Welded components of P91 9% Cr steel demand for careful welding fabrication with necessary post weld heat treatment (PWHT). Before the PWHT, a hydrogen removal heat treatment is necessary for avoidance of hydrogen assisted cracking (HAC). In this context, the microstructure and temperature-dependent hydrogen diffusion is important, and reliable diffusion coefficients of P91 weld metal are rare. For that reason, the diffusion behavior of P91 multi-layer weld metal was investigated for as-welded (AW) and PWHT condition by electrochemical permeation experiments at room temperature and carrier gas hot extraction (CGHE) from 100 to 400 °C. Hydrogen diffusion coefficients were calculated, and the corresponding hydrogen
concentration was measured. It was ascertained that both heat treatment conditions show significant differences. At room
temperature the AW condition showed significant hydrogen trapping expressed by to seven times lower diffusion coefficients. A preferred diffusion direction was found in perpendicular direction expressed by high permeability. The CGHE experiments
revealed lower diffusion coefficients for the AW condition up to 400 °C. In this context, a hydrogen concentration of approximately 21 ml/100 g was still trapped at 100 °C. For that reason, a certain HAC susceptibility of as-welded P91 weld metal cannot
be excluded, and hydrogen removal should be done before PWHT.
Supermartensitic stainless steels (SMSS) are a commonly used material nowadays for building offshore structures, i.e. pipelines in the oil and gas industry. The harsh and corrosive environments in oil and gas applications require the correct combination of alloys to attain the desired properties of steel, including high strength and good corrosion properties, even in severe sour service conditions. Welding is the most commonly used method in joining offshore components, depending on requirements requiring strength or fitting. It has been shown that the heat affected zone (HAZ) is more susceptible to certain types of corrosion, including pitting corrosion, especially during severe sour service where a high pH and lower H2S values in the flow medium can lead to pitting corrosion in the HAZ of welded structures. Subsequent hydrogen uptake in the pits can cause cracks to initiate and propagate, leading to rupture of pipelines or catastrophic failures of structures, even at low mechanical loads. Offshore standards allow a certain amount of corrosion, including pitting, to be present before action is required, however the extent of pitting corrosion is not identified by performing visual inspection alone as the subsurface pit diameter may be vastly greater than the pit diameter at the surface. The critical conditions which lead to crack initiation and propagation from a pit with hydrogen uptake are currently not known. Therefore, pitting corrosion and subsequent crack initiation are a danger to the safety of structures. The interest in this phenomenon has resulted in many experimental studies and numerical simulations.
Several numerical models of pitting corrosion and hydrogen uptake resulting in crack initiation are already in existence, but these two phenomena are regularly modelled individually. Thus, a model enabling simulation of both phenomena simultaneously would be of great benefit. Hence, the goal of this study is to develop a model enabling simulation of pit growth and crack initiation, considering hydrogen uptake in the pit from a corrosive environment.
As a first step, this paper presents an investigation into various parameters, which influence crack initiation at pits. These crack critical parameters include: pit geometry, pit location, mechanical load and hydrogen transport into the microstructure. The results will help to identify critical conditions for crack initiation starting at the pit and developing measures to avoid hydrogen assisted cracking (HAC).
Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in weld joints using a thermal conductivity detector (TCD) for hydrogen measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries (ISO 3690 type B and small cylindrical samples), and factors that additionally influence hydrogen determination. They are namely specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PI-furnace controller, as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up to the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by Evaluation of the recorded data. Generally, independent temperature measurement with dummy specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA).
A two-dimensional numerical mesoscale model has been created representing a microstructure of a typical 2205/1.4462 duplex stainless steel to further elucidate the mechanisms of hydrogen-assisted crack initiation and propagation in multiphase non-hydride forming metallic microstructures. Hydrogen-assisted cracking (HAC) was simulated by considering different stress and strain behavior as well as different diffusion behavior in both phases. For simulation of crack initiation and propagation, the element elimination technique has been applied. The model allows the simulation of path-free crack propagation which contributes to a better understanding of the HAC process in two-phase microstructures. As a particular result, the analyses revealed that a global macroscopic elastic deformation might already cause plastic deformation in both phases entailing respective HAC.
