Filtern
Erscheinungsjahr
Dokumenttyp
Referierte Publikation
- ja (62) (entfernen)
Schlagworte
- Tomography (8)
- Radiography (7)
- Water transport (7)
- Computed tomography (6)
- Electron tomography (6)
- Neutron imaging (6)
- Neutron tomography (6)
- Polymer electrolyte membrane fuel cell (PEMFC) (6)
- Fuel cell (5)
- Reconstruction algorithm (5)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
A systematic study has been carried out to investigate the neutron transmission signal as a function of sample temperature. In particular, the experimentally determined wavelength-dependent neutron attenuation spectra for a martensitic steel at temperatures ranging from 21 to 700°C are compared with simulated data. A theoretical description that includes the Debye–Waller factor in order to describe the temperature influence on the neutron cross sections was implemented in the nxsPlotter software and used for the simulations. The analysis of the attenuation coefficients at varying temperatures shows that the missing contributions due to elastic and inelastic scattering can be clearly distinguished: while the elastically scattered intensities decrease with higher temperatures, the inelastically scattered intensities increase, and the two can be separated from each other by analysing unique sharp features in the form of Bragg edges. This study presents the first systematic approach to quantify this effect and can serve as a basis , for example, to correct measurements taken during in situ heat treatments, in many cases being a prerequisite for obtaining quantifiable results.
In various kinds of radiography, deficient transmission imaging may occur due to backlighting inside the detector itself arising from light or radiation scattering. The related intensity mismatches barely disturb the high resolution contrast, but its long range nature results in reduced attenuation levels which are often disregarded. Based on X-ray observations and an empirical formalism, a procedure is developed for a first order correction of detector backlighting. A backlighting factor is modeled as a function of the relative detector coverage by the sample projection. Different cases of sample transmission are regarded at different backlight factors and detector coverage. The additional intensity of backlighting may strongly affect the values of materials’ attenuation up to a few 10%. The presented scenario provides a comfortable procedure for corrections of X-ray or neutron transmission imaging data.
Die Computer-gestützte Laminografie (CL) wurde als komplementäre Methode zur Computertomografie für die dreidimensionale Bildgebung von lateral ausgedehnten Objekten entwickelt. Ursprünglich für medizinische Zwecke verwendet, wurde diese Methode kürzlich als zerstörungsfreie nicht-invasive Methode nicht nur in der Materialforschung, sondern auch mit steigendem Interesse für kunsthandwerkliche und historische Objekte eingesetzt. Hier wird die Computer-gestützten Laminografie mit polychromatischer Neutronenstrahlung an einer historischen Tsuba eingesetzt, einem Stichblatt eines japanischen Schwerts. Eine Analyse der Lötstellen gibt Rückschlüsse auf das Herstellungsverfahren. Zudem wurden unterschiedliche Materialsysteme gefunden, vermutlich um dem Tsuba lokal eine höhere Stabilität zu verleihen. Die Messungen wurden an der Imaging-Beamline CONRAD-2 an der Neutronenquelle BER 2 des Helmholtz-Zentrums Berlins (HZB) durchgeführt.
Aufgrund des hohen Wirkungsgrades und der vielfältigen Einsatzmöglichkeiten können Brennstoffzellen einen wichtigen Beitrag zur zukünftigen Energieversorgung leisten. Für die Optimierung der Brennstoffzellentechnik ist es erforderlich, die während des Zellbetriebs ablaufenden Prozesse zu verstehen und exakt zu charakterisieren. Ein ausbalanciertes Wassermanagement ist die Grundlage für die optimale Leistungsfähigkeit einer wasserstoffbetriebenen Zelle. Das während des Betriebs entstehende Wasser muss die Membran ausreichend befeuchten, um deren Protonenleitfähigkeit aufrechtzuerhalten. Andererseits behindern zu große Wasseransammlungen in der Zelle die Gaszufuhr durch die porösen Materialien sowie in den Kanälen der Gasverteilerstrukturen. Alterungsphänomene einzelner Zellkomponenten können die Verteilung der Wasseransammlungen und somit das Wassermanagement empfindlich stören und so die Leistungsfähigkeit der Brennstoffzelle herabsetzen. Zur Analyse der Wasserverteilung werden zerstörungsfreie, bildgebende Methoden, wie die Ex-situ-Neutronentomografie und die In-situ-Synchrotronradiografie, eingesetzt. Diese Methoden können während des Brennstoffzellenbetriebs mit weiteren Messverfahren, beispielsweise der ortsaufgelösten Stromdichtemessung, kombiniert werden. Auf diese Weise werden einzelne Komponenten, wie zum Beispiel die Gasdiffusionsschichten, charakterisiert.
