The debonding of fibers under mixed-mode loading is studied on model composites containing fibers with different orientations with respect to the loading direction. The spacing of the fibers is large, accordingly no significant fiber interaction takes place. For any fiber orientation, interfacial debonding occurs, even though at different load levels. Only for the low off-axis angle, additional fiber fracture is found. Using a rectangular specimen, the interface crack starts at the edges propagating into the center at low speed. In the first phase, only the central part of the interface debonds. After the whole fiber is debonded, the crack propagates in circumferential direction. The superimposition of fiber breakage and debonding shows that the restriction of two potential failure planes - perpendicular or parallel to the fibers - has to be put in question.
The debonding of a fiber in a glass fiber / epoxy composite under transverse loading
is analysed. The stress field in the interface as well as the energy release rate are
analysed for various fiber volume fractions between 5% and 85%. The circumferential
propagation of an interface crack in a hexagonal fiber array is studied. The analysis
is performed by a finite element simulation under plane stress conditions. The
stress distribution during crack propagation is calculated for different crack phases.
The crack starts under dominating mode I stresses. After propagating some 60° the
mode II part reaches a maximum while the mode I part vanishes and the crack
closes. The further crack propagation is driven by mode II stresses only. In addition,
the stress transfer into the neighbouring fibers during debonding is studied.
The failure of fiber reinforced composites under transverse loading is investigated on a
representative volume element. The volume element is composed of a twelve fiber hexagonal
array. The debonding of the central fiber is studied under transverse shear as well as under
transverse compressive loading by calculating the mode I and mode II part of the energy
release rate. The initiation of failure is assumed to take place at the location of maximum
tensile or maximum shear stresses, respectively. In order to determine the failure initiation
point, the stress field in the interface before crack initiation is calculated.
The failure of laminates usually is initiated by the failure of the plies with the maximum transverse stresses. The failure of those plies generally reduces the load carrying capability of the laminate, even though they carry only a small part of the external load. The analysis of failure under off-axis stresses accordingly is essential for the prediction of the strength of laminates. This is taken into account in the "mechanisms based failure criteria" e.g. by Puck. Most of these inter fiber failure criteria are not based on the micromechanics of the failure process but on prescribed stress interaction functions. The failure of plies under transverse loading obviously is governed by the bond strength between fiber and matrix fiber. The interfacial debonding was studied e.g. by Paris et al. and Corea et al.. The bond strength between fiber and matrix usually is measured by using micromechanical tests e.g. pull-out, push-out or fragmentation tests. Stress analyses as well as fracture mechanical analyses show that the interfacial failure over a large range is dominated by shear stresses (Kim and Mai, Pisanova et al, Marotzke and Qiao). The stress distribution arising in those experiments however differs from the stresses acting in a lamina under transverse loading. In transverse failure of a lamina, radial stresses as well as shear stresses are dominating the failure process of the interface. In addition longitudinal shear stresses are present. Experimental work concerning off-axis loading of single fibers was done e.g. by Tandon and Kim and by Ogihara and Koyanagi. They studied the influence of the fiber alignment by using a specimen in form of a cruciform with skew wings.
The failure of composites is initiated by imperfections on microscale. The interface between fiber and matrix is a key parameter concerning failure initiation. In order to get an improved understanding of local failure processes a fracture mechanical analysis of interfacial failure in a composite ply under transverse stresses is performed. The mixed mode energy release rate is calculated. In addition the failure of interfaces under cyclic loading is studied on a single fiber model. The quasistatic debonding process is compared with the interfacial failure under fatigue loading. It is shown that the tan delta can be used as an indicator for the damage propagation.
Off-axis tests are widely used for the determination of the anisotropic mechanical properties of composite materials, this is, the longitudinal E-modulus and the strength. The mechanical properties are evaluated from the test data under idealising assumptions such as homogeneity of the material as well as a homogeneous stress distribution. In real off-axis tests, however, significant deviations from the idealising assumptions are present. The reduction of the accuracy of the results strongly depends on the off-axis angle.
In this paper a series of off-axis tests is analysed. The stresses on potential failure plane are calculated by finite element analyses. By varying the geometrical parameters it is shown how small deviations from the ideal case influence the measured elastic constants and the strength. Especially at low off-axis angles the mechanical properties strongly vary with the angle. In addition, fracture surfaces for different shear/normal stress combinations are studied and typical phenomena are identified.
The strength of laminates distinctly depends on the transverse strength of the laminas. The transverse failure is dominated by the adhesion between fiber and matrix. Usual strength criteria however do not take into account the adhesive strength explicitly. The determination of the interface strength is performed on the micromechanical scale using single fiber specimens. The fibers are loaded under off-axis loading while the debonding is monitored under a microscope. The stresses acting in the Interface are calculated by finite element analyses. It is found that for off-axial angles up to 35° interfacial debonding is the dominant failure mode while fiber breakage takes place at lower angles. The occurrence of fiber breakage and debonding under off-axis loading shows that the restriction to two potential failure planes - perpendicular or parallel to the fibers - as applied in common failure criteria has to be put in question.
Failure of composite materials is initiated by fracture processes on microscale, especially by interfacial debonding. Failure processes taking place on microscale are studied by single fiber experiments. This is, single fibers embedded in tensile specimen are loaded under various off-axis angles. Starting at microdefects interface cracks propagate circumferentially as well as longitudinally, depending on the loading angle. In addition, finite element simulations of interfacial crack propagation around single fibers as well as fibers embedded in a hexagonal composite are shown based on linear elastic fracture mechanics. The course of the energy release rate is given in dependence of the fiber volume fraction.