Filtern
Erscheinungsjahr
- 2014 (9) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (3)
- Sonstiges (2)
- Zeitschriftenartikel (1)
- Beitrag zu einem Sammelband (1)
- Handbuch (1)
- Vortrag (1)
Schlagworte
- Corrosion (2)
- Korrosion (2)
- Atmospheric corrosion (1)
- Betonstahl (1)
- Bewehrung (1)
- Cathodic protection (1)
- Chloride (1)
- Chloridinduzierte Korrosion (1)
- Concrete (1)
- Duplex stainless steels (1)
Eingeladener Vortrag
- nein (1)
Electrochemical half-cell potential measurements for the detection of reinforcement corrosion
(2014)
This specification describes the application of electrochemical half‐cell potential measurements (frequently also called potential mapping) for the detection of reinforcement corrosion in reinforced concrete structures. Areas of corroding reinforcement steel can be located in a nondestructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose the determination of the carbonation depth and the concrete cover appear to be more appropriate.
The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.
Dieses Merkblatt beschreibt die Anwendung elektrochemischer Potentialmessungen (häufig auch als Potentialfeldmessung bezeichnet) zur Detektion von Bewehrungsstahlkorrosion an Stahlbetonbauwerken. Mit Hilfe dieses Verfahrens können Bereiche korrodierender Bewehrung zerstörungsfrei lokalisiert werden. In der Regel kommt diese Messmethode bei der Detektion chloridinduzierter Korrosion zum Einsatz. In Abgrenzung hierzu sollte die Abschätzung der Gefahr einer karbonatisierungsinduzierten Korrosion durch Bestimmung der Karbonatisierungstiefe und der Betondeckung erfolgen.
Im Zusammenhang mit Planungs- und Entwicklungsaufgaben, den Forderungen in Normen und Regelwerken, in betrieblichen Arbeitsanweisungen, den Vorgaben für Zulieferteile oder bei der Auseinandersetzung mit Schadensfällen stellen sich häufig Fragen zum Korrosionsschutz sowie zu entsprechenden Prüf- und Untersuchungsverfahren. Die daraus gewonnenen Ergebnisse sollen z. B. eine Eignung von Werkstoffen oder Schutzsystemen unter spezifischen Einsatzbedingungen, die Dauerhaftigkeit des Schutzes, den Nachweis einer gleichbleibenden Qualität, die Vergleichbarkeit bekannter mit neuen Korrosionsschutzkonzepten oder den Wirkungsnachweis für gezielte Systemeingriffe belegen. Schnell wird deutlich, dass sich aus dem Blickwinkel verschiedener Branchen ganz unterschiedliche Anforderungsprofile ergeben, die ihren Niederschlag dann in unterschiedlichen Strategien der Prüf- und Untersuchungsverfahren finden.
Systematic laboratory and field exposure tests allow to compare nine different stainless steels (three ferritic, three austenitic, and three duplex grades) for civil engineering applications. The influence of surface finish was also taken into account by choosing five different industry-specific features. The three duplex stainless steels revealed excellent corrosion resistance under most of the test conditions. Especially for applications in civil engineering the lean duplex steels offer distinct advantages. The manganese-alloyed 1.4376 and the ferritic steel 1.4509 cannot be recommended as alternative materials as they did not perform satisfactorily.
Steel in concrete is protected by the alkaline pore water environment and the resulting formation of a protective passive layer against corrosion. Adverse environmental conditions due to carbonation or chloride ingress can destroy the passive layer on the steel surface. Corrosion processes starting in those areas lead to uniform corrosion or local corrosion like pitting corrosion. In comparison to uniform corrosion pitting corrosion is a form of increased local corrosion and thus leads to a progressive reduction in cross-section of the reinforcing steel. The corrosion products are first absorbed by the pores of the concrete matrix, without causing visible external changes at the concrete surface.
Carbon‐based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. The dissolved organic and inorganic carbons in electrolyte solution were quantified by using a photometric method. The structures of the coatings were investigated before and after the electrochemical tests by microscopy and scanning electron microscope/EDX analysis. The results of the electrochemical impedance measurements show that the tested coatings all have a relatively low resistance, which is between 100 and 200V. The binder and the surface porosity influence the degradation behavior of those coatings. Especially the organic binder reacts with the strong alkaline medium under dissolving of organic carbon.