Mass spectrometric detection can play a prominent role in the assessment of different reactions occurring at varied temperatures in a milled ZnO/Al mixture. This is the first time that online mass spectrometric information was used as a tool for monitoring and understanding the chemical reduction process mechanism. We have observed four different types of reaction taking place: (1) distillation of Zn metal, (2) reduction of ZnO by activated Al, (3) melting of Al and finally (4) reduction of ZnO by inactivated Al. The experimental conditions and results observed by QMS were supported with literature data and physical measurement data from X-Ray Diffraction (XRD) which gave us an idea about the complex reaction cascade which occurred during the formation of the zinc metal.
Synthetic pressed metal powder standards doped with standard solutions were used for the calibration of both commercially available high resolution GD-MS instruments Element GD and VG 9000 for zinc matrix. Different quantification procedures (IBR, Standard RSF, matrix matched RSF from the calibration with CRMs and use of doped synthetic standards) are compared using zinc matrix as an example, whereas the calibration with doped pellets turned out to be the best quantification technique for high-purity materials. The applicability of the Standard RSF concept is scrutinised. In this context, RSF values for several Matrices (Co, Cu, Fe, In and Zn) are reported additionally.
In this work, different calibration strategies for the determination of trace elements in pure copper metal by nanosecond laser ablation ICP-MS were investigated. In addition to certified reference materials (CRMs), pellets of doped copper powder were used for calibration. The micro homogeneity of the CRMs as well as the solution-doped pellets was sufficient to use them as calibration samples in combination with a laser spot size of 200 µm. In contrast, pellets doped with analytes in solid form showed a significant heterogeneity. For most of the investigated analytes and copper CRMs the measured mass fractions were within ± 20% of their certified values when other copper CRMs were used as calibration samples. When solution-doped powder pellets were used as calibration samples a systematic trend towards mass fractions below the certified values was observed for nearly all elements determined in the analysed CRMs. Thermal fractionation effects during the ablation of the solution-doped pellets were suspected as the extent of the fractionation depends on the irradiance, whereas fractionation is reduced at higher irradiance.
Ultra high purity Zn (m6N5) was obtained through triple vacuum distillation using an m4N5 Zn as input material. High-volatile impurities were removed from the zinc matrix by vacuum evaporation, while traces having lower volatility than the matrix remained in the residual material after finishing of the entire purification process. The time required for the removal of the main high-volatile impurity (Cd) was monitored using a connected gas source mass spectrometer. During distillation the Zn vapor of the distillate was condensed on the cap of a glassy carbon crucible which was water cooled by a movable copper block. The temperatures were optimized for the removal of the volatiles and for the distillation process using vapor pressure data. High resolution glow discharge mass spectrometry was applied for the analysis and purity evaluation of the distilled and input zinc. The analysis confirmed the reduction of the metallic impurities from 43 mg kg-1 to 0.5 mg kg-1 (m6N5) after three consecutive vacuum distillations. An increase in the grain size and a decrease in the micro-hardness were observed for the purified Zn material.