Case studies
(2013)
In this paper, some quite different survey tasks are described, and it can be seen that corrosion surveys will follow a certain scheme of data acquisition (first NDT measurements, than detailed testing on suspect areas), but the individual scope of on-site measurements may have a vast variety according to the local circumstances, and the interpretation always has to refer to a wider set of information than the data readings only.
Corrosion behavior of galvanized reinforcement in chloride containing mortar and carbonated mortar
(2018)
Korrosionseigenschaften von feuerverzinktem Betonstahl unterscheiden sich grundlegend von herkömmlichen Betonstahl. In diesem Vortrag sind Beispiele für das Korrosionsverhalten in chloridhaltigen und carbonatisierten Mörteln dargestellt
Alkali-activated materials such as geopolymers are currently receiving a lot of attention because of their potential to be used as binders for concrete with advantageous engineering properties and reduced manufacturing CO2 emissions. Knowledge of the durability of steel in these concretes and related properties of alkali-activated materials is a prerequisite for their application as building materials, if they are to be used for steel reinforced elements. However, to date only limited data exists on this topic. The present contribution focuses on durability-related transport properties of geopolymer-based mortars (as model systems for concrete). We report results of accelerated carbonation, rapid chloride migration (RCM) and air permeability measurements as well as porosity data for fly ash-based geopolymer mortars, including mixes containing ground granulated blast furnace slag (GGBFS). In addition, we report polarization resistance data and corrosion potential vs. time curves for carbon steel bars embedded in two of the fly ash-based geopolymer mortars and a CEM I-based mortar (as reference).
Despite comparable total porosities, the carbonation depths, the chloride migration coefficients and the air permeabilities of the mortars differed significantly. In general, the addition of GGBFS to the binders improved the performance (decreased transport coefficients); however, this was not found to be true for the air permeability in all cases. This latter effect can be explained by drying damage of the C-(A-)S-H gel in GGBFS-containing binders. On the other hand, low transport coefficients can also be achieved by optimization of the binder formulation without the addition of GGBFS, which is also reflected in the material’s air permeability. Thus, there exists no simple correlation between air permeability (of harshly dried mortars) and durability-related transport coefficients for the studied alkali-activated materials.
The corrosion potential vs. time curves in combination with polarization resistance values reveal that the steel reinforcement in geopolymer mortars assumed a passive state. However, this happened considerably later than for steel in CEM I-based mortars. The free corrosion potential of carbon steel reinforcement in the geopolymer mortars had different values than the free corrosion potential values for the CEM I-based mortar for both the active and the passive state; possible reasons for this behavior are discussed.
Electrochemical potential mapping according to guideline B3 of DGZfP (German Society for Nondestructive Testing) is a recognized technique for the localization of corroding reinforcing steels. In reinforced concrete structures the measured potentials are not necessarily directly linked to the corrosion likelihood of the reinforcing steel. The measured values may be significantly affected, different from, e.g., stress measurement, by different influences on the potential formation at the phase boundary metal/concrete itself as well as the acquisition procedure. Due to the complexity of influencing factors there is a risk that the results are misinterpreted. Therefore, in a training concept firstly the theoretical basics of the test method should be imparted. Then, frequently occurring practical situations of various influencing factors will be made accessible to the participants by a model object specially designed for this purpose. The aim is to impart profound knowledge concerning the characteristics of potential mapping for detecting corrosion of reinforcing steel in order to apply this technique in practice as reliable and economical test method.
Electrochemical half-cell potential measurements for the detection of reinforcement corrosion
(2014)
This specification describes the application of electrochemical half‐cell potential measurements (frequently also called potential mapping) for the detection of reinforcement corrosion in reinforced concrete structures. Areas of corroding reinforcement steel can be located in a nondestructive manner by means of this procedure. Half‐cell potential measurements are used in order to detect chloride‐induced corrosion. However, it is not recommended in order to assess the risk of carbonation‐induced corrosion. For this purpose the determination of the carbonation depth and the concrete cover appear to be more appropriate.
The content of this specification exclusively refers to the application of mobile, local variable reference electrodes, which are only placed on the concrete surface while measuring. The technique distinguishes itself thereby from the range of corrosion monitoring systems with stationary installed reference electrodes and sensor systems, respectively, whereby it is possible to continuously track measurements within the area of the installed electrodes. However, these methods are not dealt with in this specification.
Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization.
Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. The dissolved organic and inorganic carbons in electrolyte solution were quantified by using a photometric method. The structures of the coatings were investigated before and after the electrochemical tests by microscopy and scanning electron microscope/EDX analysis. The results of the electrochemical impedance measurements show that the tested coatings all have a relatively low resistance, which is between 100 and 200 Ω. The binder and the surface porosity influence the degradation behavior of those coatings. Especially the organic binder reacts with the strong alkaline medium under dissolving of organic carbon.
Steel in concrete is protected by the alkaline pore water environment and the resulting formation of a protective passive layer against corrosion. Adverse environmental conditions due to carbonation or chloride ingress can destroy the passive layer on the steel surface. Corrosion processes starting in those areas lead to uniform corrosion or local corrosion like pitting corrosion. In comparison to uniform corrosion pitting corrosion is a form of increased local corrosion and thus leads to a progressive reduction in cross-section of the reinforcing steel. The corrosion products are first absorbed by the pores of the concrete matrix, without causing visible external changes at the concrete surface.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.
Investigations on hydrogen-induced embrittlement of quenched and tempered prestressing steels
(2000)
In Germany in recent years failures of more than 30-year-old prestressed concrete structures have been observed. In all these cases a quenched and tempered steel type, strength class St. 1420/1570 was used. In order to assess the corrosion risk, i.e. crack initiation and propagation, under depassivating conditions lifetime tests in environments relevant for building practice were carried out using different prestressing steels of this quenched and tempered type of material.
From the results it can be concluded that the specific susceptibility of certain prestressing steels is the determining factor with respect to the occurrence of cracks rather than environmental factors.
Translated Abstract
Untersuchungen zum wasserstoffinduzierten Sprödbruch vergüteter Spannstähle
In den letzten Jahren ist es verschiedentlich zu Schadensfällen von Spannbetonbauteilen gekommen, bei denen vergüteter Spannstahl der Festigkeitsklasse St 1420/1570 eingesetzt war. Durch systematische Untersuchungen an verschiedenen Typen dieser Stahlsorte sollte geklärt werden, ob unter depassivierenden Bedingungen Rißeinleitung und -ausbreitung unter praxisnahen Verhältnissen zu erwarten ist.
Die durchgeführten Untersuchungen lassen folgern, daß die spezifische Anfälligkeit des Spannstahls für das Auftreten von Rissen einen wesentlich höheren Einfluß besitzt als die elektrolytseitigen Parameter, da sich die verschiedenen Stähle auch bei vergleichbaren Korrosionsangriffen unterschiedlich verhalten.