The reduction of the chromate contents in cements affects the electrochemical reactions of galvanized reinforcing steels in fresh concrete. By means of electrochemical measurements and bar pull-out tests the effect of chromates on the formation of protective coatings at the zinc and the bond behaviour have been investigated using chromate-containing and chromate-reduced cements. The results have shown that the bond zone was affected as a result of chromate reduction for cement types CEM I and CEM II. The disturbance to the bond zone should be considered as long-term in relation to the pore structure which is formed. The effects on the bond are largely compensated for as the concrete ages. The results of the related bond strength with displacement paths of 0.1 and 0.5?mm, respectively, are still within the range of expected figures for non-galvanized reinforcing steel despite the structural disturbance. Under practical aspects it is not necessary that the existing structural disturbance with respect to bond strength is taken into consideration.
Case studies
(2013)
In this paper, some quite different survey tasks are described, and it can be seen that corrosion surveys will follow a certain scheme of data acquisition (first NDT measurements, than detailed testing on suspect areas), but the individual scope of on-site measurements may have a vast variety according to the local circumstances, and the interpretation always has to refer to a wider set of information than the data readings only.
Carbon‐based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. The dissolved organic and inorganic carbons in electrolyte solution were quantified by using a photometric method. The structures of the coatings were investigated before and after the electrochemical tests by microscopy and scanning electron microscope/EDX analysis. The results of the electrochemical impedance measurements show that the tested coatings all have a relatively low resistance, which is between 100 and 200V. The binder and the surface porosity influence the degradation behavior of those coatings. Especially the organic binder reacts with the strong alkaline medium under dissolving of organic carbon.
Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. The dissolved organic and inorganic carbons in electrolyte solution were quantified by using a photometric method. The structures of the coatings were investigated before and after the electrochemical tests by microscopy and scanning electron microscope/EDX analysis. The results of the electrochemical impedance measurements show that the tested coatings all have a relatively low resistance, which is between 100 and 200 Ω. The binder and the surface porosity influence the degradation behavior of those coatings. Especially the organic binder reacts with the strong alkaline medium under dissolving of organic carbon.