Investigations on hydrogen-induced embrittlement of quenched and tempered prestressing steels
(2000)
In Germany in recent years failures of more than 30-year-old prestressed concrete structures have been observed. In all these cases a quenched and tempered steel type, strength class St. 1420/1570 was used. In order to assess the corrosion risk, i.e. crack initiation and propagation, under depassivating conditions lifetime tests in environments relevant for building practice were carried out using different prestressing steels of this quenched and tempered type of material.
From the results it can be concluded that the specific susceptibility of certain prestressing steels is the determining factor with respect to the occurrence of cracks rather than environmental factors.
Translated Abstract
Untersuchungen zum wasserstoffinduzierten Sprödbruch vergüteter Spannstähle
In den letzten Jahren ist es verschiedentlich zu Schadensfällen von Spannbetonbauteilen gekommen, bei denen vergüteter Spannstahl der Festigkeitsklasse St 1420/1570 eingesetzt war. Durch systematische Untersuchungen an verschiedenen Typen dieser Stahlsorte sollte geklärt werden, ob unter depassivierenden Bedingungen Rißeinleitung und -ausbreitung unter praxisnahen Verhältnissen zu erwarten ist.
Die durchgeführten Untersuchungen lassen folgern, daß die spezifische Anfälligkeit des Spannstahls für das Auftreten von Rissen einen wesentlich höheren Einfluß besitzt als die elektrolytseitigen Parameter, da sich die verschiedenen Stähle auch bei vergleichbaren Korrosionsangriffen unterschiedlich verhalten.