Influence of artificial aging of gas diffusion layers on the water management of PEM fuel cells
(2014)
The influence of artificial aging of gas diffusion layers (GDL) on the water management within the GDL was investigated in-operando by synchrotron X-ray radiography. One GDL was subjected to an accelerated aging procedure in 30% H2O2 solution, while another GDL was pristine. Radiographic measurements were combined with temporally resolved electrical analyzes. Significant differences in cell voltage and water accumulation were observed during cell operation at steady-state conditions. The cell which contained the aged GDL featured a higher water amount especially at the anode side and a lower cell voltage.
Synchrotron X-ray absorption edge imaging with high energy resolution was applied to study aging of fuel cell catalyst materials. The combination of an imaging and a high X-ray energy resolution set-up allows acquiring spatially resolved XAS (XANES and EXAFS) spectra. We analyzed the two-dimensional distribution of Pt and Ru in fresh and aged fuel cell catalysts. Spatially resolved XAS images were taken at the RuK edge and at the PtL3 edge. Taking radiographs above and below the absorption edges provides quantitative information about the thickness of the catalytic materials and additional chemical information. A strong influence of the flow field channels and the structure of the gas diffusion layers on the thicknesses of the catalytic elements were found: a thinner catalyst layer was found below the ribs of the flow field geometries as well as under crossing points of fiber bundles of the woven gas diffusion layers.
Synchrotron X-ray absorption edge imaging was used to investigate the ruthenium distribution in both fresh and aged Pt/Ru-based membrane electrode assemblies (MEA) of direct methanol fuel cells. MEAs aged in different ways were analyzed: artificially aged by MeOH depletion and aged for 1700 h in an operating fuel cell stack. An element sensitive tomographic technique – differential X-ray absorption edge tomography – was applied allowing for a 3D-visualization of the ruthenium distribution within the MEA. We found a markedly changed Ru distribution after aging which is correlated to the GDL structure, the flow field geometry, and CO2 transport in the methanol solution.
Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic
stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial
resolution of 100 µm.
Phosphoric acid as the electrolyte in high-temperature polymer electrolyte membrane fuel cell plays an essential role in ist performance and lifetime. Maldistribution of phosphoric acid in the catalyst layer (CL) may result in performance degradation. In the present study, pore-scale simulations were carried out to investigate phosphoric acid’s multiphase flow in a cathode CL. A reconstructed CL model was built using focused ion beam-SEM images, where distributions of pore, carbon support, binder, and catalyst particles can be identified. The multi-relaxation time lattice Boltzmann method was employed to simulate phosphoric Acid invading and leaching from the membrane into the CL during the membrane electrode assembly fabrication process. The predicted redistribution of phosphoric acid indicates that phosphoric acid of low viscosity or low wettability is prone to leaching into the CL.
The effective transport properties and the active electrochemical active surface area (ECSA) were computed using a pore-scale model. They were subsequently used in a macroscopic model to evaluate the cell performance. A parametric study shows that cell performance first increases with increasing phosphoric acid content due to the increase of ECSA. However, further increasing phosphoric acid content results in performance degradation due to mass transfer limitation caused by acid flooding.