Literature provides a wide range of hydrogen diffusion coefficients for low alloyed steels used in power plants. In fact, experimental boundary conditions and calculation methods have influence on the determination of these coefficients. The diffusion and trapping behavior in creep-resistant steel 7CrMoVTiB10-10 has been studied. Based on experimental carrier gas hot extraction (CGHE) data, a numerical model has been developed to describe the hydrogen transport and respective hydrogen distribution at elevated temperatures. The numerical results suggest that common calculation methods for diffusion coefficients are limited for experimental data analysis. The sample preparation time before CGHE experiment influences the determined diffusion coefficients with the consequence that non-homogeneous hydrogen concentration profiles have to be considered in the simulations.
Duplex stainless steels have been used for a long time in the offshore industry, since they have higher strength than conventional austenitic stainless steels and they exhibit a better ductility as well as an improved corrosion resistance in harsh environments compared to ferritic stainless steels. However, despite these good properties the literature shows some failure cases of duplex stainless steels in which hydrogen plays a crucial role for the cause of the damage. Numerical simulations can give a significant contribution in clarifying the damage mechanisms. Therefore, a numerical model of a duplex stainless steel microstructure was developed enabling simulation of crack initiation and propagation in both phases. The phase specific stress strain analysis revealed that local plastic deformation occurs in both austenite and δ-ferrite already in the macroscopically elastic range. Altogether, phase specific hydrogen-assisted material damage was simulated for the first time taking into account all main factors influencing hydrogen assisted cracking process. The results agree well with experimental observations and thus allow a better insight in the mechanism of hydrogen-assisted material damage.
Modeling of Hydrogen-Assisted Cracking (HAC) in Duplex Stainless Steels (DSS):
- Hydrogen causes significant degradation in DSS and consequently HAC
- Mechanisms of HAC have not been fully understood in two-phase microstructures
- Mesoscale numerical modeling for HAC in DSS was created, coupled to the macroscale, enabling simulation of HAC in both phases independent from predefined crack paths
In the field of modelling hydrogen assisted cracking (HAC) phenomenon, hydrogen diffusivity is an important input parameter for numerical simulation. In terms of hydrogen diffusion coefficients, they have great impact on realistic assessment of the evolution of possible crack critical hydrogen concentrations. In addition, the chemical compositions of steels can have a strong effect on hydrogen diffusion. Unfortunately, literature provides a wide range of available hydrogen diffusion coefficients even for similar microstructures and equal temperatures. The scattering of the data can lead to significant deviations in the results of simulating the evolving hydrogen concentrations due to hydrogen uptake (by fabrication or service). Thus, the application of such data to crack-models or for component life tie predictions can be realized up to the present only by considering envelope curves of such value, corresponding to a work or bench case scenario, respectively. For improved reliability of numerical simulaitons, it is necessary to minimize the mentioned deviation of these data. Hence, this work focuses on the validation of hydrogen diffusion coefficients obtained from permeation experiments at room temperature. Two baintic steels with different alloying concepts were investigated, the creep-resistant 7CrMoVTiB10-10 and the reactor pressure vessel grade 20MnMoNi4-5. A numerical model is presented for simulation of the corresponding hydrogen diffusion during permeation experiments using the finite element software ANSYS. Three different diffusion coefficients (obtained from different common calculation methods) are considered and compared to numerical results. The vases of thes calculation methods are permeation transients which are a direct measure for hydrogen. The results of the simulated hydrogen diffusion coefficients show that only one procedure for calculation of diffusion coefficitnes is suitable in comparision to the experimental values. Thus, it is suggested to use this method for analysis of experimental results in case of hydrogen diffusion during permeation experiments. Furthermore, this work supplies validated values for the hydrogen diffusion coefficients of both steel grades.
