führen können. Das Risiko dieser wasserstoffinduzierten Spannungsrisskorrosion kann einerseits durch eine sachgemäße Verarbeitung der Spannstähle minimiert werden, andererseits besteht die Notwendigkeit nur solche Spannstähle für die Baupraxis zuzulassen, die unter baupraktischen Bedingungen keine erhöhte Empfindlichkeit für Spannungsrisskorrosion besitzen. Die vorliegende Arbeit beschreibt die historische Entwicklung der verschiedenen vorgeschlagenen Prüfverfahren und gibt einen Überblick über die allgemeinen Anforderungen an ein geeignetes Verfahren zur Beurteilung der wasserstoffinduzierten Spannungsrisskorrosionsempfindlichkeit von Spannstählen.
Seit 1982 steht, begründet durch Untersuchungen auf Baustellen und Umsetzung der Ergebnisse in Laborversuchen, ein Prüfverfahren zur Verfügung, das eine wesentlich realistischere Einschätzung der Einsatzmöglichkeiten von Spannstählen zulässt. Dieser sog. DIBt-Test hat sich bewährt, um unter praktischen Umgebungsbedingungen gegen H-induzierte Spannungsrisskorrosion empfindliche Spannstähle von geeigneten und damit zulassungswürdigen Stählen zu unterscheiden. Des weiteren erlaubt die Prüfung ebenfalls eine Abschätzung des Korrosionsrisikos für neuentwickelte, höherfeste Spannstähle.
Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes.
Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt.
Case studies
(2013)
In this paper, some quite different survey tasks are described, and it can be seen that corrosion surveys will follow a certain scheme of data acquisition (first NDT measurements, than detailed testing on suspect areas), but the individual scope of on-site measurements may have a vast variety according to the local circumstances, and the interpretation always has to refer to a wider set of information than the data readings only.
In indoor swimming pools stainless steels are used not only due to structural and economic reasons but also due to aesthetic considerations. And therefore not only safety relevant load bearing components have to fulfil their tasks but also the visual appearance should be free of any staining. In a lot of cases basic requirements (e.g. design criteria, material selection and maintenance) being essential parts of technical regulations were not taken into account. Typical case studies with explanation of the cause of the corrosion problems and possibilities to prevent them are shown in the present paper.
Chloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setup was observed, while preferential corrosion did not occur for the Portland cement mortar. Scanning electron microscopy and auxiliary experiments in synthetic solutions indicated that this behavior was caused by inhomogeneities at the steel–mortar interface in the alkali‐activated mortar, likely due to its peculiar rheological properties in the fresh state.
Corrosion behavior of galvanized reinforcement in chloride containing mortar and carbonated mortar
(2018)
Korrosionseigenschaften von feuerverzinktem Betonstahl unterscheiden sich grundlegend von herkömmlichen Betonstahl. In diesem Vortrag sind Beispiele für das Korrosionsverhalten in chloridhaltigen und carbonatisierten Mörteln dargestellt
Alkali-activated materials such as geopolymers are currently receiving a lot of attention because of their potential to be used as binders for concrete with advantageous engineering properties and reduced manufacturing CO2 emissions. Knowledge of the durability of steel in these concretes and related properties of alkali-activated materials is a prerequisite for their application as building materials, if they are to be used for steel reinforced elements. However, to date only limited data exists on this topic. The present contribution focuses on durability-related transport properties of geopolymer-based mortars (as model systems for concrete). We report results of accelerated carbonation, rapid chloride migration (RCM) and air permeability measurements as well as porosity data for fly ash-based geopolymer mortars, including mixes containing ground granulated blast furnace slag (GGBFS). In addition, we report polarization resistance data and corrosion potential vs. time curves for carbon steel bars embedded in two of the fly ash-based geopolymer mortars and a CEM I-based mortar (as reference).
