Unlike conventional alloys, high entropy alloys are characterized by one or more solid solution phase(s) without a clearly defined solvent, all element contribute to the matrix in a way that is still not entirely understood. In addition, it is not known to what extent classic thermodynamic rules can be applied to these multi-element alloys, especially concerning the question about what factor incites the matrix to undergo a phase transformation.
This work tackles directly some of these aspects on a chosen alloy, Al8Cr17Co17Cu8Fe17Ni33 (at.%), which presents a high temperature single-phase γ state and a two-phase state with γ′ precipitates, above and below 900 ◦C, respectively. A combined investigation via microstructural observations, hardness testing, X-ray absorption and photoelectron spectroscopy was carried out above the γ′ formation temperature. Hardness values are independent of the annealing temperatures, microstructural analysis shows no phase formation and X-ray absorption spectroscopy does not reveal observable changes in neither local atomic nor electronic structure, indicating that approaching γ′ formation temperature is not influenced by atomic or electronic rearrangements.
Interestingly, short-range chemical order remains quantitatively compatible at any annealing temperature in the single-phase γ state, and the observed preferred pairs Al–Cu and Al–Ni in the γ state match with the γ’ precipitates composition below 900 ◦C.
A systematic study on a face‐centered cubic‐based compositionally complex alloy system Al–Co–Cr–Cu–Fe–Ni in its single‐phase state is carried out, where a mother senary compound Al₈Co₁₇Cr₁₇Cu₈Fe₁₇Ni₃₃ and five of its suballoys, obtained by removing one element at a time, are investigated and exhaustively analyzed determining the contribution of each alloying element in the solid solution. The senary and the quinaries are compared using experimental techniques including X‐ray absorption spectroscopy, X‐ray diffraction, transmission electron microscopy, and first principles hybrid Monte Carlo/molecular dynamics simulations. Chemical short‐range order and bond length distances have been determined both at the experimental and computational level. Electronic structure and local atomic distortions up to 5.2 Å have been correlated to the microhardness values. A linear regression model connecting hardness with local lattice distortions is presented.
Extended X-ray absorption fine structure (EXAFS) conducted on an equiatomic MoNbTaW bcc medium-entropy alloy that was annealed at 2273 K reveals unexpectedly small 1st and 2nd shell element-specific lattice distortions. An experimental size-mismatch parameter, δexp, is determined to be ca. 50% lower than the corresponding calculated value. Around W, short-range order (SRO) preferring 4d elements in the 1st and 2nd shells persists. A Nb-W ordering is found, which is reminiscent of ordering emerging at lower temperatures in the B2(Mo,W;Ta,Nb)- and B32(Nb,W)-phases. With high-temperature ordering preferences in fcc also foreshadowing low-temperature phase, these findings suggest a general feature of high-temperature SRO.
This work presents an X-ray absorption spectroscopy study on a single-phase state of the Al8Cr17Co17Cu8Fe17Ni33 compositionally complex alloy, focused on the local crystal structure around each alloying element. The comparison of 1st shell bond lengths, obtained by the analysis of extended X-ray absorption fine structure (EXAFS) measured at the K-edges of each alloying element, indicates that Al8Cr17Co17Cu8Fe17Ni33 crystallizes in a distorted arrangement of an fcc lattice. A modest bond length dependence of the alloying elements with increasing atomic number is observed, with minima and maxima at Cr/Co, and Al/Cu, respectively. 1st shell bond lengths spread over ~0.03 Å; consequently, such variations cannot result in lattice distortions greater than ~0.04 Å. EXAFS results clearly indicate short-range order in the alloy: pairing of Al with Ni and Cu is favored, correlating well with a g’ precipitate composition (Al-Ni-Cu rich) reported in previous work, while Al-Cr bonding is unfavored and no Al-Al pairs are observed. Electronic structure information was obtained through comparison between near-edge regions of alloying Elements and corresponding pure metals. Intensity comparison of K-edge features agree with a charge variation of p states in Al8Cr17Co17Cu8Fe17Ni33, where Ni and Cu act as p states electron acceptors, suggesting an orbital hybridization with Al, responsible for a shrinkage in Al metallic radius in the alloy by 0.17 Å.