Numerical investigations on hydrogen-assisted cracking in duplex stainless steel microstructures
(2016)
Duplex stainless steels (DSS) are used in various industrial applications, e.g. in offshore constructions as well as in chemical industry. DSS reach higher strength than commercial austenitic stainless steels at still acceptable ductility. Additionally, they exhibit an improved corrosion resistance against pitting corrosion and corrosion cracking in harsh environments. Nevertheless, at specific conditions, as for instance arc welding, cathodic protection or exposure to sour service environments, such materials can take up hydrogen which may cause significant property degradation particularly in terms of ductility losses which, in turn, may entail hydrogen-assisted cracking (HAC). The cracking mechanism in DSS is different from steels having only a single phase, because hydrogen diffusion, stress-strain distribution and crack propagation are different in the austenite or ferrite phase. Therefore, the mechanism of HAC initiation and propagation as well as hydrogen trapping in DSS have not been fully clarified up to the present, as for most of the two-phase microstructures. At this point the numerical simulation can bridge the gap to a better insight in the cracking mechanism regarding the stress-strain distribution as well as hydrogen distribution between the phases, both austenite and ferrite, of the DSS. For that purpose, a two dimensional numerical mesoscale model was created representing the microstructure of the duplex stainless steel 1.4462, consisting of approximately equal portions of austenite and ferrite. Hydrogen assisted cracking was simulated considering stresses and strains as well as hydrogen concentration in both phases. Regarding the mechanical properties of austenite and ferrite different statements can be found in the literature, dependent on chemical composition and thermal treatment. Thus, various stress-strain curves were applied for austenite and ferrite simulating the HAC process in the DSS microstructure. By using the element elimination technique crack critical areas can be identified in both phases of the DSS regarding the local hydrogen concentration and the local mechanical load. The results clearly show different cracking behavior with varying mechanical properties of austenite and ferrite. Comparison of the results of the numerical simulation to those of experimental investigations on DSS will improve understanding of the HAC process in two phase microstructures.
Since the mid-nineties, supermartensitic stainless steels (SMSS) have increasingly been applied to welded subsea-pipeline systems in the North Sea oil and gas fields, especially to flowlines at mild sour service conditions. However, in 2001 cracking and leaks occurred during installation and service start-up of two SMSS flowlines in the Norwegian Tune gas condensate field, welded with a new developed matching filler wire. Brittle transgranular cracking started especially at inter-run lack of fusion and propagated brittle, predominantly through the weld metal. The present paper provides a brief overview of the original failure case and respective sequence of events leading to complete replacement of the SMSS by carbon steel flowlines in 2002. Then, detailed investigations of a circumferential weld sample of the failed Tune flowline are highlighted, targeted at comparison of the failure appearance to previous investigations of this filler material type and to search for possible explanations for the brittle fracture at the crack initiation area. SEM investigations of the fracture surface revealed brittle areas only in the direction towards the top side of the weld while the major part of the investigated surface exhibited ductile fracture. As an approach to clarify, if the fracture was a consequence of hydrogen assisted cracking, five small sized specimens have been cut out of the original sample. Cracking has been introduced parallel to the original fracture surface in these specimens at respective saw cuts and bending. The results show that brittle transgranular cracking appeared only in the specimen cooled down to very low temperatures by liquid nitrogen and in the sample charged with hydrogen to an average concentration of about 15 ml/100 g. However, a fracture similar to the original surface was observed only in the hydrogenized specimen. As a further result, very similar fracture surfaces of supermartensitic stainless steel weld metals had been observed on specimens subjected to hydrogen assisted cold cracking (HACC) as well as to hydrogen assisted stress corrosion cracking (HASCC). In total, the results indicate that brittle fracture starting at the inter-run lack of fusion were not initiated by high notch tip deformation rates, but rather influenced by hydrogen, probably taken up during welding.