Despite comparable total porosities, the carbonation depths, the chloride migration coefficients and the air permeabilities of the mortars differed significantly. In general, the addition of GGBFS to the binders improved the performance (decreased transport coefficients); however, this was not found to be true for the air permeability in all cases. This latter effect can be explained by drying damage of the C-(A-)S-H gel in GGBFS-containing binders. On the other hand, low transport coefficients can also be achieved by optimization of the binder formulation without the addition of GGBFS, which is also reflected in the material’s air permeability. Thus, there exists no simple correlation between air permeability (of harshly dried mortars) and durability-related transport coefficients for the studied alkali-activated materials.
The corrosion potential vs. time curves in combination with polarization resistance values reveal that the steel reinforcement in geopolymer mortars assumed a passive state. However, this happened considerably later than for steel in CEM I-based mortars. The free corrosion potential of carbon steel reinforcement in the geopolymer mortars had different values than the free corrosion potential values for the CEM I-based mortar for both the active and the passive state; possible reasons for this behavior are discussed.
In addition to constructional requirements in civil engineering stainless steels often have to fulfil high visual demands. Unexpected impairments of the visual appearance of stainless steels under low corrosive conditions are a widespread problem today. Frequently it is supposed that this is caused by changes in the alloy composition, worse environmental conditions or improper handling. Within a research project the systematic investigation of several cases of damaged stainless steel bars has shown that the reasons are based on well-known material defects like chemical inhomogeneities (e.g. precipitations or local carburization) or geometrical defects (e.g. undercuts, rolling defects or shell formation). Thus, the failures could be clearly identified as production failures of the respective semi-finished products.
Während das Instandsetzungsprinzip W bei carbonatisierungsinduzierter Korrosion seit vielen Jahren als Standardverfahren etabliert ist, wird seine Anwendbarkeit bei chloridinduzierter Korrosion (W-Cl) in der Fachwelt bis heute kontrovers diskutiert. Zwar ergeben sich aus seiner Anwendung gegenüber anderen Instandsetzungsverfahren auf den ersten Blick u. U. deutliche wirtschaftliche Vorteile, allerdings besteht bei diesem Verfahren ein deutlich höheres Risiko, dass das Instandsetzungsziel nicht erreicht wird.
Im vorliegenden Beitrag werden die technischen Grundlagen des Instandsetzungsprinzips W-Cl sowie der aktuelle Kenntnisstand - sowohl für den gerissenen als auch für den ungerissenen Beton - dargestellt und baurechtliche Konsequenzen, die sich aus dem erhöhten Ausführungsrisiko ergeben, diskutiert.
Korrosionsmonitoring als Element zum Nachweis des Instandsetzungserfolgs bei Anwendung des Prinzips W-Cl wird vorgestellt.
Anhand von Anwendungsbeispielen werden sowohl die Risiken, die mit dem Verfahren verbunden sind, als auch das Potenzial bei erfolgreicher Anwendung veranschaulicht.
Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Nondestructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from, e.g., stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. Therefore, in a training concept firstly the theoretical basics of the test method should be imparted. Then, frequently occurring practical situations of various influencing factors will be made accessible to the participants by a model object specially designed for this purpose. The aim is to impart profound knowledge concerning the characteristics of potential mapping for detecting corrosion of reinforcing steel in order to apply this technique in practice as reliable and economical test method.
Chloride-induced damage of reinforcing steel is especially for parking garages and bridges often very severe as large amounts of chlorides act on horizontal surfaces which could lead to fast ingress of these detrimental ions up to the level of the reinforcement and subsequently to high rates of corrosion.
In order to avoid the disadvantages of conventional rehabilitation (unreliable prognosis with patch repair or high costs and regular maintenance with cathodic protection using impressed current) a new combined protection system was developed where the principle of drying out the concrete (by means of a surface protection system) is combined with a temporary cathodic protection (by means of a sprayed zinc layer) during the transitional period of the drying out process.
This new system was tested both in the laboratory and on-site at a pilot application. Based on the results obtained the possibilities and limitations of the new system are discussed in this paper.