Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Sammelband (17)
- Beitrag zu einem Tagungsband (14)
- Forschungsbericht (8)
- Zeitschriftenartikel (4)
- Vortrag (4)
- Handbuch (3)
- Sonstiges (3)
Sprache
- Deutsch (31)
- Englisch (21)
- Mehrsprachig (1)
Referierte Publikation
- nein (53) (entfernen)
Schlagworte
- Korrosion (14)
- Corrosion (6)
- Stahlbeton (6)
- Kathodischer Korrosionsschutz (5)
- Spannstahl (4)
- Betonstahl (3)
- Chlorinduzierte Korrosion (3)
- Concrete (3)
- Monitoring (3)
- Oberflächenschutzsystem (3)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes.
Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt.
Corrosion behavior of galvanized reinforcement in chloride containing mortar and carbonated mortar
(2018)
Korrosionseigenschaften von feuerverzinktem Betonstahl unterscheiden sich grundlegend von herkömmlichen Betonstahl. In diesem Vortrag sind Beispiele für das Korrosionsverhalten in chloridhaltigen und carbonatisierten Mörteln dargestellt
Alkali-activated materials such as geopolymers are currently receiving a lot of attention because of their potential to be used as binders for concrete with advantageous engineering properties and reduced manufacturing CO2 emissions. Knowledge of the durability of steel in these concretes and related properties of alkali-activated materials is a prerequisite for their application as building materials, if they are to be used for steel reinforced elements. However, to date only limited data exists on this topic. The present contribution focuses on durability-related transport properties of geopolymer-based mortars (as model systems for concrete). We report results of accelerated carbonation, rapid chloride migration (RCM) and air permeability measurements as well as porosity data for fly ash-based geopolymer mortars, including mixes containing ground granulated blast furnace slag (GGBFS). In addition, we report polarization resistance data and corrosion potential vs. time curves for carbon steel bars embedded in two of the fly ash-based geopolymer mortars and a CEM I-based mortar (as reference).
Despite comparable total porosities, the carbonation depths, the chloride migration coefficients and the air permeabilities of the mortars differed significantly. In general, the addition of GGBFS to the binders improved the performance (decreased transport coefficients); however, this was not found to be true for the air permeability in all cases. This latter effect can be explained by drying damage of the C-(A-)S-H gel in GGBFS-containing binders. On the other hand, low transport coefficients can also be achieved by optimization of the binder formulation without the addition of GGBFS, which is also reflected in the material’s air permeability. Thus, there exists no simple correlation between air permeability (of harshly dried mortars) and durability-related transport coefficients for the studied alkali-activated materials.
The corrosion potential vs. time curves in combination with polarization resistance values reveal that the steel reinforcement in geopolymer mortars assumed a passive state. However, this happened considerably later than for steel in CEM I-based mortars. The free corrosion potential of carbon steel reinforcement in the geopolymer mortars had different values than the free corrosion potential values for the CEM I-based mortar for both the active and the passive state; possible reasons for this behavior are discussed.
Electrochemical half-cell potential measurements for the detection of reinforcement corrosion
(2014)
This specification describes the application of electrochemical half‐cell potential measurements (frequently also called potential mapping) for the detection of reinforcement corrosion in reinforced concrete structures. Areas of corroding reinforcement steel can be located in a nondestructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose the determination of the carbonation depth and the concrete cover appear to be more appropriate.
The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.
Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization.
Die Zielsetzung dieses Projektes war es, ein kombiniertes Schutzsystem aus Spritzverzinkung und abdichtendem Oberflächenschutzsystem für die Instandsetzung chloridbelasteter und korrosionsgeschädigter Stahlbetonbauteile zu entwickeln. Dabei soll die Spritzverzinkung der Betonoberfläche in den ersten Jahren nach der Instandsetzung einen kathodischen Korrosionsschutz der Bewehrung bewirken, bis der Beton infolge des Oberflächenschutzsystems soweit ausgetrocknet ist, dass auch ohne kathodischen Schutz praktisch keine Korrosion der Bewehrung mehr stattfinden kann.
Anhand von Untersuchungen zur Haftung zwischen Beton, Zinkschicht und verschiedenen Oberflächenschutzsystemen wurde der Aufbau des kombinierten Schutzsystems entwickelt. Es wurden verschiedene OS-11a-Systeme ein OS-13-System sowie zwei Systeme nach ZTV-ING, Teil 7 vor und nach künstlicher Bewitterung untersucht. Anhand der Ergebnisse wurde für das kombinierte System ein OS-11a-System ausgewählt und im weiteren hinsichtlich der Wirksamkeit des kathodischen Schutzes sowie hinsichtlich der Austrocknung des Betons untersucht.
Es zeigte sich sowohl an ausgelagerten Prüfköpfen sowie auf einer angelegten Versuchsfläche auf Freideck eines Parkhauses, dass ein wirksamer galvanischer kathodischer Korrosionsschutz der Bewehrung nur bei sehr hohen Chloridgehalten (4 M.-% bezogen auf den Zementgehalt) erreicht werden kann. Bei geringeren untersuchten Chloridgehalten kam es vermutlich infolge der Austrocknung der Zink/Beton-Kontaktzone nach relativ kurzer Zeit zu einer Inaktivierung des Zinks. Bei Chloridgehalten von 4 M.-% bildeten sich zwischen der Zinkschicht und dem ausgewählten OS-System gasgefüllte Blasen. Diese Problematik, sowie die Tatsache dass die Wirksamkeit des Prinzips W (Austrocknung des Betons) bei derart hohen Chloridgehalten bezweifelt werden muss, grenzt die Anwendbarkeit des Kombinationssystems mit der Zinkschicht als Opferanode deutlich ein.
An neun Jahre alten, ausgelagerten Prüfköpfen durchgeführte Untersuchungen zeigten jedoch, dass mittels Fremdstrombeaufschlagung zwischen Zinkschicht und Bewehrung ein wirksamer kathodischer Schutz auch bei geringeren Chloridgehalten erreicht werden kann. Der Einsatz des entwickelten Kombinationssystems mit Fremdstrombeaufschlagung erscheint somit durchaus durchführbar. Dabei sollte der Fremdstrom jedoch vorsichtig dosiert werden, um den Haftverbund zum Zink nicht zu sehr zu schwächen.
Das Ziel des Vorhabens wurde somit erreicht.