Hydrogen assisted stress corrosion and cold cracking represent still a major topic regarding the safety of welded steel components against failure in many industrial branches. Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or at cathodic protection. Additionally, understanding and avoidance of hydrogen entry into weld microstructures from gaseous pressurized environments becomes increasingly important for renewable energy components. There are two types of metallurgical mechanisms associated with hydrogen assisted cracking, i.e. the cracking as well as hydrogen transport and trapping mechanisms. For numerical modelling, it has to be considered that both types are not independent of each other, that the mechanisms are not yet completely clarified and that validation of such models strongly depends on implementation of the correct hydrogen related materials properties. However, quite significant achievements have been made in modelling of hydrogen assisted cracking by indirect coupling of thermal, stress-strain as well as hydrogen uptake and diffusion analyses. After a brief introduction into the subject and by revisiting various proposed cracking mechanisms, the present contribution focuses on recent developments of a numerical model based on a comparison of actual hydrogen concentrations and mechanical loads with respective hydrogen dependent material properties as crack initiation and propagation criteria. The basic procedure for numerical simulation of crack initiation and propagation is outlined and it is shown how such numerical simulations can be validated experimentally. Furthermore, it is highlighted how such a procedure has been extended to a comprehensive model for life time prediction of welded steel pipeline components and experimentally verified. Finally, it is outlined how the model can be extended to simulate cracking in heterogeneous steel microstructures on the different scales.
Quite a number of numerical models for hydrogen-assisted cracking in different kind of steels are existing reaching from simple analytical models to more complex two- and three-dimensional finite element simulations. These numerical models have been used to simulate the processes of hydrogen-assisted cracking in homogeneous microstructure. This paper contributes to numerical simulation of hydrogen-assisted cracking in heterogeneous microstructure, e.g., in a duplex stainless steel microstructure consisting of two phase fractions. If hydrogen is absorbed during welding or during service, i.e., due to cathodic protection, hydrogen is leading to material embrittlement and leads to hydrogen-assisted cracking. In order to improve understanding of the mechanisms of hydrogen-assisted cracking in duplex stainless steels, a numerical model has been created that operates at the mesoscale and enables simulation of stress–strain distribution as well as cracking in the various phases of a metallic material. Stress–strain distribution and hydrogen-assisted cracking in the duplex stainless steel 1.4462, consisting of approximately equal portions of ferrite and austenite, was simulated using the finite element program ANSYS. It was shown by numerical simulation that higher local stresses and strains are present at ferrite and austenite than the global stresses and strains in the duplex stainless steel, while the highest plastic deformations occur at austenite and the highest stresses can be found in small ferrite bars surrounded by ductile austenitic islands. By analyzing the stress–strain distribution in the duplex microstructure, crack critical areas in the ferrite can be identified. Hydrogen-assisted cracking was modeled assuming high hydrogen concentrations and regarding the local mechanical load in each phase of the duplex stainless steel. The mesoscale model qualitatively reflects the crack initiation and propagation process in the ferritic and austenitic phase of the duplex stainless steel.
Industry faces a growing demand for high-strength structural steels with yield strengths of up to 1,300 MPa in order to cope with increasingly higher strength requirements in engineering. Higher strength levels are achieved by a special coordinated production process and an adapted chemical composition. Nevertheless, disastrous damage cases with high-strength steels have occurred in the past. The sensitivity to mechanical property degradation by hydrogen increases dramatically with strength. This phenomenon leads to hydrogen-assisted cold cracking. T-joints with fillet welds made from one side with an included angle of 60° were examined for their cold cracking behavior. Based on the T-joint, a modified heat input, even interpass temperature, plate thickness, and length ones were examined. The diffusion behavior and the effectiveness of different post-weld heat treatments in joints were simulated. The results of post-weld heat treatments are illustrated in practical hydrogen removal heat treatment diagrams. It is noticed that the T-joint is subject to a very high risk of hydrogen-assisted cold cracking (HACC). Contrary to other joints, its most critical area for cracking is not the weld metal but the heat-affected zone surrounding area of the root pass. The simulation shows that HACC in the T-joint can only be avoided by applying a sufficient post-weld heat treatment.
Duplex stainless steels (DSS) are used in various industrial applications, e.g. in offshore construction as well as in chemical industry. But, at specific conditions, as for instance arc welding fabrication, cathodic protection or exposure to sour service environments, such materials can take up hydrogen which may cause significant property degradation particularly in terms of ductility losses which, in turn, may entail hydrogen assisted cracking (HAC). If HAC occurs in a duplex stainless steel the cracking mechanism is different from steels having only one phase, because hydrogen diffusion, stress-strain distribution and crack propagation are totally different in the austenite or ferrite phase. Whereas, the mechanism of hydrogen assisted crack initiation and propagation as well as hydrogen trapping in DSS have not been fully understood up to the present, as in most two-phase microstructures. In order to better understand the mechanisms of hydrogen assisted cracking in duplex stainless steels, knowledge of the diffusion behavior and of the stress-strain distribution in the ferritic and austenitic phase is of great interest. A numerical mesoscale model was created with a view to studying the hydrogen transport and the stresses and strains in each phase of duplex stainless steel. The material investigated in this work was DSS 1.4462, consisting of approximately equal portions of ferrite and austenite. Hydrogen diffusion in the duplex base metal was studied using the finite element program ANSYS. Stress-strain distribution as well as hydrogen assisted cracking in the ferritic and austenitic phase fractions were additionally investigated. The results of numerical simulation of the hydrogen diffusion process as well as structural analyses enable the identification of crack critical areas in the DSS microstructure. Numerical simulations qualitatively reflect the crack initiation and propagation process in ferrite. Crack critical combinations of hydrogen concentrations and local mechanical loads initiating HAC can be identified.
Quite a number of models for hydrogen distribution in steels and welds have been developed in the past 20 years. They reach from simple analytical models to more complex two and three dimensional finite element simulations. So far, these models have been used to simulate hydrogen distribution in homogeneous microstructure. This paper contributes to numerical simulation of hydrogen distribution in heterogeneous microstructure, e. g. in a duplex stainless steel microstructure consisting of two phase fractions. Under appropriate conditions, such as cathodic protection, it is possible that hydrogen is absorbed leading to material embrittlement and possibly initiating hydrogen assisted cracking. In order to avoid hydrogen assisted cracking in duplex stainless steels, it is of great interest to know more about the diffusion behavior of the ferrite and austenite phase. A numerical model has been developed that operates on the mesoscale and enables simulation of hydrogen transport in the various phases of a metallic material. As a first application of this model, hydrogen distribution in a duplex stainless steel 1.4462, consisting of approximately equal portions of ferrite and austenite, was simulated using the finite element program package ANSYS. The results reflect the dependency of hydrogen distribution on the microstructural alignment of the ferrite and austenite phase fractions. Crack-critical areas can thus be identified, provided the critical strain-hydrogen combination is known for the respective microstructural phase.
Aus wirtschaftlich-technischer Perspektive ergeben sich in den letzten zehn Jahren hinsichtlich der Werkstoffinnovation und -auswahl für geschweißte Rohrleitungen im Wesentlichen zwei Entwicklungsrichtungen:
Im Bereich der niedriglegierten Stähle werden immer höher festere Feinkombaustähle mit Streckgrenzen von inzwischen über 900 MPa verwendet. Wirtschaftliches Ziel ist hierbei eine möglichst hohe Kosteneinsparung durch Reduktion der Wanddicke.
Für korrosionsbeanspruchte Komponenten, unter anderem im Petrochemie- und Energieanlagenbau besteht das wirtschaftliche Ziel primär darin, eine höhere Kosteneinsparung durch neue Legierungskonzepte zu erzielen und zwar möglichst so, dass bei mindestens gleicher Festigkeit auf die Verwendung von teuren Elementen, wie beispielsweise Nickel, verzichtet werden kann. Beispiele hierfür sind insbesondere hochlegierte martensitische Cr-V-Stähle, supermartensitische Stähle, Lean-Duplexstähle, superaustenitische Stähle und austenitische Cr-Mn-Stähle.
Für einige der neu eingeführten Grundwerkstoffe sind die Zusatzwerkstoffe noch in der Entwicklung. In jedem Fall stellen diese Werkstoffinnovationen besondere Ansprüche hinsichtlich einer Rissvermeidung während der schweißtechnischen Verarbeitung, um von vornherein riss- bzw. fehlerfreie Rohrleitungen herzustellen, die eine hohe Sicherheit gegen ein Versagen während der Inbetriebnahme und im Verlauf der vorgesehenen Lebensdauer aufweisen. Fast alle dieser neu eingeführten Rohrleitungswerkstoffe weisen eine reduzierte Heiß- oder Kaltrissresistenz vor allem während des Schweißens mit modernen Hochleistungsprozessen, bspw. Laserhybridschweißen, auf. Dabei besteht nach wie vor Forschungsbedarf hinsichtlich der jeweiligen Entstehungsmechanismen. Da es in den letzten zehn Jahren immer häufiger zu Produktionsausfällen und Schadensfällen mit teilweise katastrophalen Konsequenzen gekommen ist, werden die Ursachen und die Vermeidung fertigungsbedingter Heiß- und Kaltrisse im Folgenden zusammengefasst.
Schadensfälle in den letzten zehn Jahren mit teilweise katastrophalen Folgen belegen, dass der Vermeidung von Rissen beim Schweißen von Rohrleitungen besondere Aufmerksamkeit zu schenken ist. In der Analyse solcher Schäden ist zu unterscheiden, ob die Risse bereits während oder kurz nach der schweißtechnischen Fertigung der Rohrkomponenten oder während des anschließenden Betriebes entstanden sind. Im vorliegenden Beitrag wird sich vor allem auf die Vermeidung einer Heiß- und Kaltrissbildung beim Schweißen von Rohrleitungen konzentriert und es werden weitere Forschungsperspektiven abgeleitet.
The present contribution highlights recent trends in investigating hydrogen diffusion and cracking in steel welds. For such studies, supermartensitic stainless steels (SMSS) have exemplarily been selected. These materials have been used for offshore and marine constructions for about two decades now. They present a versatility of improved properties such as high strength to thickness ratio, good weldability and good corrosion resistance. However, as shown by respective failure cases, SMSS welds might become prone to hydrogen assisted cracking and the degradation phenomena are more easily to investigate due to the nearly homogeneous martensitic microstructure than in other materials. Generally, it has to be distinguished between cracking that occurs during or shortly after fabrication welding, or during subsequent operation of SMSS components. In order to achieve crack avoidance during fabrication and service, conclusive test sequences have to be applied, ranging from field tests at real components and full scale tests investigating the materials behavior under real service conditions to basic and small scale tests, such as tensile and corrosion tests, oriented more towards a materials ranking. Considerable testing of SMSS welds has been carried out and the present paper particularly summarizes spotlights on 1:1 scale component testing of welded tubulars, slow strain rate testing and basic tests oriented to elucidate the hydrogen behavior and degradation in SMSS weld microstructures. Also, permeation tests, hydrogen dependent degradation of mechanical properties and thermal desorption spectroscopy are adressed. As a specific item, first results of lately conducted investigations for tracking hydrogen movement in such weld microstructures by using high energy synchrotron radiation are elucidated.