Industry faces a growing demand for high-strength structural steels with yield strengths of up to 1,300 MPa in order to cope with increasingly higher strength requirements in engineering. Higher strength levels are achieved by a special coordinated production process and an adapted chemical composition. Nevertheless, disastrous damage cases with high-strength steels have occurred in the past. The sensitivity to mechanical property degradation by hydrogen increases dramatically with strength. This phenomenon leads to hydrogen-assisted cold cracking. T-joints with fillet welds made from one side with an included angle of 60° were examined for their cold cracking behavior. Based on the T-joint, a modified heat input, even interpass temperature, plate thickness, and length ones were examined. The diffusion behavior and the effectiveness of different post-weld heat treatments in joints were simulated. The results of post-weld heat treatments are illustrated in practical hydrogen removal heat treatment diagrams. It is noticed that the T-joint is subject to a very high risk of hydrogen-assisted cold cracking (HACC). Contrary to other joints, its most critical area for cracking is not the weld metal but the heat-affected zone surrounding area of the root pass. The simulation shows that HACC in the T-joint can only be avoided by applying a sufficient post-weld heat treatment.
Quite a number of models for hydrogen distribution in steels and welds have been developed in the past 20 years. They reach from simple analytical models to more complex two and three dimensional finite element simulations. So far, these models have been used to simulate hydrogen distribution in homogeneous microstructure. This paper contributes to numerical simulation of hydrogen distribution in heterogeneous microstructure, e. g. in a duplex stainless steel microstructure consisting of two phase fractions. Under appropriate conditions, such as cathodic protection, it is possible that hydrogen is absorbed leading to material embrittlement and possibly initiating hydrogen assisted cracking. In order to avoid hydrogen assisted cracking in duplex stainless steels, it is of great interest to know more about the diffusion behavior of the ferrite and austenite phase. A numerical model has been developed that operates on the mesoscale and enables simulation of hydrogen transport in the various phases of a metallic material. As a first application of this model, hydrogen distribution in a duplex stainless steel 1.4462, consisting of approximately equal portions of ferrite and austenite, was simulated using the finite element program package ANSYS. The results reflect the dependency of hydrogen distribution on the microstructural alignment of the ferrite and austenite phase fractions. Crack-critical areas can thus be identified, provided the critical strain-hydrogen combination is known for the respective microstructural phase.
Schadensfälle in den letzten zehn Jahren mit teilweise katastrophalen Folgen belegen, dass der Vermeidung von Rissen beim Schweißen von Rohrleitungen besondere Aufmerksamkeit zu schenken ist. In der Analyse solcher Schäden ist zu unterscheiden, ob die Risse bereits während oder kurz nach der schweißtechnischen Fertigung der Rohrkomponenten oder während des anschließenden Betriebes entstanden sind. Im vorliegenden Beitrag wird sich vor allem auf die Vermeidung einer Heiß- und Kaltrissbildung beim Schweißen von Rohrleitungen konzentriert und es werden weitere Forschungsperspektiven abgeleitet.
Quite a number of numerical models for hydrogen-assisted cracking in different kind of steels are existing reaching from simple analytical models to more complex two- and three-dimensional finite element simulations. These numerical models have been used to simulate the processes of hydrogen-assisted cracking in homogeneous microstructure. This paper contributes to numerical simulation of hydrogen-assisted cracking in heterogeneous microstructure, e.g., in a duplex stainless steel microstructure consisting of two phase fractions. If hydrogen is absorbed during welding or during service, i.e., due to cathodic protection, hydrogen is leading to material embrittlement and leads to hydrogen-assisted cracking. In order to improve understanding of the mechanisms of hydrogen-assisted cracking in duplex stainless steels, a numerical model has been created that operates at the mesoscale and enables simulation of stress–strain distribution as well as cracking in the various phases of a metallic material. Stress–strain distribution and hydrogen-assisted cracking in the duplex stainless steel 1.4462, consisting of approximately equal portions of ferrite and austenite, was simulated using the finite element program ANSYS. It was shown by numerical simulation that higher local stresses and strains are present at ferrite and austenite than the global stresses and strains in the duplex stainless steel, while the highest plastic deformations occur at austenite and the highest stresses can be found in small ferrite bars surrounded by ductile austenitic islands. By analyzing the stress–strain distribution in the duplex microstructure, crack critical areas in the ferrite can be identified. Hydrogen-assisted cracking was modeled assuming high hydrogen concentrations and regarding the local mechanical load in each phase of the duplex stainless steel. The mesoscale model qualitatively reflects the crack initiation and propagation process in the ferritic and austenitic phase of the duplex stainless steel.
Welded components of P91 9% Cr steel demand for careful welding fabrication with necessary post weld heat treatment (PWHT). Before the PWHT, a hydrogen removal heat treatment is necessary for avoidance of hydrogen assisted cracking (HAC). In this context, the microstructure and temperature-dependent hydrogen diffusion is important, and reliable diffusion coefficients of P91 weld metal are rare. For that reason, the diffusion behavior of P91 multi-layer weld metal was investigated for as-welded (AW) and PWHT condition by electrochemical permeation experiments at room temperature and carrier gas hot extraction (CGHE) from 100 to 400 °C. Hydrogen diffusion coefficients were calculated, and the corresponding hydrogen
concentration was measured. It was ascertained that both heat treatment conditions show significant differences. At room
temperature the AW condition showed significant hydrogen trapping expressed by to seven times lower diffusion coefficients. A preferred diffusion direction was found in perpendicular direction expressed by high permeability. The CGHE experiments
revealed lower diffusion coefficients for the AW condition up to 400 °C. In this context, a hydrogen concentration of approximately 21 ml/100 g was still trapped at 100 °C. For that reason, a certain HAC susceptibility of as-welded P91 weld metal cannot
be excluded, and hydrogen removal should be done before PWHT.
Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in weld joints using a thermal conductivity detector (TCD) for hydrogen measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries (ISO 3690 type B and small cylindrical samples), and factors that additionally influence hydrogen determination. They are namely specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PI-furnace controller, as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up to the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by Evaluation of the recorded data. Generally, independent temperature measurement with dummy specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA).